Dyeing process of chinlon-containing blended fiber

A technology of blending fibers and processes, applied in the direction of dyeing method, fiber type, fiber treatment, etc., can solve the problems of relatively high process requirements, poor dyeing stability, poor dyeing firmness, etc., to avoid strong damage and dyeing. The effect of high rate and small jump of process conditions

Active Publication Date: 2014-08-20
中山敦明纺织有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although blended fibers have many advantages, there are still some problems in the notice. For example, if the performance difference of its components is relatively large, then in the dyeing process, the requirements for its technology are relatively high, and continuous research and development must be carried out. The dyeing process of all its components
[0006] At present, there are often some problems in the dyeing process of blended fibers containing nylon: pre-treatment is easy to damage the fiber; creases are prone to occur in pre-treatment, dyeing and other processes; dyeing rate is low, dyeing is not fast; color flowers will appear; Poor staining stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of dyeing process that contains the blended fiber of nylon, comprises the following steps:

[0031] (1) Pre-setting: Pre-setting the fiber through a pre-setting machine. During the pre-setting process, the setting temperature is 158°C, the speed is 10m / min, and the overfeed is 5%;

[0032] (2) Pre-treatment: The pre-formed fiber is pre-treated with a pre-treatment solution, specifically using a softener triethanolamine stearate quaternary ammonium salt 4 g / L, an emulsifier BP 1.5 g / L, and a penetrant JFC 3 g / L, accelerator 1227 1 g / L, soda ash 2 g / L, 60% hydrogen peroxide 2 g / L, treat in a water bath at 25°C for 2 min, the bath ratio is 20:1, and then heat up in the water bath at a rate of 2.5 °C / min, when the temperature rises to 97 °C, keep at this temperature for 30 minutes, then the temperature of the water bath is lowered at a rate of 1.5 °C / min, when the temperature drops to 60 °C, discharge the treated wastewater and reinject clean water can;

[0033] (3...

Embodiment 2

[0040] A kind of dyeing process that contains the blended fiber of nylon, comprises the following steps:

[0041] (1) Pre-setting: Pre-setting the fibers through a pre-setting machine. During the pre-setting process, the setting temperature is 160°C, the speed is 12m / min, and the overfeed is 8%;

[0042] (2) Pre-treatment: The pre-formed fiber is pre-treated with a pre-treatment solution, specifically, the softener triethanolamine stearate quaternary ammonium salt 5 g / L, the emulsifier BP 2.5 g / L, the penetrant T 3.5 g / L, accelerator 1227 1.5 g / L, soda ash 2.5 g / L, 60% hydrogen peroxide 2.5 g / L, treat in a water bath at 28°C for 2.5 min, the bath ratio is 20:1, and then heat up in the water bath at a rate of 2.8 °C / min, when the temperature rises to 98 °C, keep at this temperature for 33 minutes, then the temperature of the water bath is lowered at a rate of 2 °C / min, when the temperature drops to 62 °C, discharge the treated wastewater and re-inject clean water can;

[0043] ...

Embodiment 3

[0050] A kind of dyeing process that contains the blended fiber of nylon, comprises the following steps:

[0051] (1) Pre-setting: Pre-setting the fiber through a pre-setting machine. During the pre-setting process, the setting temperature is 162°C, the speed is 15m / min, and the overfeed is 10%;

[0052] (2) Pre-treatment: The pre-formed fiber is pre-treated with a pre-treatment liquid, specifically using a softener triethanolamine stearate quaternary ammonium salt 6 g / L, an emulsifier BP 3.5 g / L, and a penetrant BX 4 g / L, accelerator 1227 2 g / L, soda ash 3 g / L, 60% hydrogen peroxide 3 g / L, treat in a water bath at 30°C for 3 min, the bath ratio is 20:1, and then heat up in the water bath at a rate of 3 °C / min, when the temperature rises to 99 °C, keep at this temperature for 35 minutes, then the temperature of the water bath is lowered at a rate of 2.5 °C / min, when the temperature drops to 65 °C, discharge the treated wastewater and reinject clean water can;

[0053] (3) Dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a dyeing process of a chinlon-containing blended fiber. The dyeing process comprises the following steps of preforming, pretreatment, drying, dyeing, drying, finished product forming and winding. According to the dyeing process, the preforming is carried out before the pretreatment, so that the phenomenon that crumples appear on the chinlon-containing blended fiber; a high-temperature leveling agent is added in the dyeing procedure, so that the problem that level dyeing effect and penetration dyeing effect are influenced and even color dots and color patches occur caused by the gathering of dyes because the heat stability resistance of fuel is lowered due to temperature increase is prevented, and good dyeing effect is achieved; the final dye-uptake rate of the chinlon-containing blended fiber can achieve 75%, the soaping color fastness of the dyed fiber achieves 5 level, and good water shrinkage and washing fastness and low strength loss of the dyed fiber are achieved.

Description

technical field [0001] The invention relates to the field of chemical fibers, in particular to a dyeing process of blended fibers containing nylon. Background technique [0002] Chemical fibers are fibers with textile properties that are made from natural polymer compounds or artificially synthesized polymer compounds through the processes of preparing spinning dope, spinning and post-treatment. It has the advantages of light resistance, wear resistance, easy washing and drying, no mildew and no moths. Widely used in the manufacture of clothing fabrics, filter cloths, conveyor belts, hoses, ropes, fishing nets, electrical insulation wires, medical sutures, tire cords and parachutes, etc. [0003] Nylon is the earliest synthetic fiber variety in the world. Its biggest feature is its high strength and good wear resistance. Its strength and wear resistance rank first among all fibers. [0004] Blended fibers, also known as multi-component fibers, refer to chemical fibers spun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/463D06M11/50D06M11/38D06P1/607D06P1/673D06P1/653D06P3/82D06P5/02D06C7/02D06M101/34
Inventor 徐建明
Owner 中山敦明纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com