Preparation method for colorful polyurethane plastic and construction process for colorful polyurethane plastic track

A kind of colorful and construction technology, applied in polyurea/polyurethane coatings, roads, roads, etc., can solve the problems of weather resistance, poor color retention, single color of plastic runway, affecting construction time, etc., and achieve good development. Good color strength, good coverage, and improved athletic performance

Active Publication Date: 2015-06-17
山东世纪联合新材料科技有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The conventional plastic runway has a single color, poor weather resistance and color retention, and the service life is affected
The reaction rate of traditional construction is slow, which affects the construction time to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0038] Example 1-4: Formula (Unit: Kg)

[0039]

Example 1

Example 2

Example 3

Example 4

Polyether polyol

5

10

10

10

Acrylic

10

15

20

20

Paraffin

20

15

15

25

Antioxidant

0.05

0.05

0.05

0.05

Filler

45

35

55

40

Paint

3

4

3

2

Chain extender

3

5

3

4

UV absorber

0.05

0.05

0.05

0.05

[0040] Among them, the polyether polyol is a mixture of a polyether polyol with a molecular weight of 3000 and a functionality of three and a polyether polyol with a molecular weight of 5000 and a functionality of three in any ratio.

[0041] The antioxidant used in the examples is antioxidant 1010, which is pentaerythritol; benzophenone is used as the ultraviolet absorber of the system.

[0042] The chain extenders are diamines, and 3,3'-dichloro-4,4'-diphenylmethanediamine (MOCA) is used in the examples.

Embodiment 5

[0043] Embodiment 5: The best embodiment

[0044] A method for preparing colorful polyurethane plastic includes the following steps:

[0045] (1) Mix 10 parts of polyether polyol, 25 parts of acrylic resin, 10 parts of paraffin, 5 parts of chain extender, and 0.05 parts of anti-aging agent, stir evenly, and heat up to 90-100°C;

[0046] (2) Add 43 parts of fillers, 6.9 parts of pigments, and 0.05 parts of anti-aging agent and mix well;

[0047] (3) Turn on the colloid mill to grind the above materials, the fineness is below 400 mesh;

[0048] (4) Continue to heat up to 90-100°C, vacuum degree below 0.095Mpa, dehydration for 2-3 hours to obtain this material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and a construction process for a colorful polyurethane plastic track, and belongs to the technical field of sports facilities. The preparation method for colorful polyurethane plastic comprises the following steps: uniformly stirring 10 to 15 parts of polyether polyol, 10 to 30 parts of hydroxylated acrylic resin, 10 to 30 parts of paraffin, 2 to 4 parts of a chain extender and 0.1 to 0.5 part of an age resistor, and raising temperature to 90 to 100 DEG C; adding 30 to 50 parts of a filler, 2 to 9 parts of a pigment and 0.1 to 0.5 parts of an age resistor, and performing uniform stirring; starting a colloid grinder to grind the materials into particle sizes of smaller than 400 meshes; continuing heating, and performing dehydration for 2 to 3 hours under the conditions of temperature of 90 to 100 DEG C and vacuum degree of lower than 0.095Mpa. According to the preparation method and the construction process, with the adoption of the high-functionality polyether polyol, reaction is accelerated, the hardness of a formed film is increased, and construction time is shortened; by the hydroxylated acrylic resin, high glossiness and higher weather resistance and color retention are achieved, and the service life is prolonged.

Description

Technical field [0001] The invention relates to a manufacturing method of colorful polyurethane plastic and a construction process of colorful polyurethane plastic track, belonging to the technical field of sports facilities. Background technique [0002] Plastic track, also known as all-weather track and field sports track, is composed of polyurethane prepolymer, mixed polyether, waste tire rubber, EPDM rubber particles or PU particles, pigments, additives, and fillers. The plastic track has the characteristics of good flatness, high compressive strength, appropriate hardness and elasticity, and stable physical properties, which are conducive to athletes' speed and technique, effectively improve sports performance and reduce the rate of fall injuries. The plastic track is composed of polyurethane rubber and other materials, with a certain degree of elasticity and color, a certain degree of anti-ultraviolet ability and aging resistance. It is internationally recognized as the bes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/62C09D175/08C09D191/06C09D7/12E01C13/06
CPCC08G18/3243C08G18/4816C08G18/6245C08G18/6685C09D7/61C09D7/63C09D175/08E01C13/06C08L91/06C08K3/34C08K2003/2241C08K5/1345C08K5/07
Inventor 路玲张珍李帅
Owner 山东世纪联合新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com