A methanol gasoline, rubber swelling technology, applied in the petroleum industry, fuel additives, liquid carbon-containing fuels and other directions, can solve problems such as automobile metal corrosion
Active Publication Date: 2015-01-07
QIDONG YONGXING RUBBER PROD
View PDF3 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] The purpose of the present invention is to overcome the deficiency of prior art, provide a kind of methanol gasoline rubber swelling inhibitor that raw material is easy to get, easy to use, to solve the swelling problem of methanol gasoline to automobile rubber parts, and prevent methanol gasoline from damaging the rubber parts during use. Corrosion of Automotive Metals
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] Take 12 kilograms of 2-mercaptobenzothiazole, 8 kilograms of iodopropyne n-butyl carbamate, 1 kilogram of butyl hydroxyanisole, 16 kilograms of 2,6-di-tert-butyl-p-cresol; dodecyl sulfonic acid Sodium 8 kg, 2-ethylimidazole 13 kg, cyclooctadiene ruthenium dichloride 6 kg, p-methoxypropiophenone 9 kg, polyisobutylene succinimide 2 kg, tert-butyldimethylchlorosilane 3 kg, 12 kg of methyl tert-butyl ether. Add them to the reaction kettle one by one, seal and stir the reaction at 55-58°C for 60-80 minutes, and serve after cooling.
Embodiment 2
[0021] Take 12 kilograms of 2-mercaptobenzothiazole, 6 kilograms of iodopropyne n-butyl carbamate, 1 kilogram of butyl hydroxyanisole, 15 kilograms of 2,6-di-tert-butyl-p-cresol; dodecyl sulfonic acid Sodium 7 kg, 2-ethylimidazole 12 kg, cyclooctadiene ruthenium dichloride 6 kg, p-methoxypropiophenone 8 kg, polyisobutylene succinimide 2 kg, tert-butyldimethylchlorosilane 3 kg, 12 kg of methyl tert-butyl ether. Add them to the reaction kettle one by one, seal and stir the reaction at 55-58°C for 60-80 minutes, and serve after cooling.
Embodiment 3
[0023] Take 13 kilograms of 2-mercaptobenzothiazole, 9 kilograms of iodopropyne n-butyl carbamate, 2 kilograms of butyl hydroxyanisole, 18 kilograms of 2,6-di-tert-butyl-p-cresol; dodecyl sulfonic acid Sodium 10 kg, 2-ethylimidazole 15 kg, cyclooctadiene ruthenium dichloride 9 kg, p-methoxypropiophenone 12 kg, polyisobutylene succinimide 3 kg, tert-butyldimethylchlorosilane 4 kg, 13 kg of methyl tert-butyl ether. Add them to the reaction kettle one by one, seal and stir the reaction at 55-58°C for 60-80 minutes, and serve after cooling.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
A methanol gasoline rubber swelling inhibitor is prepared from the following ingredients in parts by weight: 12 parts of 2-mercaptobenzothiazole, 8 parts of iodopropynyl butylcarbamate, 1 part of butylated hydroxyanisole, 16 parts of 2,6-butylated hydroxytoluene, 8 parts of sodium dodecyl sulfonate, 13 parts of 2-ethylimidazole, 6 parts of dichloro[(1,2,5,6-eta)-cycloocta-1,5-diene]ruthenium, 9 parts of methoxypropiophenone, 2 parts of polyisobutylene succinimide, 3 parts of tert-butyldimethylsilyl chloride and 12 parts of methyl tert-butyl ether. The methanol gasoline rubber swelling inhibitor is used by the method that the methanol gasoline rubber swelling inhibitor is directly added into methanol gasoline M15-M30 and mixed uniformly, and the adding quantity is 0.4-0.7% of the weight of the methanol gasoline. The methanol gasoline rubber swelling inhibitor has excellent oxidation resistance and excellent corrosion resistance, and can prevent related seal parts of a vehicle from being worn or corroded, keep the elasticity of rubber components and prevent rubber aging.
Description
Technical field [0001] The invention relates to a fuel oil additive for vehicles, in particular to a methanol gasoline rubber swelling inhibitor. Background technique [0002] Methanol gasoline refers to a new type of environmentally friendly fuel methanol and gasoline mixture that is formulated by a strict process with a certain volume (mass) ratio of national standard gasoline (93#, 97#, etc.), methanol, and additives. It also includes mixtures of methanol, ethanol, n-propanol, n-butanol and isopropanol, and gasoline. [0003] The amount of methanol incorporated is generally 5% to 30%. With 15% blending as the most, it is called M15 methanol gasoline. The anti-knock performance is good, the research octane number (RON) increases with the increase of the amount of methanol added, and the motor octane number (MON) is not affected. Combustion emissions are less toxic than ordinary leaded gasoline, and the exhaust gas contains less carbon monoxide. Good combustion cleaning perfor...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.