Mildew-proof wear-resistant asphalt paint and preparation method thereof

An asphalt paint and anti-mildew technology, used in biocide-containing paints, antifouling/underwater coatings, coatings, etc., can solve problems such as slow decomposition, soil hazards, and polluted water sources, to improve quality and solve environmental problems. Effects of contamination, good abrasion resistance

Inactive Publication Date: 2015-01-21
TIANCHANG YINHU PAINT
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The various organic resins or organic and inorganic compounds contained in a large amount of waste resin sand piled up are slow to decompose, causing serious harm to the so

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] specific implementation plan

[0015] The present invention will be described in detail below through specific examples.

[0016] A mildew-resistant and wear-resistant asphalt paint, prepared from the following raw materials in parts by weight (kg): E-22 epoxy resin 21, benzyl transparent silicone resin 9, polyether acrylate 8, tetraethylenepentamine 4, Tricresyl Phosphate 4, Nano Bamboo Fiber 2, Zinc Chromate 2, Modified Asphalt 37, Modified Waste Resin Sand 5, Ammonium Bromide 1, Glycerin Triacetate 2, Catechin 3, Epoxy Linseed Oil 4 , Amyl acetate 11, xylene 7, ethylene glycol 6, tris(dioctylphosphoryloxy)isopropyl titanate 1, aluminum powder 2;

[0017] The modified asphalt is made of the following raw materials in parts by weight (kg): asphalt 82, sulfur 0.6, polypropylene wax 0.5, nano diatomite 0.8, diaminodiphenylmethane 0.4, activated carbon 1, vinyl acetate resin 9, Maleic anhydride 4, potassium aluminum sulfate dodecahydrate 0.4, tetrahydrofuran 8, zirconi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses mildew-proof wear-resistant asphalt paint which is characterized by being prepared from the following raw materials in parts by weight: 17-23 parts of E-22 epoxy resins, 6-9 parts of benzyl transparent silicon resins, 8-11 parts of polyether acrylate, 4-7 parts of tetraethylenepentamine, 3-5 parts of tricresyl phosphate, 1-3 parts of nano bamboo fibers, 2-4 parts of zinc chromate, 37-43 parts of modified asphalt, 5-7 parts of modified waste resin sand, 1-2 parts of ammonium bromide, 2-4 parts of fungacetin, 3-4 parts of catechinic acid, 4-6 parts of epoxy linseed oil, 8-11 parts of amyl acetate, 6-9 parts of xylene, 5-7 parts of glycol, 1-2 parts of tri(dioctylphosphoryloxy) titanium isopropoxide and 2-4 parts of powdered aluminum. The mildew-proof wear-resistant asphalt paint is prepared by adding the epoxy resins on the basis of the modified asphalt, so that the characteristics of high corrosion resistance, weather fastness, waterproofness and thermal stability of the pain are ensured; the added tricresyl phosphate has the characteristics of favorable wear resistance, weather fastness, mildew resistance and radiation resistance; and the added modified waste resin sand has favorable fire resistance, antifouling property and anti-ageing property, so that the quality of the paint is improved and the waste is recycled to solve the problem of environment pollution.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to a mildew-proof and wear-resistant asphalt paint and a preparation method thereof. Background technique [0002] Asphalt paint is suitable for the protection of steel structures, electrified railway systems, ships, bridges and various galvanized equipment, iron pipes, corrugated plates, and galvanized steel frame structures in high-temperature, chemical, air pollution, and seaside high-salt environments that are prone to corrosion. coating. Epoxy resin paint is a coating with epoxy resin paint as the main film-forming substance. Strong adhesion, excellent chemical resistance, corrosion resistance, water resistance, thermal stability and electrical insulation, widely used in construction, chemical industry, automobiles, ships, electrical insulation, etc. Tricresyl phosphate has good abrasion resistance, weather resistance, mildew resistance, radiation resistance and ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D151/00C09D163/02C09D183/04C09D171/00C09D127/06C09D7/12C09D5/14C08F289/00
CPCC08F289/00C08L2205/035C09D7/61C09D7/62C09D7/65C09D151/00C08L63/00C08L83/04C08L71/00C08K13/06C08K3/06C08K3/346C08K3/04C08K2003/0812C08K2003/2296C08K2003/324C08K3/36C08F222/06
Inventor 汪鹏程祝秀凤
Owner TIANCHANG YINHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap