Preparation method of heat insulating porous ceramic made from light coal ash

A technology of porous ceramics, heat preservation and heat insulation, applied in the direction of ceramic products, solid waste removal, application, etc., can solve the problems of polluting the environment, not complying with low-carbon environmental protection policies, and not complying with environmental protection policies, etc., to achieve short production cycle and high strength The effect of height and hole roundness

Inactive Publication Date: 2014-12-03
HEFEI KESIFU SAFETY TECH
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Li Shaorong and others used organic resin foamed microspheres as pore-forming agents to prepare porous ceramics. The pore size is uniform and the size is controllable, but the gas emitted when the organic pore-forming agents are burned out will pollute the environment, which is not in line with environmental protection policies; Wu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of heat insulating porous ceramic made from light coal ash
  • Preparation method of heat insulating porous ceramic made from light coal ash

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The weight percentage of raw material components is: fly ash 35wt%, agar powder 0.3wt%, foam stabilizer sodium hexametaphosphate (PAAS) 0.15wt%, dispersant sodium polyacrylate (SHMP) 0.1wt%, foaming agent twelve Sodium alkyl sulfate (K12) 0.4wt%, water 64.05wt%.

[0025] The specific operation steps for preparing thermal insulation porous ceramics are as follows:

[0026] (1) Add 57.47g of fly ash, 0.16g of PAAS, 0.25g of SHMP and 72.53g of water into the ball mill according to the ratio of the above raw materials. Add 0.38g of agar powder into 25g of water, dissolve at 90°C to obtain agar hydrosol; take 95g of the primary slurry, preheat the primary slurry in a water bath at a temperature of 60°C, add the agar hydrosol, and dissolve at a low speed of 400 rpm. Next, the stirrer is stirred for about two minutes to make it fully mixed, and a uniform and stable ceramic slurry with a solid content of 35wt% is obtained; (3) Add foaming agent K12 of 0.4wt% of the ceramic slu...

Embodiment 2

[0029] The weight percentage of raw material components is: fly ash 40wt%, agar powder 0.3wt%, foam stabilizer sodium hexametaphosphate (PAAS) 0.15wt%, dispersant sodium polyacrylate (SHMP) 0.1wt%, foaming agent twelve Sodium alkyl sulfate (K12) 0.4wt%, water 59.05wt%.

[0030] The specific operation steps for preparing thermal insulation porous ceramics are as follows:

[0031] Put 67.20g of fly ash, 0.17g of PAAS, 0.25g of SHMP and 72.80g of water into the ball mill, the speed of the ball mill is 180 r / min, and the ball milling time is 24 hours to obtain the primary slurry; (2) Add 0.38g of agar powder into 20g of water, the temperature is 90 Dissolve at ℃ to obtain agar hydrosol; take 100g of the primary slurry, preheat the primary slurry in a water bath at a temperature of 60°C, add the agar hydrosol, and stir with a stirrer for about two minutes at a low speed of 400 rpm to make it Mix well to obtain a uniform and stable ceramic slurry with a solid content of 40wt%; (3) ...

Embodiment 3

[0034] The weight percentage of raw material components is: fly ash 35wt%, agar powder 0.2wt%, foam stabilizer sodium hexametaphosphate (PAAS) 0.15wt%, dispersant sodium polyacrylate (SHMP) 0.1wt%, foaming agent twelve Sodium alkyl sulfate (K12) 0.4wt%, water 64.15wt%.

[0035] The specific operation steps for preparing thermal insulation porous ceramics are as follows:

[0036] Add 57.47g of fly ash, 0.16g of PAAS, 0.25g of SHMP and 72.53g of water into the ball mill, the speed of the ball mill is 180 r / min, and the ball milling time is 24 hours to obtain the primary slurry; (2) Add 0.26g of agar powder into 25g of water, the temperature is 90 Dissolve at ℃ to obtain agar hydrosol; take 95g of primary slurry, preheat the primary slurry in a water bath at a temperature of 55℃, add agar hydrosol, and stir with a stirrer for about two minutes at a low speed of 400 rpm to make it Mix well to obtain a uniform and stable ceramic slurry with a solid content of 35wt%; (3) Add 0.4wt% f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a heat insulating porous ceramic made from light coal ash. The preparation method comprises the following steps: (1) taking coal ash, ground glass, a dispersant and a foam stabilizer, and adding water to stir and ball-mill to obtain primary slurry; (2) preparing agar-containing stable ceramic slurry; (3) adding a surfactant and stirring and foaming to obtain foam slurry; (4) pouring the foam slurry into a die, and curing at room temperature; (5) demoulding and drying to obtain a porous ceramic blank; and (6) sintering the porous ceramic blank at a low temperature to obtain the porous ceramic. According to the preparation method provided by the invention, coal ash is utilized to the maximum extent. In addition, agar which is free from environmental pollution is decomposed as a gel, and the dosage of the agar can be reduced to 0.1wt%, so that the porous ceramic meets the low-carbon environment-friendly policy. The porosity of the porous ceramic prepared by the method is 88-91%, the density is 0.24-0.31g/cm<3>, the heat conductivity coefficient is 0.051-0.072W/(m.K) and the compressive strength is 0.4-1.0MPa.

Description

technical field [0001] The invention belongs to the technical field of novel light heat insulating materials, and in particular relates to a preparation method of light fly ash heat insulating porous ceramics. Background technique [0002] my country's economy is now in a period of rapid development, and energy and environmental protection issues have become increasingly prominent. The strategy of energy conservation and environmental protection in buildings is in line with the current sustainable development strategy. Due to the relationship between supply and demand, the development of thermal insulation materials in my country is extremely rapid. Porous ceramics are used as thermal insulation materials due to their advantages such as small bulk density, large porosity, and low thermal conductivity, and have great development and application prospects in daily life and production. [0003] When porous ceramics are used as thermal insulation materials, while ensuring excel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B38/06B09B3/00
Inventor 曹卫陆松程旭东龚伦伦杨晖张瑞芳
Owner HEFEI KESIFU SAFETY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products