Anticorrosion wear-resistance coating

An anti-corrosion and wear-resistant coating technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of small friction loss and inability to meet demand, and achieve the effect of enhancing wear resistance, prolonging service life, and excellent wear resistance.

Active Publication Date: 2014-05-07
ANHUI JINDUN PAINT
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Anti-corrosion and wear-resistant coatings are an indispensable coating in paints and coatings. The annual economic losses caused by corrosion in the world are about 1 trillion US dollars, which is the sum of the losses caused by earthquakes, fires, and wind disasters. Anti-corrosion and wear-resistant coatings are the most effective. , the most economical and most commonly used anti-corrosion method has received widespread attention at home and abroad. Under normal conditions, anti-corrosion and wear-resistant coatings can prevent corrosion of met

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] In this embodiment, a kind of anticorrosion wear-resisting paint, its raw material comprises by weight: polyvinyl acetal modified phenolic resin 12 parts, polyvinyl acrylate emulsion 8.9 parts, lead chromate 4.4 parts, cellulose hydroxypropyl 11 parts of methyl ether, 6 parts of m-xylene, 20.3 parts of nano-aluminum powder, 3.3 parts of aluminum hydroxide, 16.8 parts of nano-calcium oxide, and 4.2 parts of zinc oxide; among them, cellulose hydroxypropyl methyl ether passed through a 100-mesh sieve The pass rate is not less than 98%, the methoxyl value is 22.5%, and the hydroxypropyl value is 10.3%; the particle size of nano-aluminum powder is 30-60nm, and the particle size of nano-calcium oxide is 50nm-200nm.

Embodiment 2

[0016] In this embodiment, a kind of anticorrosion wear-resisting paint, its raw material comprises by weight: polyvinyl acetal modified phenolic resin 13.7 parts, polyvinyl acrylate emulsion 8.7 parts, lead chromate 6 parts, cellulose hydroxypropyl 9.5 parts of methyl ether, 6.6 parts of m-xylene, 19.4 parts of nano-aluminum powder, 3.7 parts of aluminum hydroxide, 15.6 parts of nano-calcium oxide, and 5 parts of zinc oxide; among them, cellulose hydroxypropyl methyl ether passed through a 100-mesh sieve The pass rate is not less than 98%, the methoxyl value is 24%, and the hydroxypropyl value is 10%; the particle size of nano-aluminum powder is 30-60nm, and the particle size of nano-calcium oxide is 50nm-200nm.

Embodiment 3

[0018] In this embodiment, a kind of anticorrosion wear-resisting paint, its raw material comprises by weight: polyvinyl acetal modified phenolic resin 15 parts, polyvinyl acrylate emulsion 8.5 parts, lead chromate 8 parts, cellulose hydroxypropyl 7 parts of methyl ether, 8.4 parts of m-xylene, 18.5 parts of nano-aluminum powder, 4.3 parts of aluminum hydroxide, 14.7 parts of nano-calcium oxide, and 5.8 parts of zinc oxide; among them, cellulose hydroxypropyl methyl ether passed through a 100-mesh sieve The pass rate is not less than 98%, the methoxyl value is 25%, and the hydroxypropyl value is 9.7%; the particle size of nano-aluminum powder is 30-60nm, and the particle size of nano-calcium oxide is 50nm-200nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anticorrosion wear-resistance coating, comprising the following components in parts by weight: 12-20 parts of polyvinyl acetal modified phenolic resin, 8-9 parts of polyacrylic acid vinyl ester emulsion, 3-13 parts of lead chromate, 3-12 parts of cellulose hydroxypropyl methyl ether, 6-10 parts of m-xylene, 15-21 parts of nano aluminite powder, 3-7 parts of aluminium hydroxide, 12-17 parts of nano calcium oxide and 4-8 parts of zinc oxide. The anticorrosion wear-resistance coating has the advantages of good anticorrosion performance, excellent wear resistance, long service life and low cost.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an anti-corrosion and wear-resistant coating. Background technique [0002] Anti-corrosion and wear-resistant coatings are an indispensable coating in paints and coatings. The annual economic loss caused by corrosion in the world is about 1 trillion US dollars, which is the sum of the losses caused by earthquakes, fires, and wind disasters. Anti-corrosion and wear-resistant coatings are the most effective. , the most economical and most commonly used anti-corrosion method has received widespread attention at home and abroad. Under normal conditions, anti-corrosion and wear-resistant coatings can prevent corrosion of metals and prolong the service life of non-ferrous metals. The anti-corrosion function lies in the coating The shielding effect, resistance effect, wet adhesion, chemical passivation and cathodic protection. Although many kinds of anti-corrosion and wear-resistant co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D161/14C09D133/08C09D101/26C09D7/12C09D5/10
Inventor 梅长林张国胜朱恒横
Owner ANHUI JINDUN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap