Welding flux used in filigree golden blank cloisonn product and manufacturing method for cloisonn product

A production method, the technology of cloisonné, which is applied to the process for producing decorative surface effects, welding media, manufacturing tools, etc., can solve the problems of green rust on the inner wall, affecting the appearance, and poisonous rust, so that it is not easy to open seams and improve Productivity, easy soldering effect

Active Publication Date: 2014-03-12
赵爱民
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current copper-bodied cloisonné has been preserved for a long time, and its inner wall has green rust, which not only affects the appearance, but also the rust is poisonous; the inner wall of silver-bodied cloisonne has been blackened for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0030] Example 1: A kind of flux used for filigree gold tire fusion welding cloisonne products, which is composed of the following components by weight percentage: 58.5% gold, 7.5% silver, 29% red copper, 5% cadmium, and the above weight percentage is added Composition 25% arsenic trioxide.

example 2

[0031] Example 2: A kind of welding flux used in filigree gold tire fusion welding cloisonné products, its weight percentage composition: 55% gold, 8% silver, 32% red copper, 5% cadmium, in addition add 26% of the above weight components of arsenic trioxide.

example 3

[0032] Example 3: A kind of welding flux used in filigree gold tire fusion welding cloisonné products, its weight percentage composition: 60% gold, 6% silver, 27% red copper, 7% cadmium, and add 22% of the above weight components of arsenic trioxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a welding flux used in a filigree golden blank cloisonn product and a manufacturing method for the cloisonn product. The method comprises the following steps of making a blank, inlaying a wire, installing the wire, soldering, pickling, painting blue, polishing blue, painting bright white glaze, polishing blue again, polishing, plating gold and the like. The soldering medicine powder comprises the following ingredients of 55-60% of gold, 6-8% of sliver, 27-32% of red metal, 4-7% of cadmium and arsenic trioxide which accounts 22-26wt% of above ingredients. During pickling, the soldered gold blank is pickled for three times and pickled for 10-12 minutes each time; and after blue painting, the sintering temperature is 790-820DEG C. The welding flux used for soldering has the advantages of good liquidity, firmness in welding and easiness in welding. The obtained cloisonn filigree has the advantages of preciseness in positioning, abrasion resistance, high hardness and no colour fading. The white glaze varnishing technology and two-time blue polishing are adopted, so that the obtained artware has the advantages of better color and high collection value, is always new and is free from rusting, and the high-level artistic enjoyment of people can be satisfied.

Description

technical field [0001] The invention relates to a cloisonné product, in particular to a method for making a welding powder used in filigree gold tire fusion welding of the cloisonne product and the cloisonne product. Background technique [0002] Cloisonne, also known as "copper body filigree enamel", is a unique handicraft combining porcelain and copper. It is made of copper as a blank, made into various shapes, and then pinched into various flowers with copper wire, filled with enamel glaze, and fired. , polished, gold-plated and other processes. It uses gold, silver, copper and a variety of natural minerals as raw materials, integrating art, crafts, carving, inlaying, glass melting, metallurgy and other professional technologies. Cloisonne has a unique shape, exquisite workmanship, exquisite craftsmanship, exquisiteness, solemn patterns, rich colors, and splendor. It is one of the most ethnic handicrafts. In 2006, it was selected into the first batch of national intangi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B28B1/00B44C5/00B23K35/30
CPCB23K35/3013B44C1/26B44C5/00
Inventor 赵爱民王新奇
Owner 赵爱民
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products