Polyphenylene sulfide/semi-aromatic nylon composite material and preparation method thereof

A technology of semi-aromatic nylon and polyphenylene sulfide, applied in the field of polyphenylene sulfide/semi-aromatic nylon composite materials and their preparation, can solve the problems of high molding shrinkage, poor appearance of composite materials, and poor processing fluidity Good and other problems, to achieve the effect of good thermal stability, low molding shrinkage, high continuous production efficiency

Inactive Publication Date: 2015-01-14
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the problems of poor toughness of polyphenylene sulfide/semi-aromatic nylon alloy materials in the prior art, poor processing fluidity, poor appearance of composite materials, and high moldi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphenylene sulfide/semi-aromatic nylon composite material and preparation method thereof
  • Polyphenylene sulfide/semi-aromatic nylon composite material and preparation method thereof
  • Polyphenylene sulfide/semi-aromatic nylon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A polyphenylene sulfide / semi-aromatic nylon composite material is made of the following raw materials in parts by weight: 60 parts of polyphenylene sulfide resin, 50 parts of semi-aromatic nylon PA10T, 10 parts of wollastonite, and 30 parts of alkali-free glass fiber , 5 parts of maleic anhydride, 2 parts of calcium stearate lubricant, 0.5 parts of antioxidant, wherein the antioxidant is tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] Pentaerythritol ester; The preparation method of polyphenylene sulfide / semi-aromatic nylon composite material is:

[0028] (1) Put the polyphenylene sulfide resin and semi-aromatic nylon resin into the drying box respectively, and dry at 110°C for 8-10 hours;

[0029] (2) Put the glass fibers in a drying oven and dry at 90°C for 1 to 2 hours;

[0030] (3) Put the inorganic mineral filler, compatibilizer, lubricant and antioxidant into the drying box respectively, and dry at 90-100°C for 1-3 hours;

[0031] (4) Weigh the p...

Embodiment 2

[0034] A polyphenylene sulfide / semi-aromatic nylon composite material is made of the following raw materials in parts by weight: 60 parts of polyphenylene sulfide resin, 50 parts of semi-aromatic nylon PA10T, 20 parts of wollastonite, and 30 parts of alkali-free glass fiber , 10 parts of maleic anhydride, 2 parts of calcium stearate lubricant, 1 part of antioxidant, wherein the antioxidant is tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] Pentaerythritol esters;

[0035] Its preparation method is with embodiment 1.

Embodiment 3

[0037] A polyphenylene sulfide / semi-aromatic nylon composite material is made of the following raw materials in parts by weight: 60 parts of polyphenylene sulfide resin, 50 parts of semi-aromatic nylon PA10T, 20 parts of wollastonite, and 20 parts of alkali-free glass fiber , 10 parts of maleic anhydride, 2 parts of calcium stearate lubricant, 1 part of antioxidant, wherein the antioxidant is tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] Pentaerythritol esters;

[0038] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical fields of high-molecular material processing and modification, and relates to a polyphenylene sulfide/semi-aromatic nylon composite material and a preparation method thereof. The composite material is prepared by using the following components, by weight, 50-70 parts of polyphenylene sulfide, 40-60 parts of semi-aromatic nylon, 10-30 parts of a glass fiber, 10-20 parts of an inorganic mineral filler, 1-15 parts of a compatilizer, 0.5-2 parts of an antioxidant and 1-3 parts of a lubricant. The material disclosed in that invention has the advantages of low molding shrinkage, good dimension stability, high toughness, excellent high temperature resistance and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer material processing and modification, and relates to a polyphenylene sulfide / semi-aromatic nylon composite material and a preparation method thereof. Background technique [0002] Polyphenylene sulfide resin (PPS), also known as polyphenylene sulfide, has good comprehensive properties, high temperature resistance, corrosion resistance, radiation resistance, non-combustibility, and good mechanical and electrical properties. However, polyphenylene sulfide resin has low impact strength and poor bending resistance; moreover, PPS has high melt viscosity, poor fluidity, and poor processing performance; at the same time, its cost is relatively high compared with general engineering plastics. These shortcomings limit polyphenylene sulfide. The scope of application of ether resin. Semi-aromatic high-temperature-resistant nylon series materials represented by nylon 6T, 9T, 10T, 12T, etc. have excellent wea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08L77/06C08K13/04C08K7/14C08K3/34C08K3/26C08K3/30B29B9/06B29C47/92B29C48/92
CPCC08L81/02B29B9/06B29C48/92B29C2948/9259B29C2948/92704C08L2201/08C08L2205/03C08L77/06C08K13/04C08K7/14C08K3/34C08K5/1539C08K5/098C08K5/1345C08K2003/265C08K2003/3045C08K3/346C08L51/00
Inventor 杨桂生李宗仁
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap