Special quenching liquid for 50Mn steel and quenching method of 50Mn steel bearing ring
A technology for bearing rings and quenching liquid, which is applied in the quenching field of 50Mn steel special quenching liquid and 50Mn steel bearing rings, can solve the problems of uneven internal structure, complex components of quenching liquid, high cooling speed, etc. The effect of uniform shape, shortened vapor film stage, and uniform cooling rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0040] Example 1
[0041] A special quenching liquid for 50Mn steel, consisting of water glass, NaOH, sodium chloride and water, wherein the water glass (purchased from Qingdao Dongyue Paohua Soda Co., Ltd., the modulus is 2.4, the degree of Baume is 56) quality The fraction is 19.1%, the mass fraction of NaOH is 1.1%, the mass fraction of sodium chloride is 25.2%, and the balance is water.
[0042] Using the quenching liquid in the present embodiment to quench the 50Mn steel bearing ring (1m in diameter), the steps are:
[0043] (1) prepare quenching liquid, take by weighing water glass, NaOH, sodium chloride and water to prepare 50Mn steel special quenching liquid according to the above ratio;
[0044] (2) Drain the liquid in the quenching tank, rinse the quenching tank system pipeline with a cleaning agent and a water circulation cleaning agent, and after cleaning, dilute the 50Mn steel special quenching liquid prepared in step (1) by 1 times and introduce it into the quen...
Example Embodiment
[0056] Example 2
[0057] A special quenching liquid for 50Mn steel, consisting of water glass, NaOH, sodium chloride and water, wherein the water glass (purchased from Qingdao Dongyue Paohua Soda Co., Ltd., the modulus is 24, and the Baume degree is 56) quality The fraction is 18.1%, the mass fraction of NaOH is 1.3%, the mass fraction of sodium chloride is 26.3%, and the balance is water.
[0058] The 50Mn steel bearing ring (inner diameter is 1.2m) is quenched with the quenching liquid in the present embodiment, and the steps are:
[0059] (1) prepare quenching liquid, take by weighing water glass, NaOH, sodium chloride and water to prepare 50Mn steel special quenching liquid according to the above ratio;
[0060] (2) diluting the special quenching liquid for 50Mn steel prepared in step (1) by 2 times, and then introducing it into a quenching pool for standby use. The quenching pool is provided with a cooling circulation heat dissipation device, and the temperature of the ...
Example Embodiment
[0072] Example 3
[0073] A special quenching liquid for 50Mn steel, consisting of water glass, NaOH, sodium chloride and water, wherein the water glass (purchased from Qingdao Dongyue Paohua Soda Co., Ltd., the modulus is 2.4, the degree of Baume is 56) quality The fraction is 18.5%, the mass fraction of NaOH is 1.2%, the mass fraction of sodium chloride is 25.7%, and the balance is water.
[0074] Use the quenching liquid in the present embodiment to quench the 50Mn steel bearing ring (2.5m in diameter), and the steps are:
[0075] (1) prepare quenching liquid, take water glass, NaOH, sodium chloride and water according to the above proportion to prepare 50Mn steel special quenching liquid;
[0076] (2) dilute the quenching liquid for 50Mn steel prepared in step (1) by 1 times, and then introduce it into a quenching pool for standby use, and the quenching pool is provided with a cooling circulating heat dissipation device, and the temperature of the quenching liquid in the ...
PUM
Property | Measurement | Unit |
---|---|---|
Hardness | aaaaa | aaaaa |
Hardness | aaaaa | aaaaa |
Hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction