A cement-based, grouting material technology, applied in the field of building materials, can solve the problems of low compressive strength, short service life, poor fluidity, etc., and achieve the effect of reducing permeability and enhancing compactness
Inactive Publication Date: 2015-06-03
建研建材有限公司
View PDF8 Cites 12 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Because the conventional cement-based reinforcement grout is not acid-resistant, the reinforced concrete structure still has the defect of short service life
[0003] The acid-resistant concrete commonly used in engineering structures is water glass, which is generally made o
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] Select 100 kg of PO42.5 Portland cement, 50 kg of Class I fly ash, 20 kg of phenylacrylic acid-resistant rubber powder, 10 kg of naphthalene-based high-efficiency water reducer, 300 kg of machine-made sand, 20 kg of UEA expansion agent, methyl 0.5 kg of cellulose ether.
[0019] Weigh each component according to the above ratio, mix in a forced mixer for 15-20 minutes, and store in dry bags. When in use, add drinking water with 12% of the mass of the mixture and stir. The performance of the grouting material is as follows:
[0020]
Embodiment 2
[0022] Select 100 kg of PO42.5 Portland cement, 35 kg of mineral powder, 25 kg of modified rubber chloroprene acid-resistant rubber powder, 5 kg of polycarboxylate superplasticizer, 260 kg of quartz sand, UEA and nitroso mixed expansion agent 15 kg, 1 kg of hydroxyethyl cellulose ether.
[0023] Weigh each component according to the above ratio, mix in a forced mixer for 15-20 minutes, and store in dry bags. When in use, add drinking water with 10% of the mass of the mixture and stir. The performance of the grouting material is as follows:
[0024]
Embodiment 3
[0026] Select 100 kg of PO42.5 Portland cement, 10 kg of silica fume, 20 kg of fly ash, 30 kg of vinyl acetate-chloroprene rubber copolymer powder, 3 kg of polycarboxylate superplasticizer, 200 kg of gravel, UEA 10 kg of expansion agent, 0.2 kg of hydroxypropyl cellulose ether.
[0027] Weigh each component according to the above ratio, mix in a forced mixer for 15-20 minutes, and store in dry bags. When in use, add drinking water with 10% of the mass of the mixture and stir. The performance of the grouting material is as follows:
[0028]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a cement-based reinforcing grouting material with strong acid resistance. The material comprises components in parts by mass as follows: 100 parts of cement, 0-50 parts of an admixture, 20-30 parts of acid-resistant rubber powder, 3-10 parts of a water reducer, 200-300 parts of aggregate, 10-20 parts of an expanding agent and 0-0.5 parts of a water retaining agent, wherein the cement is Portland cement not lower than 42.5 level, the admixture is a mixture formed by mixing silica fume, fly ash and mineral powder in any proportion, the acid-resistant rubber powder is a mixture formed by mixing cinnamic acid, modified neoprene and vinyl acetate-neoprene copolymerized latex powder, the water reducer is a naphthalene water reducer or a polycarboxylate water reducer, the aggregate is machine-made sand, quartz sand or rubble. The material has the strong acid resistance and has advantages of self-compaction, micro-expansion, high early and later strength, construction convenience and the like of the cement-based reinforcing grouting material.
Description
technical field [0001] The invention belongs to the field of building materials, and in particular relates to a preparation technology of a cement-based reinforcement grouting material with strong acid resistance. The reinforcement grouting material can be used as concrete structure reinforcement in a strong acid corrosion environment, and can also be used as acid-resistant concrete. Background technique [0002] The concrete structures of some petrochemical and chemical enterprises, such as sewage treatment tanks, beams and columns of factory buildings, pipe corridor columns, etc., are corroded by the acidic waste water and waste gas discharged from the factory, and the concrete protective layer peels off quickly, and the internal steel bars are corroded. Durability Very poor, so it is necessary to expand the cross-sectional area for reinforcement, and the commonly used reinforcement material is cement-based reinforcement grouting material. Because the conventional cement-b...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more