EPDM (ethylene-propylene-diene monomer) rubber for air conditioners and preparation technique thereof
A preparation process and technology for air conditioners, applied in the field of air conditioner rubber, can solve the problems of easy oxidation of rubber materials, poor weather resistance, poor performance of air conditioner hoses, etc., and achieve excellent weathering resistance, reasonable formula and excellent comprehensive performance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1 EPDM rubber material for air conditioner of the present invention and preparation process (1)
[0019] Weigh each component by weight : 100 parts of EPDM raw rubber with 10% ENB weight content, 80 parts of carbon black N550, 30 parts of silica, 100 parts of paraffin oil, 6 parts of zinc oxide, 2 parts of stearic acid, 1 part of PEG4000, 8 parts of ointment, 5 parts of calcium oxide, 2 parts of BZ-80, 1 part of MBT-80, 2 parts of CBS-80, 1 part of TDEC-75, 5 parts of AC-75, 7 parts of OBSH, 2 parts of sulfur.
[0020] Preparation Process: a) First make EPDM raw rubber, carbon black, silica, paraffin oil, zinc oxide, stearic acid, PEG4000, and ointment in a rubber mixer to make A rubber, where the rubber discharge temperature of A is 150 degrees, and the Use the tablet after it has been parked for 8 hours.
[0021] b) Add 5 parts of calcium oxide, 2 parts of BZ-80, 1 part of MBT-80, 2 parts of CBS-80, 1 part of TDEC-75, 5 parts of AC-75, OBSH into the rubber compoun...
Example Embodiment
[0022] Example 2 EPDM rubber material for air conditioner of the present invention and preparation process (2)
[0023] Weigh each component by weight : 100 parts of EPDM raw rubber with 7% ENB weight content, 60 parts of carbon black N550, 30 parts of silica, 80 parts of paraffin oil, 8, zinc oxide, 1 part of stearic acid, 3 parts of PEG4000, 5 parts of ointment, oxidation 8 parts of calcium, 1 part of BZ-80, 2 parts of MBT-80, 1 part of CBS-80, 2 parts of TDEC-75, 2 parts of AC-75, 10 parts of OBSH, 1 part of sulfur.
[0024] Preparation Process: a) First make EPDM raw rubber, carbon black, silica, paraffin oil, zinc oxide, stearic acid, PEG4000, and ointment in a rubber mixer to make A rubber, where the rubber discharge temperature of A is 150 degrees, and the Use the tablet after it has been parked for 8 hours.
[0025] b) Add 8 parts of calcium oxide, 1 part of BZ-80, 2 parts of MBT-80, 1 part of CBS-80, 2 parts of TDEC-75, 2 parts of AC-75, 2 parts of AC-75, OBSH into the r...
Example Embodiment
[0026] Example 3 EPDM rubber material for air conditioner of the present invention and its preparation process (3)
[0027] Weigh each component by weight : 100 parts of EPDM raw rubber with 8% ENB weight content, 70 parts of carbon black N550, 30 parts of silica, 90 parts of paraffin oil, 7 parts of zinc oxide, 1.5 parts of stearic acid, 2 parts of PEG4000, 7 parts of ointment, 6 parts of calcium oxide, 1.5 parts of BZ-80, 1.5 parts of MBT-80, 1.5 parts of CBS-80, 1.5 parts of TDEC-75, 3 parts of AC-75, 8 parts of OBSH, 1.5 parts of sulfur.
[0028] Preparation Process: a) First make EPDM raw rubber, carbon black, silica, paraffin oil, zinc oxide, stearic acid, PEG4000, and ointment in a rubber mixer to make A rubber, where the rubber discharge temperature of A is 150 degrees, and the Use the tablet after it has been parked for 8 hours.
[0029] b) Add 6 parts of calcium oxide, 1.5 parts of BZ-80, 1.5 parts of MBT-80, 1.5 parts of CBS-80, 1.5 parts of TDEC-75, 3 parts of AC-75, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap