Edge coating method of rice straw board furniture member

A rice straw and edge technology, which is applied in the field of material and product production, can solve the problems of poor paint film adhesion, paint film impact resistance, roughness, and unsatisfactory rice straw board finishing quality, etc. The effect of improving paint film performance and promoting green development

Inactive Publication Date: 2015-05-27
梅州市汇胜木制品有限公司 +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the rough edges of rice straw boards, the edge coating quality of rice straw boards has been unsatisfactory, and its paint film adhesion and impact resistance are poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1. Sawing straight-edged boards

[0029] 1. Milling and trimming of the edge of the base material: the sliding table saw saws the rice straw board, and the saw blade rotates at 4000r / min. Saw and cut into 250*200*32mm straight-edged boards. After milling the edge of the rice straw board, clean the edge with 180# sandpaper to remove dander.

[0030] 2. Use putty to inlay rice straw board: putty made of CaCO 3 , water, white latex, carboxymethyl cellulose, etc. (200:100:20:3), using white latex with a high solid content (50%), after the edge of the rice straw board is embedded, dry at room temperature 4h, then sand the surface with 180# sandpaper to remove the excess putty on the surface; the roughness after sanding is 4.09um.

[0031] 3. Polyurethane sealing primer: spray polyurethane sealing primer on the rice straw board, the mass ratio of polyurethane sealing primer is PU primer: PU curing agent: PU thinner = 1:0.5:0.5, viscosity 17s, spray 1 Cross (coatin...

Embodiment 2

[0040] Embodiment 2. Milling machine milling plate (convex type)

[0041] 1. Milling and trimming of the edge of the base material: the sliding table saw cuts the rice straw board, and the saw blade rotates at 10000r / min. Saw and cut into 250*200*32mm straight-edged boards. After milling the edge of the rice straw board, clean the edge with 180# sandpaper to remove dander.

[0042] 2. Use putty to inlay rice straw board: putty made of CaCO 3, water, white latex, carboxymethyl cellulose, etc. (200:100:20:3), using white latex with a high solid content (50%), after the edge of the rice straw board is embedded, dry at room temperature 4h, then sand the surface with 180# sandpaper to sand off the excess putty on the surface; the roughness after sanding is about 4.4 um.

[0043] 3. Polyurethane sealing primer: spray polyurethane sealing primer on the rice straw board, the mass ratio of polyurethane sealing primer is PU primer: PU curing agent: PU thinner = 1:0.5:0.5, viscosity 1...

Embodiment 3

[0052] Example 3. Milling machine milling plate (concave type)

[0053] 1. Milling and trimming of the edge of the base material: the sliding table saw cuts the rice straw board, and the saw blade rotates at 10000r / min. Saw and cut into 250*200*32mm straight-edged boards. After milling the edge of the rice straw board, clean the edge with 180# sandpaper to remove dander.

[0054] 2. Use putty to inlay rice straw board: putty made of CaCO 3 , water, white latex, carboxymethyl cellulose, etc. (200:100:20:3), using white latex with a high solid content (50%), after the edge of the rice straw board is embedded, dry at room temperature 4h, then sand the surface with 180# sandpaper to remove the excess putty on the surface; the roughness after sanding is about 4.2um.

[0055] 3. Polyurethane sealing primer: spray polyurethane sealing primer on the rice straw board, the mass ratio of polyurethane sealing primer is PU primer: PU curing agent: PU thinner = 1:0.5:0.5, viscosity 17s, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an edge coating method of a rice straw board furniture member. The method comprises the following process steps: (1) sawing a base material; (2) milling and finishing an edge of the base material; (3) inlaying putty; (4) closing a primer by polyurethane; (5) spraying a nitrocellulose primer to a rice straw board for five times; (6) spraying a nitrocellulose finish. The method has the advantages that (1) the film coating performance of the edge of rice straw board furniture is effectively improved; rational processes and paint film surface performance testing are formulated for coating of the edge of the rice straw board furniture on the basis of process practice and scientific experiments; (2) a scientific process method is provided for coating of the edge of the rice straw board furniture; (3) the utilization rate of the rice straw board in the furniture manufacturing field is favorably improved, the primer, a middle layer and the finish are matched by using the polyurethane paint and the nitrocellulose paint with higher economy and environmental friendliness, so the film coating performance of the furniture is improved, the application of the rice straw board to the furniture manufacturing field is favorably promoted, and the environment-friendly development of the furniture industry is promoted.

Description

technical field [0001] The invention relates to a finishing method for edges of rice straw board furniture, that is, the furniture made by using rice straw boards as a base material is coated on the edges. It belongs to the technical field of material and product production. Background technique [0002] Rice straw board is a board made of rice straw as raw material, with isocyanate (MDI) resin as adhesive, and through complicated processes. During use, rice straw board does not release free formaldehyde. And its density is uniform, the surface is smooth, there is no obvious color difference, and the mechanical properties meet the requirements of GB / T 4897.1~4987.7-2003 "Particleboard". Industries such as furniture manufacturing, building decoration and packaging have been applied and promoted. However, due to the roughness of the edges of rice straw boards, the edge coating quality of rice straw boards has been unsatisfactory, and its paint film adhesion and impact resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27M3/18B05D5/00
CPCB05D5/00B27M3/18
Inventor 朱云刘壮青申黎明张宇鹏田阳张岱远
Owner 梅州市汇胜木制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com