Modified fiber board production process

A technology of modified fiber and production process, which is applied in the direction of wood processing equipment, pretreatment of molding materials, manufacturing tools, etc. It can solve the problems of low strength of fiberboard, limited range of use, warping and deformation of the board, and achieve increased volume and Density, reduced wood consumption, and improved board performance

Active Publication Date: 2014-12-03
湖北益嘉林业发展有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the commonly used fiberboards are degreased and peeled logs, crushed into wood fibers and then molded under high temperature and high pressure. Most of the existing fiberboards in the market are medium density boards and high density boards, and their density is higher than that of ordinary boards. Higher, the material of this kind of fiberboard is uniform, the surface is flat, and the decoration of the surface of the board is good, but the disadvantages are: the stability is poor, and the board is warped and deformed due to the difference in expansion force after moisture absorption, due to the strength of the fiberboard It is not high, and the nail holding power is poor. If the screw becomes loose after tightening, it is difficult to fix it again, which limits its scope of use to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified fiber board production process
  • Modified fiber board production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] see figure 1 The production process of the modified fiberboard of the present invention includes the steps of chipping, cooking and hot grinding, preparation of modified fiber material, drying, preparation of blank material, cold pressing, hot pressing, sawing, sanding and thickness determination. The steps are as follows:

[0019] Step 1 Chipping: The wood raw material is cut into wood chips with a length of 3 to 5 cm and a width of 2 to 3 cm by a chipper. Save a lot of log resources.

[0020] Step 2 Cooking and hot grinding: put the wood chips cut in step 1) into the cooking tank for cooking, the cooking temperature is 150-175 ℃, the cooking time is 2-3 minutes, and then the cooked wood chips are placed in the heat mill to heat. Grind into fibrous fibrous material, and the hot grinding pressure is 7-8.55MPa, so that the water filtration degree of the fibrous material reaches 22-28S, and then sent to the silo of the sizing equipment;

[0021] Step 3 Preparation of m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a modified fiber board production process. The modified fiber board production process includes steps of chipping, digesting, hot grinding, preparation of modified fibers, drying, preparation of blank materials, cold pressing, hot pressing, saw cutting, sanding, thickness determination and the like. In the step of preparation of modified fibers, calcium powder is added into fibers and used for replacing part of wood fibers, the calcium powder is mixed with glue prior to being mixed with the fibers during filling so as to enable clearances of the fibers to be filled by mixture of the calcium powder and the glue, and accordingly physical and chemical performances of fiber boards are improved, and improvement of board density, reduction of wood consumption and improvement of elasticity modulus indexes and static bending strength of the boards are achieved while reduction of fiber board production cost and effective saving of wood resources are realized. Wood consumption is reduced by about 20% as compared with that of common fiber boards, and the modified fiber boards produced according to the process have the advantages of high strength, high nail holding ability, excellent bending resistance and high stability and flame retardance.

Description

technical field [0001] The invention belongs to the technical field of wood-based panel production, and relates to a production process of modified fiberboard. Background technique [0002] In today's social and economic development, the demand for wood and its products is increasing, making full use of resources such as artificial fast-growing commercial forests, forest cultivation and harvesting residues, and waste wood fibers in the process of production and construction, renovation and transformation to develop wood-based panels to replace Traditional solid wood products play an irreplaceable role in protecting natural forest resources, improving the ecological environment, and meeting the demand for wood products in economic development. With the rapid development of my country's economy and the continuous improvement of urbanization rate, there is a broad market space for fiberboard products with stable quality, high environmental protection level, meeting differentiat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N3/08B27N1/02
Inventor 李昌华龙明金
Owner 湖北益嘉林业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products