Natural mineral fertilizer containing nano silicon and preparation method thereof
A nano-silicon and mineral technology, applied in fertilizer mixtures, fertilization devices, applications, etc., can solve problems such as lack of natural mineral fertilizers, and achieve the effects of improving soil physical and chemical properties, increasing stress resistance, and improving effective utilization.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
Specific embodiment one
[0021] The raw materials in the embodiments of the present invention come from the Jingzhou area of Hubei.
[0022] 45 parts of phosphate rock powder, 45 parts of dolomite, 5 parts of serpentine, 5 parts of silica, after being crushed, are loaded into the feeding car and put into the high temperature melting furnace with a hoist. The hot air from the hot blast furnace is sprayed into the blast furnace through the tuyere to make the temperature in the high temperature zone reach about 1000℃. After the materials are fully calcined and melted in the furnace, calcined for 5 hours, the melt is discharged from the discharge port, and the gauge pressure is 0.2MPa The water jet makes it extremely cold, solidifies and breaks into fine particles and flows into the water quenching tank. The dried semi-finished product is then sent to the ball mill for fine grinding, and the fineness is required to pass 80 mesh sieve above 80%. The nutrient content of the product, ...
Example Embodiment
Specific embodiment two
[0023] The raw materials in the embodiments of the present invention come from the Jingzhou area of Hubei.
[0024] 90 parts of phosphate rock powder, 5 parts of dolomite, and 5 parts of magnesite, after being crushed, are loaded into the feeding car, and put into the high-temperature melting furnace with a hoist. The hot air from the hot blast furnace is sprayed into the blast furnace through the tuyere to make the temperature in the high temperature zone reach about 1300℃. After the material is fully calcined and melted in the furnace, calcined for 1 hour, the melt is discharged from the discharge port and sprayed with 0.1MPa water. It is extremely cold and solidified and broken into fine particles to flow into the water quenching tank. The dried semi-finished product is then sent to a ball mill for fine grinding. The fineness is required to pass a 100-mesh sieve above 50%. Product nutrient content, phosphorus pentoxide (P 2 O 5 ) Content 10%, effecti...
Example Embodiment
Specific embodiment three
[0025] The raw materials in the embodiments of the present invention come from the Jingzhou area of Hubei.
[0026] 49 parts of phosphate rock powder, 50 parts of dolomite, and 1 part of olivine, after being crushed, are loaded into the feeding car, and put into the high-temperature melting furnace with a hoist. The hot air from the hot blast furnace is sprayed into the blast furnace through the tuyere to make the temperature in the high temperature zone reach about 3000℃. After the material is fully calcined and melted in the furnace, calcined for 3 hours, the melt is discharged from the discharge port and sprayed with 0.5MPa water. It is extremely cold and solidified and broken into fine particles to flow into the water quenching tank. The dried semi-finished product is then sent to a ball mill for fine grinding. The fineness is required to pass through a 160-mesh sieve. Product nutrient content, phosphorus pentoxide (P 2 O 5 ) Content 20%, effectiv...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction