Filter paper for environmental-friendly automobile filter and preparation method of filter paper

A filter and filter paper technology, applied in chemical instruments and methods, filter paper, separation methods, etc., to achieve the effects of improved dynamic performance, obvious comprehensive effect and simple process

Inactive Publication Date: 2014-05-07
北京联飞翔科技股份有限公司
View PDF6 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problems existing in the existing filter paper, the present invention aims to provide a new type of filter paper coating material for automotive environmental pr...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filter paper for environmental-friendly automobile filter and preparation method of filter paper
  • Filter paper for environmental-friendly automobile filter and preparation method of filter paper
  • Filter paper for environmental-friendly automobile filter and preparation method of filter paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1. Preparation of far-infrared ceramic powder:

[0039] 0.8kg of magnesium tourmaline ultrafine powder with a median diameter of 0.45μm, and La with a median diameter of 0.36μm 2 o 3 0.1kg, Fe 2 o 3 0.2kg, MnO 2 0.3kg, Co 2 o 3 0.2kg, CuO0.2kg.

[0040] 2. Preparation of filter paper:

[0041] 1) Add the silane coupling agent and diluent to the far-infrared ceramic powder and stir for 20 minutes, let it stand for 8 minutes, and dry at 100°C; improve the surface properties of the ceramic powder, make it better integrated with the pulp, and increase the powder in the paper of firmness.

[0042] 2) Add the far-infrared ceramic powder, sepiolite nanofibers, and sizing agent after surface pretreatment in step 1) to the beaten wood pulp at the same time, use mechanical stirring to make it evenly mixed, and then add water to adjust the concentration to 3.2% , to prepare a slurry;

[0043] 3) Slurry forming, pressing, drying to 92% dryness, calendering and finishing t...

Embodiment 2

[0053] 1. Preparation of far-infrared ceramic powder:

[0054] 2 kg of ferrite ultrafine powder with a median diameter of 1.4 μm, and CeO with a median diameter of 0.08 μm 2 0.2kg, Fe 2 o 3 0.4kg, MnO 2 0.2kg,Co 2 o 3 0.8kg, CuO0.1kg.

[0055] 2. Preparation of filter paper:

[0056] Filter paper was prepared according to the method of Example 1. Among them, high-aspect-ratio sepiolite nanofibers were prepared by high-speed airflow technology, with a diameter of 96 nm and a length of 0.21 μm.

[0057] Among them, the distribution ratio of each group is shown in Table 3.

[0058] The proportioning of table 3 embodiment 2

[0059]

[0060] The results of paper performance testing are shown in Table 4.

[0061] The filter paper performance measurement result of table 4 embodiment 2

[0062]

[0063] The diesel filter made of this filter paper has been tested in practice, and the exhaust pollutants are reduced by 34%, and the emission reaches the Euro IV standard....

Embodiment 3

[0065] 1. Preparation of far-infrared ceramic powder:

[0066] 3.1kg of ultra-fine tourmaline powder with a median diameter of 1.1μm, Ce with a median diameter of 1.7μm 2 o 3 0.2kg, Fe 2 o 3 0.7kg, MnO 2 0.4kg, Co 2 o 3 0.2kg, CuO1.2kg.

[0067] 2. Preparation of filter paper:

[0068] Filter paper was prepared according to the method of Example 1. Among them, high-aspect-ratio sepiolite nanofibers were prepared by high-speed airflow technology, with a diameter of 92 nm and a length of 0.22 μm.

[0069] Among them, the distribution ratio of each group is shown in Table 5.

[0070] The proportioning of table 5 embodiment 3

[0071]

[0072] The results of paper performance testing are shown in Table 6.

[0073] The filter paper property measurement result that table 6 embodiment 3 coating materials prepare

[0074]

[0075] The gasoline filter made of this filter paper has been tested in practice, and the exhaust pollutants are reduced by 27%, and the emission...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Median diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to filter paper for an environmental-friendly automobile filter. The filter paper for the environmental-friendly automobile filter is prepared from the following components in parts by weight: 1-5 parts of far infrared ceramic powder, 2-20 parts of sepiolite nanofibers, 0.8-1.6 parts of a silane coupling agent, 0.8-1.6 parts of a diluent, 9-20 parts of a sizing agent and 60-96 parts of wood pulp. Air, fuel oil and engine oil filters made of the filter paper are obvious in comprehensive effect; pollutants generated by exhaust gas emission of an automobile are reduced by 16-47%; the dynamic performance is improved by 6-12%; fuel oil can be saved by 2-5%; the emission standard reaches the European IV standard.

Description

technical field [0001] The invention relates to filter paper for a filter, in particular to a filter paper with an environmental protection function and a manufacturing method thereof, belonging to the technical field of automobile environmental protection. Background technique [0002] The rapid development of the automobile industry has brought prosperity and convenience to mankind. However, with the sharp increase in the number of automobiles, the environmental problems caused by automobile emissions have emerged. Nitrogen oxides, volatile organic compounds, and inhalable particulate matter in emissions account for 66%, 90%, and 26% of all pollution sources in central urban areas, respectively. Automobile filters have the function of filtering fuel, air and engine oil. The filter element is its main filtering part and undertakes the filtering work. The research on filter materials is directly related to the filtering effect. In recent years, the intensification of air po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/08D21H13/38D21H17/68D21H21/16D21H21/06
Inventor 崔庆祥金伟
Owner 北京联飞翔科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap