Preparation method of surface coating for colored thin film solar cell

A technology of thin-film solar cells and solar cells, applied in coatings, metal material coating processes, circuits, etc.

Inactive Publication Date: 2014-08-06
YUNNAN NORMAL UNIV
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the color of solar cells is either gray or black, and the color is monotonous. When combined with buildings, it will affect the appearance of buildings. Therefore, solar cells of different colors are required, that is, colored solar cells

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of surface coating for colored thin film solar cell
  • Preparation method of surface coating for colored thin film solar cell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] This embodiment follows the steps:

[0022] Sequentially use acetone, absolute ethanol and deionized water to ultrasonically clean the flat glass substrate for 10min~15min, rinse with absolute ethanol, and blow dry with N2;

[0023] JCP-450 three-target magnetron sputtering coating system is adopted, with a doping concentration of 2%~13%ZnO:B ceramic target as the raw material, and the sputtering gas is Ar gas with a purity of 99.99%;

[0024] The substrate temperature is room temperature~300℃, the background vacuum is 4.0×10-5pa~6.0×10-5pa, the flow rate of Ar gas is 10sccm~22 sccm, the sputtering pressure is adjusted to 0.5pa~1.5pa, and the power is 80w ~140w (0.4~1.2A,

[0025] 66~300V), the sputtering time is 5min~30min, and the ZnO:B thin film is prepared on the substrate by sputtering;

[0026] Put the ZnO:B film sample into the RTP-500 photothermal rapid annealing furnace, and perform rapid annealing at a temperature of 200°C~500°C for 5min~60min under N2 atm...

Embodiment 2

[0029] This embodiment follows the steps:

[0030] Sequentially use acetone, absolute ethanol and deionized water to ultrasonically clean the flat glass substrate for 10-15 minutes, rinse with absolute ethanol, and blow dry with N2;

[0031] The JCP-450 three-target magnetron sputtering coating system is adopted, the ZnO:B ceramic target with a doping concentration of 5%~25% is used as the raw material, and the sputtering gas is Ar gas with a purity of 99.99%;

[0032] The substrate temperature is from room temperature to 300°C, the background vacuum is 4.0×10-5pa~6.0×10-5pa, Ar gas with a purity of 99.999% is introduced, the gas flow is 10sccm~30sccm, and the sputtering pressure is adjusted to 0.5pa~ 1.5pa, the power is 80w~140w (0.4~1.2A, 66~300V), the sputtering time is 10min~30min, and the ZnO:B thin film is prepared on the substrate by sputtering;

[0033] Put the ZnO:B film into the RTP-500 photothermal rapid annealing furnace, and perform rapid annealing at a tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
band gapaaaaaaaaaa
electrical resistivityaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a surface coating for a colored thin film solar cell, and belongs to the field of thin film solar cells. The preparation method of the surface coating mainly comprises steps as follows: ZnO:B ceramic targets with different doping concentrations are taken as raw materials, a ZnO:B thin film is sputtered and prepared on plate glass with a magnetron sputtering coating system, and ZnO:B thin films with different thicknesses can be obtained by controlling the sputtering condition; rapid annealing treatment is performed in N2 atmosphere, and micro-nano structure ZnO:B thin films with different grain sizes, crystallization ratios and the like can be obtained by controlling the annealing condition; and optical parameters of the refractive index, the reflectivity and the like of the ZnO:B thin films with different doping concentrations, thicknesses, grain sizes, crystallization ratios change, and the ZnO:B thin films can be used as transparent conductive oxidation films of the thin film solar cell and can show different colors on the surface of the cell, so that the colored thin film solar cell is prepared. The preparation method has the advantages as follows: the surface of the thin film cell can be endowed with different colors, and the effect of colored thin film solar cell is realized; and the surface inactivation can be realized, the life of a device is prolonged, a reflection layer can be formed, and absorption of the thin film cell absorption layer to sunlight is increased.

Description

technical field [0001] The invention relates to a preparation method for the surface coating of a colored thin-film solar cell, belonging to the field of thin-film solar cells. Background technique [0002] Solar energy is an inexhaustible clean energy. Under the background of energy crisis, environmental pollution and increasing building energy consumption, solar photovoltaic technology has been paid attention to by people, has achieved rapid development, and its application fields have gradually expanded. It is widely used in photovoltaic building integration, urban street lighting, urban landscape, traffic lights, billboards, etc. But at present, the color of solar cells is either gray or black, and the color is monotonous. When combined with buildings, it will affect the appearance of buildings. Therefore, solar cells of different colors are required, that is, colored solar cells. In addition, color solar cells also have unique advantages in some occasions that require...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/35C23C14/06H01L31/18
CPCY02P70/50
Inventor 杨培志段良飞杨雯张力元自兴发
Owner YUNNAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com