Ceramic plate for cooking bench, and preparation and application method thereof

A ceramic plate and stove technology, applied in the field of building materials, can solve problems such as being easily affected by temperature changes and water vapor, affecting the home environment, and accumulating large oil pollution, etc., to achieve enhanced microscopic strain performance, simple splicing methods, and speed up construction progress Effect

Inactive Publication Date: 2014-12-10
福建格兰美学智能科技有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of my country's building materials industry, the production and consumption of ceramic tiles have achieved greater development, but most of the ceramic tiles currently on the market are low in strength and fragile, and it is difficult to meet the diverse needs of consumers.
[0003] At the same time, Chinese cooking methods are mainly frying, frying, and frying, and the oily smoke is heavy, which wil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic plate for cooking bench, and preparation and application method thereof
  • Ceramic plate for cooking bench, and preparation and application method thereof
  • Ceramic plate for cooking bench, and preparation and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0070] Example 1

[0071] A ceramic plate for a cooktop is composed of a green body and a glaze; slots for splicing are provided on both sides of the green body.

[0072] The preparation method of the ceramic plate for the cooktop comprises the following steps:

[0073] 1) After adding water to 2 kg of kaolin to make a slurry, slowly add 0.5 kg of epoxy resin toughening emulsion containing modified bamboo fiber, stir thoroughly for 0.5 h, dry, calcined at 200°C for 0.5 h, crush, and pass through a 200-mesh sieve Obtain modified kaolin;

[0074] 2) Mix the modified kaolin in step 1) with 1 kg of phosphogypsum, 0.8 kg of quartz, 0.5 kg of feldspar, and 0.3 kg of lime, and then ball mill to obtain a ceramic slurry;

[0075] 3) Dry or dry the ceramic slurry in step 2) and press it into a ceramic slab body;

[0076] 4) Dry the ceramic slab body in step 3) in a drying kiln until the water content is 3%, raise the temperature of the green body to 1000°C at 10°C / min, keep it warm f...

Example Embodiment

[0091] Example 2

[0092] A ceramic plate for a cooktop is composed of a green body and a glaze; slots for splicing are provided on both sides of the green body.

[0093] The preparation method of the ceramic plate for the cooktop comprises the following steps:

[0094] 1) Add water to 3 kg of kaolin to make a slurry, slowly add 1 kg of epoxy resin toughening emulsion containing modified bamboo fiber, stir thoroughly for 1 hour, dry, calcined at 250°C for 0.5 hour, pulverize, and pass through a 300-mesh sieve to obtain Modified kaolin;

[0095] 2) Mix the modified kaolin in step 1) with 1.5 kg of phosphogypsum, 1.5 kg of quartz, 0.8 kg of feldspar, and 0.5 kg of lime, and then ball mill to obtain a ceramic slurry;

[0096] 3) Dry or dry the ceramic slurry in step 2) and press it into a ceramic slab body;

[0097] 4) Dry the ceramic slab body in step 3) in a drying kiln until the water content is 5%, raise the temperature of the green body to 1200°C at 12°C / min, keep it warm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ceramic plate for a cooking bench, and a preparation and application method thereof. The ceramic plate is composed of a billet and a glaze, wherein both sides of the billet are provided with slots for splicing; and the billet is prepared from kaolin, phosphogypsum, epoxy resin toughening emulsion containing modified bamboo fiber, quartz, feldspar and lime. The application method comprises the following steps: in the cooking bench table top laying or cooking bench integral body construction process, inserting inserts into the slots of the ceramic plate, or coating a tile adhesive layer in the slots of the ceramic plate and inserting inserts into the slots, thereby implementing splicing of the ceramic plates. The ceramic plate has the advantages of favorable toughness, favorable water resistance, favorable wear resistance and favorable self-cleaning performance. The application method is simple, can effectively reduce and even avoid the use of the tile adhesive, can obviously accelerate the construction schedule, and is suitable for constructing the cooking bench table top and cooking bench integral body.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a ceramic plate for a stove top and a preparation method and application thereof. Background technique [0002] Ceramics are plate or block ceramic products produced by clay, quartz sand and other inorganic non-metallic raw materials through batching, ball milling, molding, sintering and other processes. They are used to decorate and protect the walls and floors of buildings. With the rapid development of my country's building materials industry, the production and consumption of ceramic tiles have achieved greater development. However, most of the ceramic panels currently on the market are low in strength and fragile, and it is difficult to meet the diverse needs of consumers. [0003] At the same time, Chinese cooking methods are mainly frying, frying, and frying, and the oily smoke is heavy, which will cause a lot of oil stains to accumulate on the tiles and seams...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/13C04B41/86
Inventor 张可池
Owner 福建格兰美学智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap