Car brake block mixed with piemarker fiber and preparing method of car brake block

A technology of brake pads and fibers, applied in the field of car brake pads and their preparation, can solve the problems of not developing to pay attention to comfort, environmental protection, braking effect and safety, etc.

Inactive Publication Date: 2014-06-04
QINGDAO UNIV
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the development of domestic automobile brake pads is still at the stage of focusing on braking effect and safety, and has not developed to the stage of emphasizing comfort and environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The ratio of each component in formula 1 is:

[0049] name

Proportion

Abutilon fiber

10％

Aramid pulp

3.5％

Lepenas fiber

15％

ceramic fiber fleece

6％

Rare earth modified phenolic resin

16％

nonionic polyacrylamide

2％

A silane coupling agent

2％

Titanate coupling agent

2％

Graphite fluoride

3.5％

soft coke

5％

Molybdenum disulfide

1.5％

Flake aluminum powder

2.5％

Ultrafine silica powder

15％

titanate platelets

16％

[0050] Process using recipe 1:

[0051] 1. Batching, mixing, batching in the automatic batching system according to the ratio of formula 1, and

[0052] Stir in a stirrer for 5-8 minutes at a speed of 400-600 r / min.

[0053] 2. Cold pressing, pour the mixed raw materials into the mold, and preliminarily pre-press molding on the pre-pressing machine;

[0054] 3. Hot pressing, transfer the prel...

Embodiment 2

[0059] The ratio of each component in formula 2 is:

[0060] name

Proportion

Abutilon fiber

12％

Aramid pulp

3.5％

Lepenas fiber

15％

ceramic fiber fleece

6％

Rare earth modified phenolic resin

13％

nonionic polyacrylamide

2％

A silane coupling agent

2％

Titanate coupling agent

2％

Graphite fluoride

3.5％

soft coke

5％

Molybdenum disulfide

1.5％

Flake aluminum powder

2.5％

Ultrafine silica powder

16％

titanate platelets

16％

[0061] Process using recipe 2:

[0062] 1. Batching and mixing, according to the ratio of formula 2, batching is carried out in the automatic batching system, and stirred in the mixer for 5-8 minutes, the speed is 400-600r / min.

[0063] 2. Cold pressing, pour the mixed raw materials into the mold, and preliminarily pre-press molding on the pre-pressing machine;

[0064] 3. Hot pressing, transf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a car brake block with a piemarker fiber and a preparing method of the car brake block. The car brake block comprises the natural piemarker fiber, aramid fiber pulp, rare-earth modified phenolic resin, a friction performance modifier, padding and the like, and comprises, by weight, 30-35 parts of reinforced fiber, 13-16 parts of binding agent, 9-12 parts of friction performance modifier and 40-45 parts of padding. The piemarker fiber on which the alkali treatment and ultrasonic treatment are carried out is low in price, light, high in specific strength, specific modulus and tensile strength and good in abrasion resistance and has other superior properties, and belongs to renewable resources. The car brake block prepared under the optimal technological condition and mixed with the piemarker fiber has a stable friction coefficient, a good brake effect and brake smoothness, is low in noise, good in comfort and friendly to the environment and is an ideal environment-friendly friction material.

Description

technical field [0001] The invention relates to the technical field of friction materials for car braking, in particular to a car brake pad mixed with avelphine fibers and a preparation method thereof. Background technique [0002] Friction materials are functional accessories used in automobiles and machinery for transmission, braking, deceleration, steering, parking, etc. According to the function and installation position, it is mainly divided into brake lining and clutch facing. In the past 20 years, the composition and manufacturing process of the friction materials used in vehicles represented by automobiles have undergone significant changes. The new friction materials have better resistance to thermal degradation, longer life and are more conducive to environmental protection and human beings. healthy. Friction materials are key safety parts in the automobile industry. The starting, braking and parking of automobiles are all inseparable from friction materials. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16D69/02C09K3/14
Inventor 姜著川
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap