Preparation and application methods of long-acting high-affinity softener prepared from essence microcapsules

A technology of essence microcapsule and application method, applied in the field of textile finishing, can solve the problems of not being able to adapt well to downstream products, not being able to control the aroma well, and the wrapping rate of the essence being low, etc., and achieving good storage stability, good effect and wide application The effect of adaptability

Active Publication Date: 2014-04-23
TIANJIN CHENGJIAN UNIV
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the microcapsules on the market usually have the disadvantages of low essence content, low essence encapsulation rate, short fragranc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] (1) Preparation of composite dispersant

[0027] Weigh 100 parts of non-ionic surfactant and 900 parts of deionized water, stir at 50 ° C to make it fully dissolved, and prepare an aqueous solution with a mass fraction of 10%;

[0028] Weigh 100 parts of non-ionic amphiphilic polymers and 900 parts of deionized water, stir at 90°C to fully dissolve them, and prepare an aqueous solution with a mass fraction of 10%;

[0029] Weigh 50-300 parts of nonionic surfactant aqueous solution and 1-50 parts of nonionic amphiphilic polymer aqueous solution and stir and mix at 50°C to obtain a composite dispersant, which is set aside;

[0030] (2) Preparation of etherified melamine resin solution

[0031] Stir and mix 70-110 parts of etherified melamine resin and 50-80 parts of deionized water in a beaker to obtain a dispersion of etherified melamine resin for later use;

[0032] (3) Preparation of essence microcapsule emulsion

[0033] Put 50-350 parts of the composite dispersant...

Embodiment 1

[0041] Weigh 10 parts of nonionic surfactant and 90 parts of deionized water, stir at 50°C to fully dissolve them, and prepare an aqueous solution with a mass fraction of 10%; weigh 1 part of nonionic amphiphilic polymer and 9 parts Deionized water was stirred at 90°C to fully dissolve it to prepare an aqueous solution with a mass fraction of 10%; the two were stirred and mixed at 50°C to obtain a composite dispersant.

[0042] The prepared composite dispersant, 490 parts of deionized water, 250 parts of essence, and 10 parts of glacial acetic acid solution were placed in a beaker, and emulsified with a high-shear dispersing emulsifier at a speed of 8000r / min to obtain a core material emulsion . Move the core material emulsion to a four-necked bottle, and under stirring conditions, add dropwise the etherified melamine resin dispersion that is fully stirred and miscible by 70 parts of etherified melamine resin and 80 parts of deionized water, and disperse for 10 minutes after d...

Embodiment 2

[0046] Weigh 30 parts of nonionic surfactant and 270 parts of deionized water, stir at 50°C to make them fully dissolve, and prepare an aqueous solution with a mass fraction of 10%; weigh 5 parts of nonionic amphiphilic polymer and 45 parts of Deionized water was stirred at 90°C to fully dissolve it to prepare an aqueous solution with a mass fraction of 10%; the two were stirred and mixed at 50°C to obtain a composite dispersant.

[0047] Put the prepared composite dispersant, 300 parts of deionized water, 350 parts of essence, and 20 parts of glacial acetic acid solution into a beaker, and emulsify with a high-shear dispersing emulsifier at a speed of 10,000 r / min to obtain a core material emulsion . Move the core material emulsion to a four-necked bottle, and under stirring conditions, add dropwise the etherified melamine resin dispersion that is fully stirred and miscible by 110 parts of etherified melamine resin and 50 parts of deionized water, and disperse for 30 minutes ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides preparation and application of a long-acting high-affinity softener prepared from essence microcapsules. The long-acting high-affinity essence microcapsule softener is prepared in the following steps: preparing a compound dispersant by using a nonionic surfactant and amphiphilic macromolecules, and preparing the essence microcapsules by taking essence as a core material and taking etherified melamine resin as a wall material; and preparing a fragrant microcapsule softener by taking the essence microcapsules as a raw material. The invention further provides an application method of the long-acting high-affinity fragrant microcapsule softener. The essence microcapsules prepared by a simple, convenient and environment-friendly method can be suitable for softeners, laundry detergents and the like of various ionic systems, the essence content can be 20-30 percent, and the solid content can be 22-35 percent. Compared with other commercially-available essence microcapsule, the solid content of the essence microcapsules can be 10-15 percent higher than that of the commercially available essence microcapsule products, the essence coating rate can be 60-70 percent, and the stability is good. Meanwhile, the long-acting high-affinity fragrant microcapsule softener prepared by taking the essence microcapsules as a raw material is good in the perfuming effect on fabrics and long in fragrance lasting time on fabrics, the fragrance can last for six months in a standing state, and high fragrance explosive power can be achieved by rubbing.

Description

technical field [0001] The invention belongs to the technical field of textile finishing, and specifically relates to a composite dispersant prepared from nonionic surfactants and amphiphilic macromolecules, with essence as the core material and etherified melamine resin as the wall material, which is prepared by an interfacial polymerization method The preparation and application method of the softener using long-acting high-affinity essence microcapsules can be adapted to softeners and laundry detergents of various ionic systems. Background technique [0002] Microcapsule technology refers to the technology of using natural or synthetic polymer materials to coat the target object with chemical or physical methods to form tiny particles with a core-shell structure with a diameter of 0.1-1000 μm. Microcapsules have the functions of protecting substances from environmental influences, reducing toxicity, masking bad taste, controlling core release, prolonging storage period, c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M23/12B01J13/16D06M101/06
Inventor 费学宁张宝莲赵洪宾谷迎春于妙卓
Owner TIANJIN CHENGJIAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap