Rubber adhesive and preparation method thereof

A rubber adhesive and liquid rubber technology, applied in the direction of adhesives, rubber derivatives, adhesive types, etc., can solve the problems of insufficient adhesion, poor washing performance, easy to pollute the battery pool, etc., to achieve good sealing performance, Excellent anti-sag, easy construction effect

Active Publication Date: 2014-06-25
依多科(常熟)汽车材料有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Most of the existing automotive rubber adhesives use polysulfide rubber or solid rubber, such as neoprene, styrene-butadiene rubber, nitrile rubber, butyl rubber, etc., which have good shockproof effect, oil resistance and corrosion resistance, but solid rubber Type adhesi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber adhesive and preparation method thereof
  • Rubber adhesive and preparation method thereof
  • Rubber adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0034] Example 1

[0035] A rubber adhesive, in terms of weight percentage, the rubber adhesive consists of the following components:

[0036]

[0037] The preparation method of the above rubber adhesive includes the following steps:

[0038] (1) Put liquid rubber into the reaction kettle first, and the liquid rubber is obtained by mixing liquid polybutadiene and hydroxyl-terminated liquid polybutadiene uniformly;

[0039] (2) Add sulfur, accelerator ZBEC, antioxidant, dehumidifier, carbon black and zinc oxide to the liquid rubber obtained in step (1) in sequence, and stir for 10 minutes under vacuum;

[0040] (3) Open the reactor, add heavy calcium carbonate to the mixture obtained in step (2) above, stir for 10 minutes in vacuum, then open the reactor, add the coated calcium carbonate and talc to the reactor, and stir for 10 minutes in vacuum;

[0041] (4) Open the reactor, scrape off the mixture obtained in the above step (3) attached to the wall of the reactor, and stir under vacuum ...

Example Embodiment

[0047] Example 2

[0048] A rubber adhesive, in terms of weight percentage, the rubber adhesive consists of the following components:

[0049]

[0050] The preparation method of the above rubber adhesive includes the following steps:

[0051] (1) Put liquid rubber into the reaction kettle first, which is obtained by mixing liquid polybutadiene and maleic anhydride-terminated liquid polybutadiene uniformly;

[0052] (2) Sulfur, accelerator ZDEC, antioxidant, foaming agent, dehumidifier, carbon black and zinc oxide are sequentially added to the liquid rubber obtained in step (1), and stirred for 10 minutes under vacuum;

[0053] (3) Open the reactor, add heavy calcium carbonate to the mixed solution obtained in step (2) above, stir under vacuum for 10 minutes, then open the reactor, add the coated calcium carbonate, talc and mica powder to the reactor, vacuum Stir for 10min;

[0054] (4) Open the reactor, scrape off the mixture obtained in the above step (3) attached to the wall of the re...

Example Embodiment

[0060] Example 3

[0061] A rubber adhesive, in terms of weight percentage, the rubber adhesive consists of the following components:

[0062]

[0063] The preparation method of the above rubber adhesive includes the following steps:

[0064] (1) Put liquid rubber into the reaction kettle first, and the liquid rubber is obtained by mixing liquid polybutadiene and liquid polybutadiene terminated by epoxy groups;

[0065] (2) Add sulfur, accelerator ZBEC, antioxidant, dehumidifier, carbon black and zinc oxide to the liquid rubber obtained in step (1) in sequence, and stir for 10 minutes under vacuum;

[0066] (3) Open the reactor, add heavy calcium carbonate to the mixture obtained in step (2) above, stir for 10 minutes in vacuum, then open the reactor, add the coated calcium carbonate and mica powder to the reactor, and stir for 10 minutes in vacuum;

[0067] (4) Open the reactor, scrape off the mixture obtained in the above step (3) attached to the wall of the reactor, and stir under vac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Shear strengthaaaaaaaaaa
Shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a rubber adhesive which comprises the following components in percentage by weight: 20-40 percent of liquid rubber, 2-6 percent of a vulcanizing agent, 0.1-0.6 percent of an accelerator, 0.4-0.8 percent of an antioxidant, 0-3 percent of a foaming agent, 1-3 percent of a dehumidifying agent, 0-3 percent of a thixotropic agent, 1-2 percent of zinc oxide and 40-55 percent of fillers, wherein the sum of the weight percentage of all the components is 100%. The invention also provides a preparation method of the rubber adhesive. The rubber adhesive disclosed by the invention has good status retention property and oil level steel plate stationarity when not cured, and a cured material has high intensity, good airtightness, shock absorptivity, noise reduction performance and the like, so the rubber adhesive can be widely applicable to adhesion and sealing of metal plates in automobile and engineering machinery industries.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and relates to an adhesive used for bonding metal sheets in the automobile and machinery industries, in particular to a rubber adhesive and a preparation method thereof. Background technique [0002] Automobile plays an extremely important role in people's daily life and work, and is an indispensable means of transportation and transportation for modern production, modern economic construction and national defense construction. With the rapid development of science and technology, the types and performance of automobiles are also increasing and tending to be perfect, and people's requirements for the reliability of automobile quality and technological advancement are also constantly increasing. [0003] Automobile adhesive sealant is an important auxiliary material required for automobile production. Such materials should be used in structural reinforcement, fastening and anti-loosening, sealin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J109/00C09J115/00C09J11/04C09J11/06
CPCY02P20/141
Inventor 舒元宏白长科朱爱军毛晨峰
Owner 依多科(常熟)汽车材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap