An anti-aging and heat-resistant technology, applied in the field of chemical material preparation, can solve problems such as poor heat resistance and unsatisfactory anti-aging performance, and achieve good performance stability

Active Publication Date: 2014-09-10
佛山市埃森塑胶电器有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the performance of modified plastics with PVC as the main component has been greatly improved, but they still cannot meet higher requirements. Among them, their heat resistance is not good, and their anti-aging performance cannot meet the growing market requirements. Therefore, it is necessary to develop a material with excellent heat resistance and aging resistance to meet the needs of the application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A heat-resistant and aging-resistant material, comprising by weight components: 80 parts of PVC, 10 parts of bisphenol A epoxy resin, 5 parts of toluene diisocyanate, 0.8 parts of calcium lignosulfonate, 8 parts of polyethylene glycol 600, 6 parts of styrene, 5 parts of calcium stearate, 1 part of magnesium stearate, 2 parts of acrylamide, 0.5 part of N-cyclohexyl p-methoxyaniline.

[0023] The preparation method of the heat-resistant and aging-resistant material described above comprises the following steps:

[0024] (1) Weigh each component according to parts by weight, and add PVC, bisphenol A epoxy resin, styrene, stabilizer and antioxidant into a mixing mixer, and mix and stir at 70°C for 10 minutes to obtain a mixture One, discharge;

[0025] (2) Add calcium lignosulfonate and acrylamide to mixture 1 obtained in step (1), stir and react at 95°C for 25 minutes at a stirring speed of 50 rpm to obtain mixture 2;

[0026] (3) Add the remaining components to the mixt...

Embodiment 2

[0029] A heat-resistant and aging-resistant material, comprising: 90 parts by weight of PVC, 15 parts of bisphenol A epoxy resin, 6 parts of toluene diisocyanate, 1 part of calcium lignosulfonate, 10 parts of polyethylene glycol 600, 10 parts of styrene, 6 parts of stabilizer, 2 parts of lubricant, 3 parts of acrylamide, 1 part of antioxidant.

[0030] The preparation method of the heat-resistant and aging-resistant material described above comprises the following steps:

[0031] (1) Weigh each component according to weight, and add PVC, bisphenol A epoxy resin, styrene, stabilizer and antioxidant into a mixing mixer, and mix and stir at 72°C for 13 minutes to obtain a mixture One, discharge;

[0032] (2) Add calcium lignosulfonate and acrylamide to the mixture 1 obtained in step (1), under the condition of vacuum degree of 0.05MPa, stir and react at 96°C for 28 minutes, and the stirring speed is 55 rpm, Obtain mixture two;

[0033] (3) Add the remaining components to the m...

Embodiment 3

[0036] A heat-resistant and aging-resistant material, comprising by weight components: 92 parts of PVC, 16 parts of bisphenol A epoxy resin, 7 parts of toluene diisocyanate, 1.2 parts of calcium lignosulfonate, 12 parts of polyethylene glycol 600, 11 parts of styrene, 7 parts of stabilizer, 3 parts of lubricant, 4 parts of acrylamide, 1 part of antioxidant.

[0037] The preparation method of the heat-resistant and aging-resistant material described above comprises the following steps:

[0038] (1) Weigh each component by weight, and add PVC, bisphenol A epoxy resin, styrene, stabilizer and antioxidant into a mixing mixer, and mix and stir at 75°C for 15 minutes to obtain a mixture One, discharge;

[0039] (2) Add calcium lignosulfonate and acrylamide to the mixture 1 obtained in step (1), under the condition of vacuum degree of 0.06MPa, stir and react at 98°C for 30 minutes, and the stirring speed is 56 rpm, Obtain mixture two;

[0040] (3) Add the remaining components to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a heat-resisting ageing resistant material and a preparation method thereof. The material comprises following components in parts by weight: 80-100 parts of polyvinyl chloride (PVC), 10-20 parts of bisphenol A epoxy resin, 5-10 parts of toluene diisocynate, 0.8-2 parts of lignin calcium sulfonate, 8-15 parts of polyethylene glycol 600, 6-15 parts of styrene, 5-10 parts of stabilizer, 1-5 parts of lubricant, 2-6 parts of acrylamide, and 0.5-3 parts of antioxidant. The preparation method comprises the steps of adding the PVC, bisphenol A epoxy resin, styrene, stabilizer and antioxidant into a mixing blender, mixing at certain conditions, then adding the lignin calcium sulfonate and acrylamide, heating up, then adding the left components, stirring for 10-20 minutes at 80-90DEG C, rising the temperature and reacting, so as to obtain the mixture, and finally, extruding the mixture by a twin-screw extruder so as to obtain the heat-resisting ageing resistant plastic.

Description

technical field [0001] The invention belongs to the technical field of chemical material preparation, and in particular relates to a heat-resistant and aging-resistant material and a preparation method thereof. Background technique [0002] Polyvinyl chloride, referred to as PVC (Polyvinyl chloride polymer), is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator. It is a homopolymer of vinyl chloride. Vinyl chloride homopolymers and vinyl chloride copolymers are collectively referred to as vinyl chloride resins. PVC is a white powder with an amorphous structure and a small degree of branching. The molecular weight of industrially produced PVC is generally in the range of 50,000 to 120,000, with a large polydispersity, and the molecular weight increases with the decrease of the polymerization temperature; there is no fixed melting point, it starts to soften at 80-85°C, and becomes viscoelastic at 130°C , 160 ~ 180 ℃ began to change into a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L63/02C08L97/00C08L75/08C08K13/02C08K5/09C08K5/18C08K5/01C08K5/20C08G18/76C08G18/48
Inventor 潘琳肖运根过俊宏
Owner 佛山市埃森塑胶电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap