Adhesive metal pond porcelain glaze

A technology of adhesion and porcelain, which is applied in the field of metal porcelain glazes, can solve the problems of unsatisfactory performance of porcelain bottom glaze and porcelain surface glaze, etc., and achieve strong adhesion, good corrosion resistance, and maintain the effect of corrosion resistance

Active Publication Date: 2015-12-09
佛山市中成釉料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the commonly used metal pond porcelain glazes have unsatisfactory properties of the porcelain bottom glaze and pond porcelain surface glaze.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A metal porcelain glaze material with strong adhesion, comprising a porcelain bottom glaze and a porcelain surface glaze;

[0035] Described pond porcelain surface glaze is made up of following components:

[0036] 1 part by mass of sodium tripolyphosphate,

[0037] 1 part by mass of phosphorus pentoxide,

[0038] 5 parts by mass of boron oxide,

[0039] 1 part by mass of cobalt oxide,

[0040] 1 part by mass of sodium fluorosilicate,

[0041] 4 parts by mass of zinc oxide,

[0042] 25 parts by mass of silicon carbide,

[0043] 1 part by mass of aluminum oxide,

[0044] 1 part by mass of calcium fluoride,

[0045] 30 parts by mass of monovalent basic oxide;

[0046] Described pond porcelain bottom glaze is made up of following components:

[0047] 1 part by mass of sodium pyrophosphate,

[0048] 2 parts by mass of barium molybdate,

[0049] 65 parts by mass of silicon dioxide,

[0050] 13 parts by mass of aluminum oxide,

[0051] 1.5 parts by mass of molybd...

Embodiment 2

[0061] A metal porcelain glaze material with strong adhesion, comprising a porcelain bottom glaze and a porcelain surface glaze;

[0062] Described pond porcelain surface glaze is made up of following components:

[0063] 2 parts by mass of sodium tripolyphosphate,

[0064] 2 parts by mass of phosphorus pentoxide,

[0065] 6 parts by mass of boron oxide,

[0066] 2 parts by mass of cobalt oxide,

[0067] 2 parts by mass of sodium fluorosilicate,

[0068] 5 parts by mass of zinc oxide,

[0069] 25 parts by mass of silicon carbide,

[0070] 1 part by mass of aluminum oxide,

[0071] 1 part by mass of calcium fluoride,

[0072] 30 parts by mass of monovalent basic oxide;

[0073] Described pond porcelain bottom glaze is made up of following components:

[0074] 1 part by mass of sodium pyrophosphate,

[0075] 2 parts by mass of barium molybdate,

[0076] 65 parts by mass of silicon dioxide,

[0077] 13 parts by mass of aluminum oxide,

[0078] 1.5 parts by mass of mo...

Embodiment 3

[0088] A metal porcelain glaze material with strong adhesion, comprising a porcelain bottom glaze and a porcelain surface glaze;

[0089] Described pond porcelain surface glaze is made up of following components:

[0090] 1.2 parts by mass of sodium tripolyphosphate,

[0091] 1.2 parts by mass of phosphorus pentoxide,

[0092] 5.6 parts by mass of boron oxide,

[0093] 1.2 parts by mass of cobalt oxide,

[0094] 1.2 parts by mass of sodium fluorosilicate,

[0095] 4.5 parts by mass of zinc oxide,

[0096] 25 parts by mass of silicon carbide,

[0097] 1 part by mass of aluminum oxide,

[0098] 1 part by mass of calcium fluoride,

[0099] 30 parts by mass of monovalent basic oxide;

[0100] Described pond porcelain bottom glaze is made up of following components:

[0101] 1 part by mass of sodium pyrophosphate,

[0102] 2 parts by mass of barium molybdate,

[0103] 65 parts by mass of silicon dioxide,

[0104] 13 parts by mass of aluminum oxide,

[0105] 1.5 parts b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metal enamel glaze with strong adherence, comprising an enamel base coat and an enamel cover glaze. According to the metal enamel glaze with strong adherence disclosed by the invention, the enamel base coat is coated on a green body, so that the green body has the characteristic of high-temperature resistance, and simultaneously has better corrosion resistance, and the glaze surface can keep the characteristic of corrosion resistance for a long period of time in a high-temperature environment.

Description

technical field [0001] The invention relates to a metal pond porcelain glaze material with strong adhesion. Background technique [0002] Currently commonly used metal pond porcelain glazes have unsatisfactory properties of the porcelain bottom glaze and the pond porcelain top glaze. Contents of the invention [0003] The object of the present invention is to provide a kind of strong adhesion metal pond porcelain glaze material, the porcelain underglaze coating on the embryo body can make the embryo body have the characteristics of high temperature resistance, and has good corrosion resistance at the same time. In a high temperature environment, it can maintain the characteristics of corrosion resistance for a long time. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of metal pond porcelain glaze material with strong adhesion, comprising pond porcelain bottom glaze and pond porcelain top glaze; [0005] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/22
Inventor 单佳单永其张文斌
Owner 佛山市中成釉料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com