Environment-friendly electric wire and cable material

A kind of wire and cable material, environmental protection technology, applied in the field of wire and cable industry, can solve environmental pollution and other problems, and achieve the effect of perfect performance, improved performance and good weather resistance

Inactive Publication Date: 2014-07-09
KUNSHAN XINZHICHENG ELECTRONICS TECH
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the chlorine contained in PVC, it will cause environmental pollution during the production process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] According to a kind of environment-friendly electric wire and cable material of this embodiment, this electric wire and cable material comprises following weight components:

[0037] PP: 100 copies;

[0038] PET: 31 copies;

[0039] ACR resin: 8 parts;

[0040] Polypropylene fiber: 8 parts;

[0041] 1:1 mixture of EPDM rubber and ethylene-butylene elastomer: 30 parts;

[0042] Plasticizer: epoxy soybean oil: 31 parts;

[0043] Stabilizer: isooctyl trimercaptoacetate antimony: 1.5 parts;

[0044] Lubricant: a mixture of paraffin oil and paraffin wax with a weight component ratio of 1:2: 8 parts;

[0045] Talcum powder: 10 parts;

[0046] Flame retardant: a mixture of zinc borate and nano-scale antimony trioxide with a weight component ratio of 1:3: 7.5 parts;

[0047] Polyisobutenyl succinimide: 1.5 parts;

[0048] Titanium dioxide: 0.8 parts.

[0049] The preparation method of an environment-friendly wire and cable material is as follows: batching according to ...

Embodiment 2

[0051] According to a kind of environment-friendly electric wire and cable material of this embodiment, this electric wire and cable material comprises following weight components:

[0052] PP: 100 copies;

[0053] PET: 33 parts;

[0054] ACR resin: 9 parts;

[0055] Polypropylene fiber: 10 parts;

[0056] 1:1 mixture of EPDM rubber and ethylene-butylene elastomer: 33 parts;

[0057] Plasticizer: epoxy soybean oil: 32 parts;

[0058] Stabilizer: isooctyl trimercaptoacetate antimony: 2 parts;

[0059] Lubricant: a mixture of paraffin oil and paraffin wax with a weight component ratio of 1:2: 10 parts;

[0060] Talcum powder: 10 parts;

[0061] Flame retardant: a mixture of zinc borate and nano-scale antimony trioxide with a weight component ratio of 1:3: 7.5 parts;

[0062] Polyisobutenyl succinimide: 2 parts;

[0063] Titanium dioxide: 0.8 parts.

[0064] The preparation method of an environment-friendly wire and cable material is as follows: batching according to the f...

Embodiment 3

[0066] According to a kind of environment-friendly electric wire and cable material of this embodiment, this electric wire and cable material comprises following weight components:

[0067] PP: 100 copies;

[0068] PET: 35 copies;

[0069] ACR resin: 10 parts;

[0070] Polypropylene fiber: 12 parts;

[0071] 1:1 mixture of EPDM rubber and ethylene-butylene elastomer: 35 parts;

[0072] Plasticizer: epoxy soybean oil: 33 parts;

[0073] Stabilizer: isooctyl trimercaptoacetate antimony: 2.5 parts;

[0074] Lubricant: a mixture of paraffin oil and paraffin wax with a weight component ratio of 1:2: 12 parts;

[0075] Talcum powder: 10 parts;

[0076] Flame retardant: a mixture of zinc borate and nano-scale antimony trioxide with a weight component ratio of 1:3: 7.5 parts;

[0077] Polyisobutenyl succinimide: 2.5 parts;

[0078] Titanium dioxide: 0.8 parts.

[0079] The preparation method of an environment-friendly wire and cable material is as follows: batching according ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly electric wire and cable material. The environment-friendly electric wire and cable material comprises following ingredients, by weight, 100 parts of PP, 30 to 35 parts of PET, 8 to 10 parts of ACR resin, 8 to 12 parts of polypropylene fiber, 30 to 35 parts of a mixture of ethylene-propylene-diene monomer and ethylene / butene elastomer, 31 to 33 parts of a plasticizer, 1.5 to 2.5 parts of a stabilizing agent, 8 to 12 parts of a lubricant, 10 parts of talc, 7.5 parts of a fire retardant, 1.5 to 2.5 parts of polyisobutylene succinimide, and 0.8 part of titanium dioxide. Main materials PP and PET, and auxiliary reagents of the environment-friendly electric wire and cable material are all environment-friendly materials, so that environmental protection performance of the environment-friendly electric wire and cable material is excellent.

Description

technical field [0001] The invention relates to an environment-friendly wire and cable material, which belongs to the wire and cable industry. Background technique [0002] Wire and cable is a wire product used to transmit electric (magnetic) energy, information and realize electromagnetic energy conversion. As the main carrier of power transmission, wire and cable are widely used in electrical equipment, lighting circuits, household appliances, etc. The quality of wire and cable directly affects the quality of the project and the safety of consumers' lives and property. Although the wire and cable industry is only a supporting industry, it accounts for 1 / 4 of the output value of China's electrical industry. It has a wide variety of products and a wide range of applications, involving industries such as electric power, construction, communications, and manufacturing, and is closely related to various sectors of the national economy. Wires and cables are also known as the "...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L67/02C08L23/16C08L23/08C08L51/00C08K13/02C08K3/34C08K3/22C08K5/1515C08K3/38
CPCC08K2003/2241C08L23/12C08K2201/011C08L2201/02C08L2201/08C08L2203/202C08L2205/035C08L2205/16H01B3/441
Inventor 胡永红
Owner KUNSHAN XINZHICHENG ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com