A high-purity, waste lead paste technology, applied in chemical instruments and methods, nanotechnology, carboxylate preparation, etc., can solve the problem of low purity of lead powder

Active Publication Date: 2014-06-25
湖北金洋冶金股份有限公司 +1
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process ignores the impurities such as Fe and Cu in the waste lead paste. During the complexation process of organic acids, impurities such as Fe and Cu will also complex with organic acids to form in...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-purity lead acetate and nanometer lead powder from waste lead paste
  • Method for preparing high-purity lead acetate and nanometer lead powder from waste lead paste
  • Method for preparing high-purity lead acetate and nanometer lead powder from waste lead paste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] like figure 1 Shown, according to the preparation method of high-purity lead acetate trihydrate of the present invention, may further comprise the steps:

[0056] (1) After the waste lead-acid battery was acid-poured, it was crushed, sorted, and screened to obtain lead paste; take 100 g of waste lead paste, add 20 g of sodium carbonate, 1 g of sodium bicarbonate and 300 g of water In the compound desulfurization agent solution (waste lead paste: sodium carbonate: sodium bicarbonate: solvent water = 1:0.2:0.01:3), stir and react at room temperature for 4 hours, filter and separate, the obtained filter residue is 92g of desulfurization lead paste, and return the filtrate to The compound desulfurizer solution is reused. The sulfur content in the desulfurized lead paste was measured, and the primary conversion rate was calculated to be 95.33%.

[0057] (2) Add 9.2 g of acetic acid solution with a mass concentration of 10% to the obtained 92 g of desulfurized lead paste (t...

Embodiment 2

[0060] Compared with Example 1, its difference is that the consumption of medicament wherein has been changed, comprises the following steps:

[0061] (1) After the waste lead-acid battery is poured acid, it is crushed and sorted, and the lead paste is obtained by screening. Get waste lead plaster 100 g, add the compound desulfurizer solution (waste lead plaster: sodium carbonate: sodium bicarbonate: solvent water=1:0.5: 5:20), stirred and reacted at room temperature for 6 hours, filtered and separated, the obtained filter residue was desulfurized lead paste, and the filtrate was returned to the composite desulfurized agent solution for reuse. The sulfur content in the desulfurized lead paste was measured, and the primary conversion rate was calculated to be 99.37%.

[0062] (2) Add 482.5 g of acetic acid solution with a mass concentration of 30% to the obtained 96.5 g of desulfurized lead paste (the mass ratio of desulfurized lead paste: acetic acid solution is 1:5) and 10 g...

Embodiment 3

[0065] Compared with Example 1, its difference is that the consumption of medicament wherein has been changed, comprises the following steps:

[0066] (1) After the waste lead-acid battery is poured acid, it is crushed and sorted, and the lead paste is obtained by screening. Get waste lead plaster 100 g, add the compound desulfurizer solution (waste lead plaster: sodium carbonate: sodium bicarbonate: solvent water=1:0.4: 2:10), stirred and reacted at room temperature for 6 hours, filtered and separated, the obtained filter residue was desulfurized lead paste, and the filtrate was returned to the composite desulfurized agent solution for reuse. The conversion rate of the obtained desulfurized lead paste was analyzed, and the primary conversion rate was 99.60% through calculation.

[0067] (2) Add 290.1 ​​g of acetic acid solution with a mass concentration of 30% to 96.7 g of the obtained desulfurized lead paste (the mass ratio of desulfurized lead paste: acetic acid solution i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing high-purity lead acetate and nanometer lead powder, and particularly relates to a method for preparing high-purity lead acetate and nanometer lead powder from waste lead paste of a waste lead acid battery. The method comprises the following steps: carrying out solid-liquid separation after adding the waste lead paste to a solution with a desulfurizer to desulfurize, so as to obtain waste lead paste; adding an acetic acid solution and a solution as a reducing agent to the obtained desulfurized lead paste, so as to obtain a soluble acid solution containing lead; adding a glacial acetic acid to the obtained soluble acid solution containing lead to carry out recrystallization and purification, so as to obtain high-purity lead acetate trihydrate crystal and a glacial acetic acid solution; and putting the high-purity lead acetate crystal into a tube furnace or a muffle furnace to roast, so as to obtain the nanometer lead powder. The lead acetate and the nanometer lead powder are prepared according to the method disclosed by the invention; the method is simple in production flow, low in energy consumption, high in lead recovery rate, free of sulfur dioxide pollution, and relatively low in environmental pollution, and can achieve discharge free of pollutants, and the economic performance is superior to that of a lead powder preparation process of a traditional pyrogenic process or a general wet process.

Description

technical field [0001] The invention relates to a preparation method of high-purity lead acetate and nano-lead powder, in particular to a method for preparing high-purity lead acetate and nano-lead powder by using waste lead paste of waste lead-acid batteries, belonging to the technical field of recycled lead production. [0002] Background technique [0003] Lead-acid batteries are the most used secondary batteries in the world, and the amount of lead consumed in the production of lead-acid batteries accounts for more than 82% of the total lead consumption. With the continuous scrapping of lead-acid batteries, the output of waste lead-acid batteries is increasing. Waste lead-acid batteries are usually composed of four major parts: waste lead paste accounts for 30%~40%, lead and lead alloy grids account for 24%~30%, waste plastic packaging and diaphragm paper and other organic matter account for 22%~30%, waste Electrolyte accounts for 11%~30%. As the main component of was...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C53/10C07C51/41B22F9/22B82Y40/00H01M10/54
CPCB22F9/30B82Y40/00C07C51/412C07C53/10C22B13/045Y02W30/84
Inventor 杨家宽孙晓娟李富元李瑞霞周峰张伟朱新锋胡雨辰梁莎
Owner 湖北金洋冶金股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap