Ceramic brick

Abstract

The invention relates to a ceramic brick which is prepared from the following raw materials in parts by weight: 8-14 parts of fly ash, 7-12 parts of bentonite, 4-6 parts of limestone aggregate, 3.5-6.4 parts of cattle bone, 5-8 parts of castorite, 6-9 parts of sodium fluosilicate, 4-7 parts of calcite, 6-8 parts of calcined kaolin, 2.5-4.6 parts of forsterite, 5-13 parts of white wax, 4-6 parts of sodium borate, 7-9 parts of crystalline sodium carbonate, 12-16 parts of magnesium borate whisker, 4-11 parts of silicon micropowder and 16-26 parts of Portland cement. The ceramic brick has the advantages of favorable water absorptivity and favorable hardness, and can well reduce the waste of resources.

Description

technical field [0001] The invention relates to a ceramic tile. Background technique [0002] With the progress of society and the development of economy, while consuming a lot of resources, it also causes serious pollution. The pollution in the construction industry is particularly serious, and ceramic tiles are widely used to decorate and protect the walls and floors of buildings and structures. The ceramic tiles are smooth and delicate, the luster glaze is crystal clear and shiny, and the matt glaze is soft and comfortable. However, most of the ceramic tiles on the market have the disadvantages of low water absorption and brittleness. When heavy objects collide, they are prone to cracking, causing damage to the ceramic tiles, and resulting in a low service life. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the problem to be solved by the present invention is to provide a ceramic brick with good water absorption and hardness, which ca...

AI Technical Summary

Problems solved by technology

However, most of the ceramic tiles on the market have the disadvantages of low water absorption and brittleness. When hea