Preparation method of composite elastic fiber

A technology for compounding elastic fibers and polyolefin elastomers, applied in the fields of fiber chemical characteristics, melt spinning, rayon manufacturing, etc., can solve the problems of single types of elastic fibers, achieve elastic elongation performance, good mechanical properties, and extensive practice The effect of applying value

Active Publication Date: 2016-08-17
镇江优佰供应链科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the types of elastic fibers commonly used are relatively single, and they are only used in sportswear and underwear, which cannot meet people's diverse needs for elastic clothing fabrics. In recent years, scientists have been committed to developing a variety of elastic fibers to meet clothing for various occasions. fabric demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of preparation method of composite elastic fiber, it comprises the steps:

[0027] 1) Mix polyolefin elastomer, thermoplastic resin, silicone rubber, radiation sensitizer and antioxidant at the ratio of 60%, 25%, 10%, 4.9% and 0.1%, and send it into the twin-screw extruder, and control the temperature of each zone Between 130-250°C, extrude and pelletize to obtain polyolefin mixed masterbatch;

[0028] The polyolefin elastomer is a block copolymer of ethylene and octene POE (ExxonMobil, USA, brand 8230); the thermoplastic resin is linear low-density polyethylene (Dow, USA, brand 1210); the silicone rubber is Vinyl-terminated polydimethylsiloxane (Jilin Xiangyou Polymer Material Co., Ltd., brand XY-202-B); radiosensitizer is triallyl isocyanurate; antioxidant is hindered phenols ( CHEMNOX1010).

[0029] 2) Send the polyolefin mixed masterbatch into the hopper of the melt spinning machine. The temperature of each zone of the melt spinning machine is controlled be...

Embodiment 2

[0032] A kind of preparation method of composite elastic fiber, it comprises the steps:

[0033] 1) Select polyolefin elastomer, thermoplastic resin, silicone rubber, radiation sensitizer and antioxidant to mix in the proportion of 70%, 15%, 10%, 4.9%, 0.1%, and send it into the twin-screw extruder, and control the temperature of each zone Between 150-200°C, extrude and pelletize to obtain polyolefin mixed masterbatch;

[0034] The polyolefin elastomer is a block copolymer of ethylene and octene POE (ExxonMobil, USA, brand 8230); the thermoplastic resin is linear low-density polyethylene (Dow, USA, brand 1210); the silicone rubber is Vinyl-terminated polydimethylsiloxane (Jilin Xiangyou Polymer Material Co., Ltd., brand XY-202-B); radiosensitizer is triallyl isocyanurate; antioxidant is hindered phenols ( CHEMNOX1010).

[0035] 2) Send the polyolefin mixed masterbatch into the hopper of the melt spinning machine. The temperature of each zone of the melt spinning machine is c...

Embodiment 3

[0038] A kind of preparation method of composite elastic fiber, it comprises the steps:

[0039] 1) Mix polyolefin elastomer, thermoplastic resin, silicone rubber, radiation sensitizer and antioxidant at the ratio of 75%, 10%, 10%, 4.9% and 0.1%, and send it into the twin-screw extruder, and control the temperature of each zone Between 120-170°C, extrude and pelletize to obtain polyolefin mixed masterbatch;

[0040] The polyolefin elastomer is a block copolymer of ethylene and octene POE (ExxonMobil, USA, brand VM6202); the thermoplastic resin is linear low-density polyethylene (Dow, USA, brand 1210); the silicone rubber is Vinyl-terminated polydimethylsiloxane (Jilin Xiangyou Polymer Material Co., Ltd., brand XY-202-B); radiosensitizer is acrylate; antioxidant is hindered phenol (CHEMNOX1076).

[0041] 2) Send the polyolefin mixed masterbatch into the hopper of the melt spinning machine. The temperature of each zone of the melt spinning machine is controlled between 150-250°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a spinning new material and specifically relates to a preparation method of a composite elastic fiber. The preparation method provided by the invention comprises the following steps: 1) selecting polyolefin elastomer masterbatch, thermoplastic resin, silicone rubber, a radiation sensitizer and an antioxidant, mixing according to a certain proportion, sending into a twin-screw extruder, and performing extrusion and dicing to prepare polyolefin mixed masterbatch; 2) sending the polyolefin mixed masterbatch into a hopper of a melt spinning machine, spraying out by a spinning jet, cooling by a side air-blowing corridor, and winding onto a bobbin by a winding device to obtain nascent composite elastic fiber; 3) placing the prepared nascent composite elastic fiber under a radiation environment for treatment at the radiation dose of 50-500kGy to prepare the composite elastic fiber. The composite elastic fiber prepared by the method provided by the invention has the advantages of good mechanical properties, elastic elongation and elastic recovery ratio, and can be used for producing products with various specifications according to process adjustment so as to meet the development of various types of fabric.

Description

technical field [0001] The invention relates to a preparation method of a new textile material, in particular to a preparation method of a composite elastic fiber. Background technique [0002] With the rapid development of China's economy and the continuous improvement of people's living standards, people who love fashion feel oppressed by the busyness and competition in the city. Comfort is demanded. In order to meet the comfort of fabrics, designers choose elastic fibers, so the demand for elastic fibers has been in a strong growth stage in recent years. [0003] At present, the types of elastic fibers commonly used are relatively single, and they are only used in sportswear and underwear, which cannot meet people's diverse needs for elastic clothing fabrics. In recent years, scientists have been committed to developing a variety of elastic fibers to meet clothing for various occasions. fabric needs. Contents of the invention [0004] The technical problem to be solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/06D01F1/10D01F11/04D01D5/08D01D7/00
Inventor 王晓广张会娟黄年华张建强周晓洁
Owner 镇江优佰供应链科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap