Oil resistant gasket

A gasket and oil-resistant technology, applied in the field of rubber material science, can solve problems such as poor low temperature resistance, poor electrical performance, and poor ozone resistance, and achieve the effects of low price, excellent oil resistance, and less raw materials

Inactive Publication Date: 2014-11-26
宁国天运橡塑制品有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantages are poor low temperature resistance, poor ozone resistance, poor electrical properties, and slightly lower elasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] An oil-resistant gasket, characterized in that it comprises the following raw materials in parts by weight: 80 parts of high acrylonitrile NBR, 3 parts of zinc oxide, 0.5 part of stearic acid, 0.1 part of sulfur, 10 parts of semi-reinforced furnace black, and 25 parts of activated calcium carbonate , 5 parts of plasticizer DOS, 3 parts of plasticizer TP-90B, 1 part of accelerator CZ, 1 part of accelerator TMTD.

[0012] Compared with the prior art, the present invention has the following advantages: (1) the product produced by the present invention is cheap, uses less raw materials, and the production process is simple; (2) the present invention has safety and environmental protection, excellent oil resistance, heat resistance, and A series of advantages such as aging performance. (3) The present invention uses NBR and PVC together, and the gasket produced has both excellent bending resistance and high fatigue resistance and sealing performance.

Embodiment 2

[0014] An oil-resistant gasket, characterized in that it comprises the following raw materials in parts by weight: 120 parts of high acrylonitrile NBR, 7 parts of zinc oxide, 1.5 parts of stearic acid, 0.3 parts of sulfur, 30 parts of semi-reinforced furnace black, and 45 parts of activated calcium carbonate , plasticizer DOS15 parts, plasticizer TP-90B7 parts, accelerator CZ3 parts, accelerator TMTD1-3 parts.

[0015] Compared with the prior art, the present invention has the following advantages: (1) the product produced by the present invention is cheap, uses less raw materials, and the production process is simple; (2) the present invention has safety and environmental protection, excellent oil resistance, heat resistance, and A series of advantages such as aging performance. (3) The present invention uses NBR and PVC together, and the gasket produced has both excellent bending resistance and high fatigue resistance and sealing performance.

Embodiment 3

[0017] An oil-resistant gasket, characterized in that it comprises the following raw materials in parts by weight: 100 parts of high acrylonitrile NBR, 5 parts of zinc oxide, 1 part of stearic acid, 0.2 parts of sulfur, 20 parts of semi-reinforced furnace black, and 35 parts of activated calcium carbonate , plasticizer DOS10 parts, plasticizer TP-90B5 parts, accelerator CZ2 parts, accelerator TMTD2 parts.

[0018] Compared with the prior art, the present invention has the following advantages: (1) the product produced by the present invention is cheap, uses less raw materials, and the production process is simple; (2) the present invention has safety and environmental protection, excellent oil resistance, heat resistance, and A series of advantages such as aging performance. (3) The present invention uses NBR and PVC together, and the gasket produced has both excellent bending resistance and high fatigue resistance and sealing performance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an oil resistant gasket characterized by comprising the following raw materials by weight: 80-120 parts of high acrylonitrile NBR, 3-7 parts of zinc oxide, 0.5-1.5 parts of stearic acid, 0.1-0.3 part of sulfur, 10-30 parts of semi reinforcing furnace black, 25-45 parts of active calcium carbonate, 5-15 parts of plasticizer DOS, 3-7 parts of plasticizer TP-90B, 1-3 parts of promoter CZ and 1-3 parts of promoter TMTD. Compared with the prior art, the oil resistant gasket has the following advantages: (1) the product of the oil resistant gasket has the advantages of low price, less use of raw materials and simple production process; (2) the oil resistant gasket has the advantages of being safe, environmentally friendly, good in oil resistance, heat resistance and aging resistance and other a series of advantages; and (3) by simultaneous use of the NBR and PVC, the manufactured oil resistant gasket has excellent resistance to bending, and high fatigue resistance and sealing performance.

Description

technical field [0001] The invention relates to the scientific field of rubber materials, in particular to an oil-resistant gasket. Background technique [0002] Nitrile-butadiene rubber (NBR) is produced by emulsion polymerization of butadiene and acrylonitrile. Nitrile rubber is mainly produced by low-temperature emulsion polymerization. It has excellent oil resistance, high wear resistance, good heat resistance, and good viscosity. The relay is strong. Its disadvantages are poor low temperature resistance, poor ozone resistance, poor electrical properties, and slightly lower elasticity. Nitrile rubber is mainly used in the manufacture of oil-resistant rubber products. Such as rubber hoses, rubber rollers, sealing gaskets, storage tank linings, aircraft fuel tank linings, and large oil bags that are in contact with oil. Utilizing the good heat resistance of NBR, it is also possible to manufacture conveyor belts for transporting hot materials (below 140°C). It can also ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08K13/02C08K3/22C08K5/09C08K3/06C08K3/04C08K3/26
Inventor 吴延福
Owner 宁国天运橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap