A kind of fireproof exterior wall dry powder mortar

A dry powder mortar and exterior wall technology, applied in the field of building materials, can solve the problems of poor high temperature resistance effect of polystyrene board, rising overall project cost, unsatisfactory fire prevention effect, etc., and achieves environmental protection requirements, economical and practical materials, and good adhesion. force effect

Inactive Publication Date: 2016-09-21
DEQING YANGTAI BUILDING MATERIAL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the high temperature resistance effect of polystyrene board is extremely poor, and the fire prevention effect is not ideal. It once caused fires in Shanghai, Shenyang and other places, and the country forcibly banned the use of polystyrene board.
The inorganic vitrified bead insulation mortar is relatively safe because it is composed of non-combustible inorganic materials, but its high cost will lead to an increase in the overall cost of the project

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fireproof exterior wall dry powder mortar
  • A kind of fireproof exterior wall dry powder mortar
  • A kind of fireproof exterior wall dry powder mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A dry powder mortar for a fireproof exterior wall, consisting of the following components by weight percentage:

[0033]

[0034]

[0035] Described portland cement is 42.5R cement;

[0036] The particle size of the quartz sand is 200 mesh;

[0037] The yellow sand is river sand with a mud content of 1% and a density of 2500kg / m 3 ;

[0038] The particle diameter of described gangue powder is 600 mesh;

[0039] Described bentonite is organic bentonite;

[0040] Described redispersible latex powder is the rubber powder that polyvinyl acetate and polyvinyl alcohol generate through copolymerization reaction;

[0041] The cellulose ether is methyl hydroxyethyl cellulose ether;

[0042] The particle diameter of described fused magnesia fine powder is 600 orders;

[0043] The particle diameter of described sepiolite powder is 200 orders;

[0044] The used raw material of embodiment 2-6 is identical with embodiment 1, and the proportioning ratio of each raw materi...

Embodiment 7

[0052] A dry powder mortar for a fireproof exterior wall, consisting of the following components by weight percentage:

[0053]

[0054]

[0055] Described portland cement is 32.5R cement;

[0056] The particle size of the quartz sand is 200 mesh;

[0057] The yellow sand is river sand with a mud content of 1% and a density of 2500kg / m3 ;

[0058] The particle diameter of described gangue powder is 600 mesh;

[0059] Described bentonite is organic bentonite;

[0060] Described redispersible latex powder is the rubber powder that polyvinyl acetate and polyvinyl alcohol generate through copolymerization reaction;

[0061] The cellulose ether is methyl hydroxypropyl cellulose ether;

[0062] The particle diameter of described fused magnesia fine powder is 600 orders;

[0063] The particle diameter of described sepiolite powder is 200 orders;

[0064] The used raw material of embodiment 8-12 is identical with embodiment 7, and the proportioning ratio of each raw materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses fireproof dry-mixed mortar for an exterior wall. The fireproof dry-mixed mortar is composed of the following components in percentage by weight: portland cement, quartz sand, filler, bentonite, redispersible latex powder, cellulose ether, citric acid, fine fused magnesite powder and sepiolite powder. The fireproof dry-mixed mortar has a favorable adhesive force with a fundamental plane, and materials are economic and practical, so that the cost can be reduced; meanwhile, a base layer treated by using the material cannot bulge and flake, so that a construction site can be kept clean, and the requirement for environment friendliness can be better met; and part of yellow sand is replaced with gangue, so that the pollution can be relieved, the cost can be reduced, and the fireproof effect can also be achieved.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a dry powder mortar for fireproof exterior walls and a preparation method thereof. Background technique [0002] With the rapid development of the construction industry, the requirements for the quality of the construction industry are getting higher and higher. Due to the influence of the technical proficiency of the construction workers and various raw materials such as cement and sand, the mortar configured on the construction site, whether it is masonry mortar, plastering mortar or ground leveling mortar, often cracks in the plastering mortar of buildings (even if It is the most traditional clay wall brick that will crack in a large area when it is plastered with cement mortar), resulting in unstable project quality, less than the required strength, and even poor quality, which has become a common problem in construction quality. In addition, with the improvemen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B14/06C04B111/28
Inventor 林德
Owner DEQING YANGTAI BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com