Nano-bamboo-carbon filling modified PTT toughening master batch

A nano-bamboo carbon and toughening masterbatch technology, applied in the field of PTT toughening masterbatch, can solve the problems of high notch sensitivity, low notch impact strength, and restrictions on the application of PTT, and achieve high concentration, improve mechanical properties and heat resistance The effect of performance, good practical value and application prospect

Inactive Publication Date: 2015-08-26
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when PTT is used alone, it has the defects of low notched impact strength and high notch sensitivity, which will greatly limit the application of PTT in various fields.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A PTT toughened masterbatch filled with nano-bamboo carbon, its components are proportioned by mass percentage: 22% PTT resin, 30% nano-bamboo carbon, 6% SMA, 4% barium stearate, white oil 2.5%, calcium carbonate 20%, POE 15%, methacrylic acid 0.45%, azobisisobutyronitrile 0.05%. Bamboo charcoal, the calcium carbonate is heavy calcium carbonate particles with a particle size less than 5 μm.

[0022] Preparation method: (1), put the PTT resin in a forced air circulation oven and dry at 110°C-120°C for 6-8 hours, and dry the nano-bamboo carbon and calcium carbonate at 60°C-80°C respectively 1 to 2 minutes, ready for use; (2) Weigh dry calcium carbonate according to the weight ratio and add it to a high-speed mixer with a cylinder temperature of 60°C to 80°C and a speed of not less than 3000r / min, and stir for 3 to 15 Minutes, then add methacrylic acid and azobisisobutyronitrile weighed by weight ratio by spraying process, stir for 10-45 minutes, then add POE weighed by w...

Embodiment 2

[0024] A PTT toughened masterbatch filled with nano-bamboo carbon, its components are proportioned by mass percentage: PTT resin 29%, nano-bamboo carbon 15%, SMA 5%, triphenyl phosphite 3%, TAS -2A 2.4%, calcium carbonate 25%, POE 20%, methacrylic acid 0.5%, azobisisobutyronitrile 0.1%, the nano-bamboo carbon is surface modified with nano-titanium dioxide, and the particle size is 20-80nm The nano-bamboo carbon, the calcium carbonate is heavy calcium carbonate particles with a particle size of less than 5 μm.

[0025] Preparation method: (1), put the PTT resin in a forced air circulation oven and dry at 110°C-120°C for 6-8 hours, and dry the nano-bamboo carbon and calcium carbonate at 60°C-80°C respectively 1 to 2 minutes, ready for use; (2) Weigh dry calcium carbonate according to the weight ratio and add it to a high-speed mixer with a cylinder temperature of 60°C to 80°C and a speed of not less than 3000r / min, and stir for 3 to 15 Minutes, then add methacrylic acid and azo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-bamboo-carbon filling modified PTT toughening master batch. The toughening master batch comprises the following ingredients, by weight, 15%-50% of PTT resins, 15%-40% of nano bamboo carbon, 3%-8% of compatilizers, 2%-6% of heat stabilizers, 0.5%-3% of dispersants, 15%-25% of calcium carbonate, 10%-20% of POE, 0.1%-1% of methacrylic acid and 0.01%-0.1% of initiators. The beneficial effects are that the toughening master batch has advantages of good core-shell toughening effects, high concentration, no pollution, low cost and convenient usage, and has functions of strong adsorption, sterilization, deodorization, purification, anti-ultraviolet ray and the like. When 10%-25% of the master batch is added during PTT production, modified effects of good toughening, sterilization, aging-resistance and filling are achieved, mechanical properties and heat resistance of materials are raised obviously, the cost is lowered, and therefore the nano-bamboo-carbon filling modified PTT toughening master batch has good practical values and application prospects.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PTT toughening masterbatch filled and modified with nanometer bamboo carbon. Background technique [0002] Polytrimethylene terephthalate (PTT) is a kind of poly(ethylene terephthalate) (PET) and polybutylene terephthalate obtained by polycondensation of terephthalic acid and 1,3-propanediol. Alcohol ester (PBT) is a new type of polyester polymer material, and PTT is more excellent than PET and PBT in terms of mechanical properties, weather resistance, heat aging resistance and hydrolysis resistance. Due to its excellent comprehensive properties, PTT is widely used in the fields of fibers, films, engineering plastics, etc. However, when PTT is used alone, it has the defects of low notched impact strength and high notch sensitivity, which will greatly limit the application of PTT in various fields. Nano-bamboo charcoal has a strong adsorption capacity, adjusts humidi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/02C08L35/06C08K13/06C08K9/10C08K3/26C08K9/02C08K3/04C08K5/098C08K5/526C08J3/22
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com