Preparation method and application of nano barium sulphate
A technology of nano-barium sulfate and preparation steps, which is applied in the direction of electrolysis process, reflection/signal coating, electrolysis components, etc. It can solve the problems of poor product stability and large particle size, and achieve stable product quality, good effect and stable performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1
[0030] 1) Prepare 45 parts by weight of barium chloride and 45 parts by weight of sodium sulfate into solutions with the same concentration of 0.5 mol / L, and set aside;
[0031] 2) Mix an appropriate amount of sodium chloride solution with a concentration of 0.5mol / L and 3 parts by weight of anti-agglomeration agent and add them to the electrolytic cell. Use carbon rods as electrode materials for the cathode and anode. The power supply is a DC power supply with a voltage of 120V. , Conduct electrolysis under normal temperature and pressure;
[0032] 3) Under the condition that step 2) is energized, add the barium chloride solution and sodium sulfate solution obtained in step 1) at the same speed from the anode and cathode of the electrolytic cell at the same time, and react for 3 minutes while keeping the power on. After power off Get a mixed solution. During the electrification reaction, the barium ions in the solution quickly move to the cathode under the acti...
Example Embodiment
[0035] Example 2
[0036] 1) Prepare 45 parts by weight of barium chloride and 45 parts by weight of sodium sulfate into solutions with the same concentration of 4.0 mol / L, and set aside;
[0037] 2) Mix an appropriate amount of sodium chloride solution with a concentration of 0.5mol / L and 5 parts by weight of anti-agglomeration agent and add them to the electrolytic cell. Use carbon rods as electrode materials for the cathode and anode. The power supply is a DC power supply with a voltage of 240V. , Conduct electrolysis under normal temperature and pressure;
[0038] 3) Under the condition that step 2) is energized, add the barium chloride solution and sodium sulfate solution obtained in step 1) at the same speed from the anode and cathode of the electrolytic cell at the same time, and react for 5 minutes while keeping the power on. After power off Get a mixed solution. During the electrification reaction process, the barium ions in the solution move quickly to the cathode under ...
Example Embodiment
[0041] Example 3
[0042] 1) Prepare 50 parts by weight of barium chloride and 50 parts by weight of sodium sulfate into solutions with the same concentration of 2.5 mol / L, and set aside;
[0043] 2) Mix an appropriate amount of sodium chloride solution with a concentration of 1.5 mol / L and 5 parts by weight of anti-agglomeration agent and add them to the electrolytic cell. Use carbon rods as electrode materials for the cathode and anode. The power supply is a DC power supply with a voltage of 220V. , Conduct electrolysis under normal temperature and pressure;
[0044] 3) Under the condition that step 2) is energized, add the barium chloride solution and sodium sulfate solution obtained in step 1) at the same speed from the anode and cathode of the electrolytic cell at the same time, and react for 3 minutes while keeping the power on. After power off Get a mixed solution. During the electrification reaction process, the barium ions in the solution move quickly to the cathode under...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap