Preparation method of low-temperature cross-linking resin for textiles

A low-temperature cross-linking, textile technology, applied in textiles, papermaking, fiber processing, etc., can solve the problems of high energy consumption and unsatisfactory, and achieve the effect of saving energy and realizing energy saving and environmental protection.

Active Publication Date: 2016-09-28
HANGZHOU MEIGAO HUAYI CHEM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the unsatisfactory problems of environmental protection and high energy consumption in the cross-linked resin in the prior art, and provides a low-temperature cross-linked resin, which is environmentally friendly and has a good finishing effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of low-temperature cross-linking resin for textiles
  • Preparation method of low-temperature cross-linking resin for textiles
  • Preparation method of low-temperature cross-linking resin for textiles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Mix 90g of vinyl acetate, 10g of acrylic acid and 10g of diacetone acrylamide to form a mixed monomer, and dissolve 0.33g of ammonium persulfate in 30g of water. Put 10g of polyvinyl alcohol 1799 and 150g of water into the reaction vessel, start stirring, raise the temperature to 90°C, keep it warm for 1.5 hours and then cool down to 75°C, then add 4.4g of sodium lauryl sulfate and isomeric tridecanol polyoxygen The composite emulsifier composed of vinyl ether, after fully dissolving, slowly add the mixed monomer and ammonium persulfate aqueous solution dropwise, and the dropwise addition is completed within 3 hours, then raise the temperature to 85°C, keep the temperature for 2 hours, cool down to below 50°C, use Adjust the pH to 7.21 with ammonia water, then add 10.3 g of adipic acid dihydrazide, stir for 1 hour, mix well and discharge, and the obtained product is a low-temperature cross-linked resin product.

[0032] See attached figure 1 , it is the infrared spectr...

Embodiment 2

[0034] Mix 90g of vinyl acetate, 10g of acrylic acid and 15g of diacetone acrylamide to form a mixed monomer, and dissolve 0.35g of ammonium persulfate in 30g of water. Put 12g of polyvinyl alcohol 1799 and 160g of water into the reaction vessel, start stirring, raise the temperature to 88°C, keep it warm for 1.5 hours and then cool down to 73°C, then add 4.6g of sodium lauryl sulfate and isomeric tridecanol polyoxygen The composite emulsifier composed of vinyl ether, after fully dissolving, slowly add the mixed monomer and ammonium persulfate aqueous solution dropwise, and the dropwise addition is completed within 3 hours, then raise the temperature to 84°C, keep the temperature for 3 hours, cool down to below 50°C, use Adjust the pH to 6.84 with ammonia water, then add 16g of adipic acid dihydrazide, stir for 1 hour, mix well and discharge, and the obtained product is a low-temperature cross-linked resin product.

[0035] See attached figure 2 , it is the infrared spectrog...

Embodiment 3

[0037] Mix 90g of vinyl acetate, 10g of methacrylic acid and 10g of diacetone acrylamide to form a mixed monomer, and dissolve 0.33g of ammonium persulfate in 30g of water. Put 10g of polyvinyl alcohol 1799 and 150g of water into the reaction vessel, start stirring, raise the temperature to 89°C, keep it warm for 1.5 hours and then cool down to 72°C, then add 4.5g of sodium lauryl sulfate and isomeric tridecanol polyoxygen The composite emulsifier composed of vinyl ether, after fully dissolving, slowly add the mixed monomer and ammonium persulfate aqueous solution dropwise, and the dropwise addition is completed within 3 hours, then raise the temperature to 83°C, keep the temperature for 2 hours, cool down to below 50°C, use Adjust the pH to 7.08 with ammonia water, then add 10.5 g of adipic acid dihydrazide, stir for 1 hour, mix well and discharge, and the obtained product is a low-temperature cross-linked resin product.

[0038] See attached image 3 , it is the infrared sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of textile auxiliary agent, especially relates to a method for preparing a low temperature crosslinking resin for textiles. The method is carried out according to the following steps: mixing raw materials, stirring and controlling temperature, adding a monomer mixture, adding a monomer mixture and discharging. The method has high environmental performance, and can effectively save energy and achieve energy saving and environmental protection.

Description

technical field [0001] The invention relates to the field of textile auxiliaries, in particular to a method for preparing a low-temperature cross-linking resin used for textiles. Background technique [0002] Cross-linked resins are widely used in the finishing of fabrics such as stiffness, wrinkle resistance, and coating, among which it is particularly important for the stiffness finishing of curtain fabrics, luggage fabrics, and tent fabrics and the durable non-ironing finishing of cotton fabrics. At present, domestic resin finishing agents are mainly modified melamine resins and urea-formaldehyde resins, which have good stiffness and anti-wrinkle effects. However, this type of resin will release formaldehyde, which will seriously affect the physical and mental health of producers, users and consumers, and cause extremely adverse effects on the environment. [0003] As the international market has increasingly stringent environmental protection requirements for fabrics, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/21C08F218/08C08F220/58C08F220/06C08F2/26C08F2/30C08J3/24
Inventor 高雏燕陈焜
Owner HANGZHOU MEIGAO HUAYI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap