Application of nano-silica sol in waterborne steel structure anticorrosion paint and its protective paint
A nano-silica, steel structure technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of poor water resistance of anti-corrosion paint, and achieve the effects of good water resistance, improved protection performance, and improved water resistance
Active Publication Date: 2016-06-29
CHONGQING HAILIAN WATERBORNE COATING
View PDF2 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to solve the problem of poor water resistance of acrylic water-based steel structure anticorrosion paint, and to provide a method of using modified nano-silica sol hybrid water-based acrylic acid to make water-based steel structures anti-corrosion Paint protection properties improved
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] The present invention will be described in further detail below in conjunction with specific embodiments.
[0016] 1. The nano-silica sol of the present invention is applied in the water-based steel structure anticorrosion paint, and the acidic silica sol (a colloidal solution of nano-scale polymer inorganic metasilicate with a solid content of 25%) is added to 2-5% of the silica sol KH560 silane coupling agent (glycidyl ether oxypropyl trimethoxysilane), coupled at 55±5°C to form a modified nano-silica sol; then added to water-based acrylic emulsion for steel structure Corrosive water-based industrial coatings.
[0017] Two, the embodiment of water-based steel structure anticorrosion paint, formula composition comprises the raw material of following weight percentage:
[0018]
[0019] 3. Preparation method of water-based steel structure anticorrosion paint:
[0020] (1) First put the acidic silica sol collagen solution into the reactor, heat it to 55°C with a wat...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides application of a nano silicon dioxide sol in a water-based steel structure anticorrosive paint, which comprises the following steps: adding a KH560 silane coupling agent, which accounts for 2-5% of acidic silica sol, into the silica sol, and coupling at 55+ / -5 DEG C to form a modified nano silicon dioxide sol; and adding into a water-based acrylic acid emulsion so as to be applied to the water-based industrial paint for steel structure corrosion resistance. The invention also provides a water-based steel structure anticorrosive paint comprises 3-6% of modified nano silicon dioxide sol, 40-60% of water-based acrylic acid emulsion, 11-16% of pigment, 16-21% of filler, 0.8-1.0% of various assistants and 10-15% of deionized water. The nano silicon dioxide sol is treated by the special technique, and reasonably matched with the emulsion to prepare the nano silicon dioxide sol modified acrylic acid water-based paint, so that the film-forming density and water resistance of the product are greatly enhanced, thereby obviously improving the protective property of the product.
Description
technical field [0001] The invention relates to an industrial coating composition, in particular to the application of nano-silica sol in water-based anticorrosion paint for steel structures, and a water-based acrylic industrial coating composition hybridized with modified nano-silica sol. Background technique [0002] For the one-component emulsion type acrylic water-based steel structure anticorrosion paint for steel structure anticorrosion applications, even if pigments and fillers with good chemical antirust and physical shielding functions are considered to improve the antirust performance of the product, due to the film-forming substance itself Some defects, such as: due to the emulsifier used in emulsion polymerization, it remains in the paint film from the beginning to the end, thus affecting the compactness and water resistance of the paint film, and finally affecting the protective performance of the product. Contents of the invention [0003] In view of the abov...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D7/12C09D5/08C09D125/14
Inventor 徐文黄志忠魏林江
Owner CHONGQING HAILIAN WATERBORNE COATING