Glass oil paint

A paint and glass technology, applied in the field of paint, can solve the problems of weak acid and alkali resistance, cannot be used on glass, and weak paint adhesion, and achieves strong acid and alkali resistance, water resistance, strong adhesion, and production. cost-effective effect

Active Publication Date: 2014-07-02
SHANGHAI DABAO CHEM PROD
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] General paint adhesion is not strong, acid resistance and alkali resistance are not strong, can not be used on glass, there are defects to a certain extent, can not meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of glass paint of the present embodiment, the parts by weight of its components are: 27 parts of modified drying oils, 17 parts of hydroxyethyl cellulose, 6 parts of butyl stearate, 15 parts of water-soluble resins, shellac 8 parts of resin, 6 parts of lacquer resin, 15 parts of zinc phosphate, 6 parts of zinc molybdate, 16 parts of mica powder, 4 parts of citric acid, 4 parts of anti-corrosion and anti-rust emulsion, 8 parts of thinner.

[0013] The modified drying oil is prepared by polycondensation of phthalic anhydride, glycerol and pentaerythritol in a ratio of 3:2:2.

[0014] The anti-corrosion and anti-rust emulsion is a mixture of paint powder, maleic anhydride, zeolite powder, rosin phenolic resin, and mica powder, and the mixing ratio is 1:2:1:2:0.5.

[0015] The thinner is a polyurethane paint solvent, and the polyurethane paint solvent is composed of xylene.

Embodiment 2

[0017] A kind of glass paint of the present embodiment, the parts by weight of its components are: 20 parts of modified drying oils, 12 parts of hydroxyethyl cellulose, 3 parts of butyl stearate, 12 parts of water-soluble resins, shellac 5 parts of resin, 3 parts of lacquer resin, 12 parts of zinc phosphate, 4 parts of zinc molybdate, 11 parts of mica powder, 1 part of citric acid, 2 parts of anti-corrosion and anti-rust emulsion, 5 parts of thinner.

[0018] The modified drying oil is prepared by polycondensation of phthalic anhydride, glycerol and pentaerythritol in a ratio of 3:2:2.

[0019] The anti-corrosion and anti-rust emulsion is a mixture of paint powder, maleic anhydride, zeolite powder, rosin phenolic resin, and mica powder, and the mixing ratio is 1:2:1:2:0.5.

[0020] The thinner is a polyurethane paint solvent, and the polyurethane paint solvent is composed of xylene.

Embodiment 3

[0022] A kind of glass paint of the present embodiment, the parts by weight of its components are: 26 parts of modified drying oils, 15 parts of hydroxyethyl cellulose, 4 parts of butyl stearate, 13 parts of water-soluble resins, shellac 6 parts of resin, 5 parts of lacquer resin, 14 parts of zinc phosphate, 5 parts of zinc molybdate, 12 parts of mica powder, 2 parts of citric acid, 3 parts of anti-corrosion and anti-rust emulsion, 6 parts of thinner.

[0023] The modified drying oil is prepared by polycondensation of phthalic anhydride, glycerol and pentaerythritol in a ratio of 3:2:2.

[0024] The anti-corrosion and anti-rust emulsion is a mixture of paint powder, maleic anhydride, zeolite powder, rosin phenolic resin, and mica powder, and the mixing ratio is 1:2:1:2:0.5.

[0025] The thinner is a polyurethane paint solvent, and the polyurethane paint solvent is composed of xylene.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an glass oil paint which comprises the following components in parts by weight: 20-27 parts of modified dry oil, 12-17 parts of hydroxyethyl cellulose, 3-6 parts of butyl stearate, 12-15 parts of water-soluble resin, 5-8 parts of lac resin, 3-6 parts of lacquer resin, 12-15 parts of zinc phosphate, 4-6 parts of zinc molybdate, 11-16 parts of mica powder, 1-4 parts of citric acid, 2-4 parts of antiseptic antirust emulsion and 5-8 parts of thinners. According to the glass oil paint, raw materials are common in the market, so that the production cost is low, and the glass oil paint has strong adhesive force, acid and alkali resistance and water resistance, can effectively remove and prevent iron rust due to addition of the antiseptic antirust emulsion, and can be smeared on glass, so as to meet the demands of people.

Description

technical field [0001] The invention relates to a paint, in particular to a glass paint. Background technique [0002] Paint is a chemical mixture coating that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. Paint is a coating made of raw materials such as iron oxide or resin to decorate and protect objects. [0003] General paint adhesion is not strong, acid resistance and alkali resistance are not strong, can not be used on glass, there are defects to a certain extent, and cannot meet people's needs. Contents of the invention [0004] The purpose of this invention is to provide a kind of glass paint with strong adhesion, strong acid resistance and alkali resistance, which can be used on glass. [0005] In order to achieve the above object, the present invention is achieved through the following technical solutions: a glass paint, the parts by weight of its components are: 20-27 parts of modified drying oil, 12-17 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D101/28C09D193/02C09D7/12
Inventor 蒋玉俊
Owner SHANGHAI DABAO CHEM PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com