Imitation wood material and method of making the same
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of imitating wood and slurry, which is applied in the field of imitating wood materials and its manufacturing, can solve the problems of easy deformation, easy to return brine, poor water resistance, etc., and achieve the effect of good water resistance
Active Publication Date: 2015-09-02
方志江
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The existing products made of imitation wood materials have the following deficiencies: first, they are easily deformed under long-term storage; second, they are easy to return to halogen after long-term storage; Fourth, it is easy to harden the body to swell or crack under long-term placement; fifth, the water resistance is poor
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0024] A kind of imitation wood material, including surface slurry and inner slurry, the surface slurry contains magnesium oxide and magnesium chloride with a mass ratio of 10:9:0.05:0.05:0.05:1.5:0.5:0.5:0.5:0.1:0.05 , ferrous sulfate, aluminum sulfate, phosphoric acid, fly ash, silica fume, quartz ash, talcum powder wood powder and sodium tripolyphosphate, the slurry contains a mass ratio of 10:9:0.05:0.05:0.05:1.5: 0.5:0.5:0.5:0.1:0.05 of magnesium oxide, magnesium chloride, ferrous sulfate, aluminum sulfate, phosphoric acid, fly ash, silica fume, quartz dust, talc wood chips and sodium tripolyphosphate.
[0025] In this embodiment, the lining slurry also includes the crushed material of the product side material, and the mass ratio of it to wood chips is 1:1.
[0026] The manufacture method of imitation wood material described in above embodiment, comprises the following steps:
[0027] Step 1, prepare the surface slurry, adjust 9kg of magnesium chloride to 25 degrees of ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a wood-imitation material which comprises an outer sizing agent and in inner sizing agent, wherein the outer sizing agent comprises magnesium oxide, magnesium chloride, ferrous sulfate, aluminum sulfate, phosphoric acid, fly ash, silica fume, quartz grey, talcum powder, wood powder and sodium tripolyphosphate according the mass ratio of 10:9:0.05:0.05:0.05:1.5:0.5:0.5:0.5:0.1:0.05, and the inner sizing agent comprises magnesium oxide, magnesium chloride, ferrous sulfate, aluminum sulfate, phosphoric acid, fly ash, silica fume, quartz grey, talcum powder, sawdust and sodium tripolyphosphate according to the mass ratio of 10:9.0:0.05:0.05:0.05:1.5:0.5:0.5:0.5:0.1:0.05. The invention further discloses a manufacturing method for the wood-imitation material. The wood-imitation material disclosed by the invention is prevented from deformation, efflorescing, scumming, and whitening, is good in water resistance, and hardening body swelling or cracking does not appear.
Description
technical field [0001] The invention relates to a wood-like material and a manufacturing method thereof. Background technique [0002] The existing products made of imitation wood materials have the following deficiencies: first, they are easily deformed under long-term storage; second, they are easy to return to halogen after long-term storage; Fourth, the hardened body is prone to bursting or cracking under long-term storage; fifth, the water resistance is poor. Contents of the invention [0003] Based on this, aiming at the above problems, the present invention proposes an imitation wood material with the functions of environmental protection, fire prevention, moth prevention, anticorrosion, heat insulation, heat preservation and sound insulation and its manufacturing method. [0004] In order to solve the above-mentioned technical problems, the present invention firstly provides a kind of imitation wood material, comprising surface slurry and inner slurry, the surface...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more