Vanadium-titanium magnetite concentrate recleaning method realized through alkaline leaching, classification and reverse flotation

A vanadium-titanium-magnetite concentrate and reverse flotation technology is applied in flotation, chemical instruments and methods, solid separation, etc., to achieve the effects of improving comprehensive utilization rate, improving blast furnace utilization coefficient, and reducing ironmaking costs

Active Publication Date: 2014-08-06
ANSTEEL GRP MINING CO LTD
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In order to overcome the deficiencies of the above-mentioned beneficiation methods, the technical problem to be solved by the present invention is to provide a low cost, high recovery quality and efficiency, simple process, and good operability to utilize alkali The method of leaching, grading, reverse flotation and re-election of vanadium-titanium magnetite concentrate has realized efficient separation of titanium and iron in vanadium-titanium magnetite concentrate, improved the grade of iron before entering the furnace, and reduced the amount of TiO entering the blast furnace. 2 , S, Si, Al and other impurities, improve the blast furnace utilization factor, reduce the discharge of blast furnace slag, reduce the cost of ironmaking, and increase the TiO 2 Comprehensive utilization of resources to reduce environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vanadium-titanium magnetite concentrate recleaning method realized through alkaline leaching, classification and reverse flotation
  • Vanadium-titanium magnetite concentrate recleaning method realized through alkaline leaching, classification and reverse flotation
  • Vanadium-titanium magnetite concentrate recleaning method realized through alkaline leaching, classification and reverse flotation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Such as figure 1 as shown,

[0034] 1) Alkaline leaching

[0035] The TFe content is 53.2%, TiO 2 content of 12.2%, SiO 2 The content is 4.92%, Al 2 o 3 The vanadium-titanium magnetite concentrate with a content of 4.88% and a S content of 0.81% is placed in a NaOH alkali solution with a mass concentration of 25%, and is subjected to alkali leaching reaction at a temperature of 360° C. for 3 hours, and the reactant is filtered to obtain the filtrate and Alkali leaching filter cake A, NaOH consumption 82kg / t is fed to ore, and described filtrate is fed into recovery treatment system, and its chemical reaction formula is:

[0036]

[0037] 2) Grading

[0038] Add water to the alkali leaching filter cake A in step 1) to form an ore slurry with a mass concentration of 20% and feed it into a cyclone for classification, and classify the grit B and overflow Y.

[0039] 3) Anti-flotation

[0040] with H 2 SO 4 It is the activator and pH adjuster of titanium compoun...

Embodiment 2

[0045] 1) Alkaline leaching

[0046] The TFe content is 51.3%, TiO 2 content of 13.9%, SiO 2 The content is 4.89%, Al 2 o 3 The vanadium-titanium magnetite concentrate with a content of 4.97% and a S content of 0.76% is placed in a NaOH alkali solution with a mass concentration of 15%, and is subjected to alkali leaching reaction at a temperature of 310° C. for 2 hours, and the reactant is filtered to obtain a filtrate and Alkali leaching filter cake A, NaOH consumption 81kg / t feeds ore, and described filtrate feeds recovery processing system, and its chemical reaction formula is the same as embodiment 1.

[0047] 2) Grading

[0048] Add water to the alkali leaching filter cake A in step 1) to form an ore slurry with a mass concentration of 21% and feed it into a cyclone for classification, and classify the grit B and overflow Y.

[0049] 3) Anti-flotation

[0050] with H 2 SO 4 It is the activator and pH adjuster of titanium compounds, the fatty acid is used as the co...

Embodiment 3

[0055] 1) Alkaline leaching

[0056] The TFe content is 52.6%, TiO 2 content of 12.3%, SiO 2 The content is 4.55%, Al 2 o 3 The vanadium-titanium magnetite concentrate with a content of 4.68% and a S content of 0.72% was placed in a NaOH alkali solution with a mass concentration of 45%, and was subjected to alkali leaching reaction at a temperature of 290° C. for 3 hours, and the reactant was filtered to obtain the filtrate and Alkali leaching filter cake A, NaOH consumption 88.5kg / t feeds ore, and described filtrate feeds recovery processing system, and its chemical reaction formula is the same as embodiment 1.

[0057] 2) Grading

[0058] Add water to the alkali leaching filter cake A in step 1) to form an ore slurry with a mass concentration of 22% and feed it into a cyclone for classification, and classify the grit B and overflow Y.

[0059] 3) Anti-flotation

[0060] with H 2 SO 4 It is the activator and pH adjuster of titanium compounds, the fatty acid is used as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a vanadium-titanium magnetite concentrate recleaning method realized through alkaline leaching, classification and reverse flotation. The method comprises the steps of placing vanadium-titanium magnetite concentrate in aqueous alkali with a mass concentration of 5%-52% for alkaline leaching reaction at a temperature between 280 DEG C and 370 DEG C for 0.5 h - 5 h and conducting filtering to obtain a filtrate and an alkaline leached filter cake A; adding water into A to form pulp with a mass concentration of 20%-25%, and feeding the pulp into a cyclone for classification to obtain effused flow Y and set sand B; adding water into the set sand B to obtain pulp with a mass concentration of 25%-30%, and conducting reverse flotation to obtain iron ore concentrate with the TFe content ranging from 65% to 69.5% and titanium concentrate with the TiO2 content ranging from 55% to 70%. The method has the advantages that efficient sorting of the vanadium-titanium magnetite concentrate is realized, alkali consumption is low, the content of impurities such as Al and Si entering a blast furnace is reduced, the content of detrimental impurities TiO2 and S is reduced especially, the utilization coefficient of the blast furnace is increased, blast furnace slag emission is reduced, the problems of high S content and severe pollution in the smelting process are solved, and the comprehensive utilization rate of titanium resources is increased.

Description

technical field [0001] The invention relates to a beneficiation process of vanadium-titanium magnetite concentrate, in particular to a method for re-selecting vanadium-titanium magnetite concentrate by alkali leaching, classification and reverse flotation. Background technique [0002] Vanadium-titanium magnetite is a compound ore of multi-metal elements, which is a symbiotic magnetite mainly containing iron, vanadium and titanium. The vanadium-titanium magnetite concentrate is one of the products obtained from vanadium-titanium magnetite through ore dressing, in which vanadium exists in the titanium magnetite in the same quality and isomorphism to replace high-valent iron ions. Titanomagnetite is the main crystal mineral (Fe 3 o 4 ) and guest crystal ore [titanium iron spar 2FeO·TiO 2 , Ilmenite FeO TiO 2 , Al-Mg spinel (Mg, Fe) (Al, Fe) 2 o 4 ] The complex formed. For example, the chemical multi-element analysis results of vanadium-titanium magnetite raw ore and van...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B03B7/00B03D1/00
Inventor 郭客巴红张志强李之奇刘政东陈巍赵亮宋仁峰
Owner ANSTEEL GRP MINING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com