High-performance anti-static antibacterial glass-fiber reinforced AS composite material and preparation method thereof

Abstract

The invention provides a high-performance anti-static antibacterial glass-fiber reinforced AS (acrylonitrile-styrene) composite material and a preparation method thereof. The high-performance anti-static antibacterial glass-fiber reinforced AS composite material comprises the following components in percentage by weight: 43-88.4 percent of AS resin, 10-30 percent of glass fiber, 1-5 percent of a compatilizer, 0.1-1 percent of a coupling agent, 10-15 percent of an antistatic agent, 0.5-2 percent of an antibacterial agent and 0.1-3 percent of an additive, wherein the compatilizer is made of PMMA (polymethyl methacrylate); the coupling agent adopts a silane coupling agent. The AS resin is used as a matrix, and has the advantages of excellent performance, low cost, simple preparation process and the like; made of PMMA, the compatilizer is not only used for enhancing the binding force between the glass fiber and the AS resin, but also suitable for enhancing a composite material system of fiber and resin with similarity properties.

Description

technical field [0001] The invention belongs to the field of modified plastics, in particular to a high-performance antistatic and antibacterial glass fiber reinforced AS composite material and a preparation method thereof. Background technique [0002] Acrylonitrile-styrene resin, namely AS resin, is a kind of thermoplastic made by copolymerization of styrene (St) and acrylonitrile (AN) as raw materials. AS resin has excellent performance and excellent Dimensional stability, electrical properties, wear resistance, chemical resistance, dyeability, molding processing and mechanical processing are good, and it is an important engineering plastic. [0003] Glass fiber reinforced plastics have the advantages of high specific strength, corrosion resistance, heat insulation, and low molding shrinkage. Using glass fiber reinforcement can greatly improve the tensile properties of plastics. Adding glass fiber to AS resin can enhance the strength and thermal deformation resistance of...

AI Technical Summary

Problems solved by technology

The compound increases the Vicat softening temperature, but the flexural modulus is too low, only 5000MPa; and due to the addition of a large amount of ABS and SMA, the manufacturing cost increases

In Chinese patents CN1362443A and CN1352212A, methacrylic acid-butadiene-styrene copolymer (MBS), AS, SMA, ABS and glass fiber are used as raw materials to blend the AS compound, but it increases the glass fiber Dipping treatment steps, complex process and further cost increase

In addition, the Chinese patent CN201110138482 uses AS, glass fiber, and coupling agent as raw materials, and by adjusting the screw combination, a reinforced AS composite material with a relatively uniform density is prepared, but the tensile strength of the prepared composite material is 100-110MPa, and the impact strength At 5.5-6.5kJ / m 2 , the performance is also lower