Microcrystal ecological section bar

An ecological and profile technology, applied in the field of decorative profiles, can solve problems such as easy to show dirt, achieve the effects of long service life, simple construction process, and enhanced flame retardant performance

Inactive Publication Date: 2014-10-08
山东宏亮新型环保装饰材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current microcrystalline ecological profile has the following disadvantages: 1. Obvious scratches: the surface gloss of the microcrystalline material is high, which can reach 90%. A certain number of pinholes are easy to show when encountering dirty things

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microcrystal ecological section bar
  • Microcrystal ecological section bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Proportion (parts by weight): 30 parts of heavy calcium carbonate powder, 2 parts of quartz sand, 10 parts of polyvinyl chloride, 1 part of polytetrafluoroethylene, 1 part of chlorinated polyethylene, 521 parts of chlorinated paraffin, 0.6 parts of hydrotalcite 0.6 parts, 0.6 parts of octyltin maleate, 1 part of stearic acid, 0.6 parts of oxidized polyethylene wax, 0.7 parts of fumed silica, 0.15 parts of sodium bicarbonate, and 1 part of titanium dioxide.

[0038] Among them, the particle size of heavy calcium carbonate powder, quartz sand and hydrotalcite are all less than 0.1mm.

[0039] Preparation:

[0040] 1. Mixing: Weigh the raw materials according to the above weight parts, and fully knead them in a high-speed mixer: the raw materials placed first are polyvinyl chloride, polytetrafluoroethylene, heavy calcium carbonate powder, quartz sand and hydrotalcite, at high temperature , high friction, and high shear to achieve the purpose of uniform mixing; add oxidize...

Embodiment 2

[0044] Proportion (parts by weight): 32 parts of heavy calcium carbonate powder, 3 parts of quartz sand, 12 parts of polyvinyl chloride, 2 parts of polytetrafluoroethylene, 1.5 parts of chlorinated polyethylene, 1.5 parts of chlorinated paraffin-521.5 parts, 1 part of hydrotalcite 1 part, 1 part of octyltin maleate, 1.5 parts of stearic acid, 1 part of oxidized polyethylene wax, 1 part of fumed silica, 0.2 part of sodium bicarbonate, and 2 parts of titanium dioxide.

[0045] Among them, the particle size of heavy calcium carbonate, quartz sand and hydrotalcite are all less than 0.1mm.

[0046] Preparation:

[0047] 1. Mixing: Weigh the raw materials according to the above weight parts, and fully knead them in a high-speed mixer: the raw materials placed first are polyvinyl chloride, polytetrafluoroethylene, heavy calcium carbonate powder, quartz sand and hydrotalcite, at high temperature , high friction, and high shear to achieve the purpose of uniform mixing; add oxidized po...

Embodiment 3

[0051] 20 parts of heavy calcium carbonate powder, 1 part of quartz sand, 10 parts of polyvinyl chloride, 0.5 parts of polytetrafluoroethylene, 0.5 parts of chlorinated polyethylene, 520.5 parts of chlorinated paraffin, 0.5 parts of hydrotalcite, octyltin maleate 0.5 parts, stearic acid 0.5 parts, oxidized polyethylene wax 0.5 parts, fumed silica 0.5 parts, sodium bicarbonate 0.1 parts.

[0052] Among them, the particle size of heavy calcium carbonate, quartz sand and hydrotalcite are all less than 0.1mm.

[0053] Preparation:

[0054] 1. Mixing: Weigh the raw materials according to the above weight parts, and fully knead them in a high-speed mixer: the raw materials placed first are polyvinyl chloride, polytetrafluoroethylene, heavy calcium carbonate powder, quartz sand and hydrotalcite, at high temperature , high friction, and high shear to achieve the purpose of uniform mixing; add oxidized polyethylene wax, stearic acid, chlorinated paraffin-52 and octyltin maleate after ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

A microcrystal ecological section bar is disclosed. The microcrystal ecological section bar is prepared from following raw materials: heavy calcium carbonate powder, quartz sand, polyvinyl chloride, polytetrafluoroethylene, chlorinated polyethylene, chlorinated paraffin-52, hydrotalcite, dioctyl(maleate)tin, stearic acid, oxidized polyethlene wax, fumed silica and sodium bicarbonate. On the premise of maintaining difficult deformation, fire protection, flame retardance and environmental protection properties of common microcrystal section bars, strength, wear resistance and compactness of the section bar are enhanced, and the flame retardant property of the section bar is further enhanced.

Description

technical field [0001] The invention relates to a decorative profile in the technical field of construction engineering, in particular to a microcrystalline ecological profile, including a microcrystalline ecological line, a microcrystalline ecological floor and a microcrystalline ecological board. Background technique [0002] In the current line decoration, marble lines, artificial stone lines, and wooden lines are usually used, but because marble lines and artificial stone lines are difficult to construct, have a high damage rate, and have radiation; wooden lines are easily deformed when exposed to water, and are not fireproof (in China There have been hundreds of fire accidents in many cities), and these types of lines have been eliminated by the country. In the current flooring, solid wood flooring, composite flooring, bamboo flooring, etc. are usually used, but solid wood flooring, composite flooring, and bamboo flooring have disadvantages such as complex laying proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L27/18C08L23/28C08L23/30C08K13/02C08K3/26C08K3/36C08K5/57C08K5/09C08K3/22
Inventor 刘志国
Owner 山东宏亮新型环保装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com