Finishing liquid for hot-galvanized plate and preparation method for finishing liquid

A hot-dip galvanized sheet and solution technology, which is applied in the petroleum industry, lubricating compositions, etc., can solve the problems of rolling mills, rolls, and steel plate corrosion, zinc particles or impurities combined with the roll surface are difficult to eliminate, light spots in skinning and roll marks in skinning, etc. problems, to achieve excellent rust resistance, eliminate or reduce bright spot defects in finishing, and excellent wetting effect

Active Publication Date: 2014-12-10
江苏苏北能源科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] When skin-passing hot-dip galvanized sheets in existing skin-passing machines, zinc particles or other impurities adhering to the skin-passing support rolls will also be copied to the work rolls. The tighter combination will become more and more difficult to eliminate, resulting in skinning bright spots and skinning roll marks. Therefore, high-pressure water is used behind the skinning machine to wash the roll gap and roll surface in time. Because the rolling mill, rolls and steel plates are all For ferrous metals, long-term washing with water will cause corrosion of rolling mills, rolls and steel plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A skin-passing solution for hot-dip galvanized sheets of the present invention consists of the following parts by weight:

[0053] Component 1: 23 parts of water

[0054] 8 parts of dibasic acid

[0055] 12 parts of tricarboxylic acid

[0056] 57 parts of triethanolamine

[0057] Component two: 54 parts of water

[0058] Sodium carbonate 8 parts

[0059] Potassium hydroxide 5 parts

[0060] 3 parts disodium edetate

[0061] 10 parts of sodium metasilicate pentahydrate

[0062] Reverse blocking polyether 8 parts

[0063] Neodecanoic acid 8 parts

[0064] 4 parts sodium benzoate

[0065] A kind of preparation method of hot-dip galvanized sheet skinning solution of the present invention, its steps are as follows:

[0066] a) Component 1: Take 23 parts of water, add 8 parts of dibasic acid, 12 parts of tribasic carboxylic acid, and 57 parts of triethanolamine, stir while adding, heat up to 60°C, keep warm for 2 hours, let the liquid completely react until it...

Embodiment 2

[0071] A skin-passing solution for hot-dip galvanized sheets of the present invention consists of the following parts by weight:

[0072] Component 1: 30 parts of water

[0073] 7 parts of dibasic acid

[0074] 10 parts of tricarboxylic acid

[0075] 53 parts of triethanolamine

[0076] Component two: 55 parts of water

[0077] Sodium carbonate 7 parts

[0078] Potassium hydroxide 4 parts

[0079] 2 parts disodium edetate

[0080] 8 parts of sodium metasilicate pentahydrate

[0081] Reverse blocking polyether 12 parts

[0082] Alkylphenol polyoxyethylene ether phosphate potassium salt 8 parts

[0083] 4 parts sodium benzoate

[0084] A kind of preparation method of hot-dip galvanized sheet skinning solution of the present invention, its steps are as follows:

[0085] a) Component 1: Take 30 parts of water, add 7 parts of dibasic acid, 10 parts of tribasic carboxylic acid, and 53 parts of triethanolamine, stir while adding, heat up to 60°C, keep warm for 2 hours, let ...

Embodiment 3

[0090] A skin-passing solution for hot-dip galvanized sheets of the present invention consists of the following parts by weight:

[0091] Component 1: 30 parts of water

[0092] 7 parts of dibasic acid

[0093] 10 parts of tricarboxylic acid

[0094] 53 parts of triethanolamine

[0095] Component two: 58 parts of water

[0096] Sodium carbonate 7 parts

[0097] Potassium hydroxide 4 parts

[0098] 2 parts disodium edetate

[0099] 8 parts of sodium metasilicate pentahydrate

[0100] Reverse blocking polyether 10 parts

[0101] Neodecanoic acid 7 parts

[0102] 4 parts sodium benzoate

[0103] A kind of preparation method of hot-dip galvanized sheet skinning solution of the present invention, its steps are as follows:

[0104] a) Component 1: Take 30 parts of water, add 7 parts of dibasic acid, 10 parts of tribasic carboxylic acid, and 53 parts of triethanolamine, stir while adding, heat up to 60°C, keep warm for 2 hours, let the liquid completely react until ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to finishing liquid for a hot-galvanized plate and a preparation method for the finishing liquid. The finishing liquid comprises a component I and a component II, wherein the component I comprises following ingredients in parts by weight: 23-33 parts of water, 5-8 parts of dibasic acid, 8-12 parts of tricarboxylic acid and 54-57 parts of triethanolamine; the component II comprises following ingredients in parts by weight: 47-68 parts of water, 4-8 parts of sodium carbonate, 3-5 parts of potassium hydroxide, 2-4 parts of disodium ethylenediamine tetraacetate, 6-10 parts of sodium metasilicate pentahydrate, 8-12 parts of reverse block polyether, 6-8 parts of neodecanoic acid and 3-6 parts of sodium benzoate. The finishing liquid has relatively good rust-proof and lubricating effects, has excellent wetting and cleaning properties and relatively high cleaning ability, and can lubricate and repair the surface of a roll; the finished galvanized plate is smooth in surface, and defects of finishing spots and coating moire can be effectively eliminated or reduced; the finishing liquid has good foam-inhibiting and defoaming functions, so that liquid can be avoided from remaining on the surfaces of the roll and a steel plate and the foam can be avoided from overflowing around to affect the working environment.

Description

technical field [0001] The invention relates to the field of iron and steel industry, in particular to a skin pass solution for hot-dip galvanized sheets and a preparation method thereof. Background technique [0002] At present, with the development of the iron and steel industry, the production technology of hot-dip galvanized sheet in the iron and steel industry has developed rapidly. The rapid development of hot-dip galvanized technology makes the surface quality comparable to that of cold-rolled sheet and electro-galvanized sheet. Hot-dip galvanized products are used in the fields of automobiles and household appliances. Widely used, especially the amount of hot-dip galvanized sheets for automobiles has also increased sharply, and the production technology of hot-dip galvanized sheets for automobiles is constantly improving. my country has become the world's largest producer of hot-dip galvanized sheets. While vigorously improving the productivity of hot-dip galvanized ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10M177/00C10N30/12
Inventor 肖颖谭小燕
Owner 江苏苏北能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products