Aluminum-based composite radiating material for LED (light-emitting diode) doped neodymium oxide

A technology of aluminum-based composite and heat-dissipating materials, applied in the direction of heat exchange materials, chemical instruments and methods, etc., can solve problems such as cost constraints and insufficient insulation performance, and achieve improved heat dissipation and temperature resistance, extended service life, and good heat conduction and the effect of insulating properties

Active Publication Date: 2014-10-01
YANYANG LAMP SET TIANCHANG CITY
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing LED heat dissipation materials are mainly made of metal materials such as aluminum and copper. In actual use, there are disadvantages such as cost limitations and insufficient insulation performance. Therefore, it is necessary to improve the formula of the material to achieve a better heat dissipation effect. , improve the performance of the lamps and prolong the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0011] The LED heat dissipation material in this embodiment is made of the following raw materials in parts by weight: aluminum 75, aluminum nitride 12, iron oxide black 5, neodymium oxide 2, steel slag 8, metakaolin 12, water glass 8, ferrous sulfate 3, sucrose fatty acid Esters 4, additives 5.

[0012] The auxiliary agent is made of the following raw materials in parts by weight: polyaluminum sulfate 5, animal bone 10, sodium sand 3, polyimide 5, silver-coated copper powder 10, magnesium oxide 14, light magnesium carbonate 5, prepared The method is: first calcinate the animal bone at 800-900°C for 11 hours, then cool it for later use, then dissolve polyaluminum sulfate in an appropriate amount of water to prepare an aqueous solution with a concentration of 5.0%, and put the calcined animal bone and other remaining ingredients into In the solution, mix and stir to disperse for 3 hours, concentrate and dry, grind to 400-mesh fine powder, and obtain it.

[0013] The manufactur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a lamp radiating material and specifically relates to an aluminum-based composite radiating material for LED (light-emitting diode) doped neodymium oxide and a production method thereof. The radiating material is prepared from the following materials in parts by weight: 73-75 parts of aluminum, 10-12 parts of aluminum nitride, 4-5 parts of iron oxide black, 2-3 parts of neodymium oxide, 6-8 parts of steel slag, 10-12 parts of metakaolin, 6-8 parts of sodium silicate, 2-3 parts of ferrous sulfate, 2-5 parts of sucrose fatty acid ester and 4-5 parts of auxiliaries. The radiating material disclosed by the invention has integrated advantages of components such as aluminum, aluminum nitride, metakaolin, and the like, has good heat conduction and insulating performances; all materials are mixed and ground in sodium silicate aqueous liquor to increase compatibility of materials, so that the materials are easier to form; the doped neodymium oxide can improve radiating and temperature-resisting performances of the material; and the radiating material prepared in the invention is compact in structure, bright in color and luster, light and firm, good in thermal stability, durable, and efficient and lasting in radiating capacity, so that the LED lamp is effectively protected, and service life of the lamp is greatly prolonged.

Description

technical field [0001] The invention relates to a heat dissipation material for lamps, in particular to an aluminum-based composite heat dissipation material doped with neodymium oxide for LEDs and a production method thereof. Background technique [0002] LED is called the fourth-generation light source, which has the advantages of energy saving, environmental protection, safety, low energy consumption, and high brightness. It is widely used in daily life. The heat dissipation performance of the LED lamp itself is very important, which directly affects the service life of the lamp. and lighting effects. Existing LED heat dissipation materials are mainly made of metal materials such as aluminum and copper. In actual use, there are disadvantages such as cost limitations and insufficient insulation performance. Therefore, it is necessary to improve the formula of the material to achieve a better heat dissipation effect. , Improve the performance of lamps and prolong their ser...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/05C09K5/14
Inventor 翁震娣郑金山柳加云吴有军
Owner YANYANG LAMP SET TIANCHANG CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap