Water-based epoxy paint and preparation method thereof

A water-based epoxy coating, water-based technology, applied in the field of coatings, can solve problems such as lack of coatings

Inactive Publication Date: 2015-09-16
JIANGSU UNIV OF TECH
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the technical defects of the prior art, and provides a water-based epoxy coating and its preparation method, so as to solve the technical problem in the prior art of lacking a coating which is specially used for iron buildings and plays a protective role

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068]A water-based epoxy coating, which is composed of two components A and B in a ratio of 1:4 (w / w), wherein component A is composed of the following components by mass: 8 parts of amino resin, 1 part of leveling agent , 15 parts of distilled water; component B includes the following components by mass: 15 parts of water-dispersible epoxy acrylic resin, 1 part of dispersant, 0.8 part of defoamer, 25 parts of distilled water, 10 parts of iron black, 10 parts of superfine talcum powder 5 parts of precipitated barium sulfate, 5 parts of zinc phosphate, 2 parts of antirust agent, nano-MoS 2 10 parts of anti-wear agent; nano-CaCO 3 10 parts of ultraviolet absorber.

[0069] The preparation method of above-mentioned waterborne epoxy paint, comprises the following steps:

[0070] 1) Nano-CaCO 3 UV absorber preparation: CaCl 2 and Na 2 CO 3 They were respectively prepared into solutions with a concentration of 0.4mol / L. Take 200mL CaCl 2 Add the solution into a beaker, then...

Embodiment 2

[0081] A water-based epoxy coating, which is composed of two components A and B in a ratio of 1:4 (w / w), wherein component A is composed of the following components by mass: 8 parts of amino resin, 1 part of leveling agent , 15 parts of distilled water; component B includes the following components by mass: 20 parts of water-dispersible epoxy acrylic resin, 1 part of dispersant, 0.8 part of defoamer, 25 parts of distilled water, 10 parts of iron black, 10 parts of superfine talcum powder 8 parts of precipitated barium sulfate, 8 parts of zinc phosphate, 2 parts of antirust agent, nano-MoS 2 18 parts of anti-wear agent, nano CaCO 3 18 parts of ultraviolet absorber.

[0082] The preparation method of above-mentioned waterborne epoxy paint, comprises the following steps:

[0083] 1) Nano-CaCO 3 UV absorber preparation: CaCl 2 and Na 2 CO 3 They were respectively prepared into solutions with a concentration of 0.4mol / L. Take 200mL CaCl 2 Add the solution into a beaker, the...

Embodiment 3

[0094] A water-based epoxy coating, which is composed of two components A and B in a ratio of 1:4 (w / w), wherein component A is composed of the following components by mass: 8 parts of amino resin, 1 part of leveling agent , 15 parts of distilled water; component B includes the following components by mass: 25 parts of water-based epoxy acrylic resin, 1 part of dispersant, 0.8 part of defoamer, 25 parts of distilled water, 10 parts of iron black, 10 parts of superfine talcum powder, 10 parts of precipitated barium sulfate, 10 parts of zinc phosphate, 2 parts of antirust agent, nano-MoS 2 20 parts of anti-wear agent, nano-CaCO 3 20 parts of ultraviolet absorber.

[0095] The preparation method of above-mentioned waterborne epoxy paint, comprises the following steps:

[0096] 1) Nano-MoS 2 Preparation of anti-wear agent: 1) Dissolve an appropriate amount of sulfur (S) powder in CS 2 and CCL 4 In the mixed solution, after the S is completely dissolved, the spherical MoO prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a water-based epoxy paint and a preparation method thereof. The paint comprises an amino resin, a leveling agent, distilled water, a water-based epoxy acrylic resin, a dispersing agent, a defoaming agent, iron oxide black, superfine talcum powder, precipitated baryte, zinc phosphate, a rust inhibitor and the like; and a nano MoS2 anti-wear agent and a nano CaCO3 ultraviolet absorbent are further added to enhance the properties. By reasonably designing the component types and contents, the thickness of the paint film can reach 100 mu m above, the water resistance is greater than 240 hours, the transmittivity for ultraviolet light with the wavelength of 290-400nm is less than 0.4, the wear-resistant revolution number is up to 1000-1400, the mass loss of the paint film is less than 0.07 g/100r, and the salt spray resistance is greater than 200 hours. The paint can be brushed on the internal and external walls of an iron building, has excellent protective effect, and is especially suitable for protecting iron building cultural relics.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based epoxy coating and a preparation method thereof. Background technique [0002] Coatings refer to materials that are coated on the surface of objects, can bond with the substrate and form a complete and tough protective film. Since its inception, coatings have been widely used in the field of architectural technology, and their functions can be summarized into three aspects, namely, the protection of buildings, decoration and other specific functions. In the prior art, in order to protect buildings, coatings should be designed according to the use environment, building type, and substrate characteristics. For example, in order to improve the fire performance of wooden buildings, the relevant coatings should have certain flame retardant properties. [0003] Iron buildings represented by iron towers have been in the outdoor environment for a long time. With the erosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D161/20C09D5/08C09D7/12
Inventor 王泽董观秀徐修玲卢雅琳谈衡叶霞李仁兴
Owner JIANGSU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap