Neutral de-waxing degreasing agent used for steel and copper workpieces after polishing and production method thereof

Abstract

The invention discloses a neutral de-waxing degreasing agent used for steel and copper workpieces after polishing. The neutral de-waxing degreasing agent used for steel and copper workpieces after polishing is characterized in comprising following raw materials, by mass, 8 to 12% of sodium tripolyphosphate, 0.1 to 0.2% of sodium dodecyl sulfate, 6 to 8% of sulfuric acid, 2 to 3% of a wax solvent special-purpose surfactant, 2 to 3% of an accumulated carbon removing surfactant, 2 to 3% of NP-6, 1 to 2% of penetrant JFC, and the balance water. A production method comprises following steps: a powder production stirrer is turned on, according to operating instructions of powder production stirring, weighed sodium tripolyphosphate, and sodium dodecyl sulfate are delivered into the powder production stirrer successively and slowly with stirring; after uniform mixing of an obtained solid product, weighed the wax solvent special-purpose surfactant, the accumulated carbon removing surfactant, NP-6, penetrant JFC, and water are delivered into the powder production stirrer successively and slowly until uniform mixing is realized; and an obtained product is collected and packaged.

Description

technical field

[0001] The invention relates to a cleaning agent for removing polishing paste and a production method thereof, in particular to a non-corrosive cleaning equipment capable of rapidly and thoroughly removing steel and copper workpieces with a large amount of polishing paste adherents remaining after high-speed mechanical polishing Post-neutral dewaxing degreaser and production method. Background technique

[0002] After steel and copper workpieces are polished by high-speed machinery, a large amount of polishing powder adherents will remain on the surface, which needs to be cleaned with water. However, due to the incompatibility of additives and corrosion inhibitors used in existing cleaning agents for removing polishing paste, the following problems exist:

[0003] 1. Corrosion of the stainless steel tank of cleaning equipment;

[0004] 2. The cleaning speed is slow, the temperature condition is high, and sometimes the problem of incomplete cleaning occurs...