Preparation method of organosilicon styrene-acrylate fine emulsion

A technology of organosilicon benzene and acrylic microemulsion, which is applied in the field of preparation of organosilicon styrene acrylic microemulsion, which can solve the problems of high price, complicated process, and the preparation process of organosilicon styrene acrylic microemulsion, etc., and achieve the goal of improving compatibility Effect

Active Publication Date: 2015-09-09
ZHEJIANG UNIV
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coagulation rate of 5.5% is still relatively high in practical applications, and the preparation process of silicone styrene-acrylic microemulsion needs to be improved.
[0005] In the preparation of silicone styrene-acrylic microemulsion, commonly used silicone monomers are: (1) cyclosiloxane, such as octamethylcyclotetrasiloxane (D 4 ), vinyl cyclosiloxane (D 4vi ), which generally requires ring-opening under acid or base catalysis and then polymerized with acrylate, the process is more complicated; (2) organosiloxane monomers containing polymerization activity, such as 3-(methacryloyloxy)propyl trimethyl Oxysilane (MEMO), 3-(methacryloyloxy)propyltriethoxysilane, vinyltriisopropoxysilane, vinyltriethoxysilane, can be directly copolymerized with acrylate monomers, but The price is relatively expensive, which restricts the increase of the silicone content in the silicone styrene-acrylic microemulsion from the cost, and limits the improvement of the comprehensive performance of the silicone styrene-acrylic emulsion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] (1) Styrene, n-butyl acrylate, methyltrimethoxysilane and 3-(methacryloyloxy)propyltrimethoxysilane are used in a molar ratio of 2:1:0.92:0.08 and 2wt.% (mass The fractions are based on the total mass of the monomers, the same below) Hexadecane is added together into a single-necked flask equipped with magnetic stirring, and stirred for more than 1 hour to completely dissolve the stabilizer and become an oil phase mixture;

[0042] (2) Add 2.1wt.% sodium dodecyl sulfate (SDS) and 1.4wt.% OP-10 together with deionized water whose mass is 1.5 times the total mass of monomers into a four-necked flask equipped with magnetic stirring , stirred for more than 1 hour to become an aqueous phase mixture;

[0043] (3) The oil phase mixture is gradually added dropwise to the water phase mixture, and the hydrolysis reaction of the organic silicon and the emulsification process of the whole mixture are carried out simultaneously at 30° C., and the hydrolysis and emulsification time i...

Embodiment 2

[0048] (1) Styrene, butyl acrylate, methyltrimethoxysilane and 3-(methacryloyloxy)propyltrimethoxysilane are mixed according to the molar ratio of 2:1:0.92:0.08 and 1wt.% hexadecane With 1wt.% methyl methacrylate-n-butyl acrylate-siloxane random copolymer (Mn=4600g / mol, PDI=1.17PS:BA(mol)=2:1,3-(methacryloyl Oxygen) propyltrimethoxysilane content is 20mol%) is added together in the one-necked flask equipped with magnetic stirring, stirs more than 1 hour, makes stabilizer dissolve completely, becomes oily phase mixture;

[0049] (2) Add 2.1wt.% sodium dodecyl sulfate (SDS) and 1.4wt.% OP-10 together with deionized water whose mass is 1.2 times the total mass of monomers into a four-necked flask equipped with magnetic stirring , stirred for more than 1 hour to become an aqueous phase mixture;

[0050] (3) The oil phase mixture is gradually added dropwise to the water phase mixture, and the hydrolysis reaction of the organic silicon and the emulsification process of the whole mi...

Embodiment 3

[0055] (1) Styrene, n-butyl acrylate, methyltriethoxysilane and 3-(methacryloyloxy)propyltrimethoxysilane are mixed according to the molar ratio of 2:1:0.71:0.08 and 1wt.% ten Hexane and 1wt.% methyl methacrylate-n-butyl acrylate-siloxane random copolymer (Mn=4600g / mol, PDI=1.17, PS:BA(mol)=2:1,3-(form Acryloyloxy) propyltrimethoxysilane content is 20mol%) together into a single-necked flask equipped with a magnetic stirrer, stirred for more than 1 hour, so that the stabilizer is completely dissolved to become an oil phase mixture;

[0056] (2) Add 2.1wt.% sodium dodecyl sulfate (SDS) and 1.4wt.% OP-10 together with deionized water whose mass is 1.2 times the total mass of monomers into a four-necked flask equipped with magnetic stirring , stirred for more than 1 hour to become an aqueous phase mixture;

[0057] (3) The oil phase mixture is gradually added dropwise to the water phase mixture, and the hydrolysis reaction of the organosilicon and the emulsification process of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an organosilicon styrene-acrylate fine emulsion, which comprises the following steps: mixing styrene, an acrylate monomer, organosilicon monomers and a stabilizer, and completely dissolving by stirring to obtain an oil-phase mixture, wherein the organosilicon monomers comprise non-functional organosilicon monomers and functional organosilicon monomers, and the non-functional organosilicon monomers are at least one of methyltrimethyl(ethyl)oxysilane, propyltrimethyl(ethyl)oxysilane and phenyltrimethyl(ethyl)oxysilane; dissolving an emulsifier in water, and stirring uniformly to obtain a water-phase mixture; and adding the oil-phase mixture into the water-phase mixture, carrying out hydrolysis-emulsification reaction, carrying out ultrasonic fine emulsification, and carrying out fine emulsion polymerization reaction on the mixed solution at 60-100 DEG C under oxygen-free conditions to obtain the organosilicon styrene-acrylate emulsion. The silicon content and solid content of the organosilicon styrene-acrylate fine emulsion are higher, and the coagulation rate can be lowered to 1% below.

Description

technical field [0001] The invention relates to the technical field of emulsion preparation, in particular to a method for preparing an organosilicon styrene-acrylic miniemulsion. Background technique [0002] Styrene-acrylic emulsion (styrene-acrylate emulsion) is a system that has been studied more in emulsion polymerization, and it is also one of the top ten non-crosslinked emulsions with important industrial application value in the world today. As an important intermediate chemical product, styrene-acrylic emulsion has a very wide range of uses. It is mainly used as architectural coatings, metal surface latex coatings, floor coatings, paper adhesives, adhesives, plastic processing additives, etc. Although styrene-acrylic emulsion is cheap, its weather resistance is average, and its outdoor application is still limited. [0003] Silicone-modified styrene-acrylic emulsion is referred to as silicone-styrene-acrylic emulsion. Silicone has excellent properties such as anti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F212/08C08F220/18C08F230/08C08F220/28C08F2/26C08F2/30
Inventor 范宏张先伟王颖欣李伯耿
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products