Special low-detonation velocity explosive for explosive welding
A low-explosive-velocity explosive and explosive welding technology is applied in the field of explosives to achieve the effects of stable detonation, good dispersion and moderate density.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Embodiment 1, the special low detonation velocity explosive of explosive welding of detonation velocity 2150m / s, intensity 7cm, martyrdom distance 3cm, and preparation method thereof:
[0017] Take 160kg of No. 2 powdery emulsion explosive in bulk, take 60kg of granular calcium carbonate with a fineness of 80 mesh, and mix them evenly to obtain a detonation velocity of 2150m / s, a violent force of 7cm, and a detonation distance of 3cm. , Density 0.84g / cm3 special low detonation velocity powder emulsion explosive for explosive welding.
[0018] The explosive is used for explosive welding of 4mm thick S316L stainless steel plate and 16mm thick Q345 carbon steel plate to produce (S316L+Q345) 4 / 16×1800×4500mm metal composite plate, and the composite effect is good after ultrasonic flaw detection.
Embodiment 2
[0019] Embodiment 2, the special low-detonation-velocity explosive of explosive welding of detonation velocity 2200m / s, intensity 8.2cm, martyrdom distance 4cm, and preparation method thereof:
[0020] Take 160kg of bulk No. 2 powdery emulsion explosive, take 55kg of granular calcium carbonate with a fineness of 100 mesh, the moisture content of the calcium carbonate particles is not higher than 0.5wt%, and mix evenly to obtain a detonation velocity of 2200m / s, a violent force of 8.2cm, and a detonation distance of 2200m / s. 4cm, density 0.78g / cm3 special low detonation velocity powder emulsion explosive for explosive welding.
[0021] The explosive is used for explosive welding of 3mm thick TA1 pure titanium plate and 20mm thick Q345R carbon steel plate to produce (TA1+Q345R) 3 / 20×2150×5130mm metal composite plate, and the composite effect is good after ultrasonic flaw detection.
Embodiment 3
[0022] Embodiment 3, the special low detonation velocity explosive of explosive welding of detonation velocity 2050m / s, intensity 7cm, martyrdom distance 4cm, and preparation method thereof:
[0023] Take 200kg of bulk No. 2 powdery emulsion explosive, take 85kg of granular calcium carbonate with a fineness of 100 mesh, the moisture content of the calcium carbonate particles is not higher than 0.5wt%, and mix evenly to obtain a detonation velocity of 2050m / s, a violent force of 7cm, and a detonation distance of 4cm , Density 0.82g / cm3 special low detonation velocity powder emulsion explosive for explosive welding.
[0024] The explosive is used for explosive welding of Φ2150×8mm iron-nickel copper Bfe30 and Φ2150×70mm carbon steel pipe Q345R to produce (Bfe30+Q345R) 8 / 70×Φ2150 metal composite tube sheet. The composite effect is good after ultrasonic flaw detection.
[0025] Prove by embodiment 1-3, prepare according to the special low detonation velocity explosive technical sc...
PUM
Property | Measurement | Unit |
---|---|---|
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com