Resistance furnace and brazing method for brazing zinc electrolytic anode conductive beam

A technology of conductive beams and zinc electrolysis, which is applied in the direction of welding/welding/cutting items, electric heating devices, welding equipment, etc., can solve the problems of operators' occupational health and working environment hazards, the increase of tank voltage, and the influence of current efficiency, etc., to achieve Improve occupational health and working environment, reduce direct current unit consumption, and reduce ineffective power consumption

Active Publication Date: 2017-01-04
NORTHWEST RES INST OF MINING & METALLURGY INST
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technology has the following defects: 1) due to the inability to form a metallurgical bond between copper and lead
3) Due to the existence of a large area of ​​gaps on the copper / lead joint surface, an oxide layer is easily formed under the action of an acidic gas phase medium, which further increases the contact resistance, increases the cell voltage, and affects the current efficiency
4) During the casting process, due to the overheating of molten metal, a large amount of lead vapor is produced, which is harmful to the occupational health of operators and the working environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resistance furnace and brazing method for brazing zinc electrolytic anode conductive beam
  • Resistance furnace and brazing method for brazing zinc electrolytic anode conductive beam

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.

[0021] like figure 1 and figure 2 As shown, the resistance furnace of the present invention includes a U-shaped base 9 arranged horizontally, a U-shaped furnace bottom 8 is horizontally arranged on the base 9, a track 11 is installed on the bottom surface of the base 9, and one end of the track 11 is located in the base 9. The other end of the track 11 extends out of the base 9; the track 11 is provided with a traveling furnace car 10 that can reciprocate along the track 11; a U-shaped shell is horizontally arranged on the furnace bottom 8, and the open end of the shell faces the track 11 protrudes from one end of the base 9, and is equipped with a front furnace door 16. Inside the casing, along the direction from the inner wall of the casing to the middle of the casing, a first side wall 4, an insulating layer 5 and a second side wall 6 are ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a resistance furnace for brazing a zinc electrolysis anode electric conducting cross beam and a brazing method. The resistance furnace comprises a U-shaped base horizontally arranged, wherein the base has a furnace bottom; a rail is arranged on the bottom surface of the base, and is provided with an advancing furnace car capable of performing a reciprocating motion; a furnace body is arranged on the furnace bottom; a cavity is formed in the furnace body; electric furnace wires are arranged on the side wall of the cavity; a front furnace gate is formed in the side wall of the furnace body; the advancing furnace car is pushed into the base in use; and the working surface of the advancing furnace car and the cavity of the furnace body are formed to an empty cavity. A copper plate and lead plates with two specifications are prepared; one lead plate, the copper plate and the other one lead plate are laminated on the working surface of the advancing furnace car in sequence; brazing filler metals are laid in gaps among the plates; a pressure plate is covered; the advancing furnace car enters the base; after the segmented temperature rise and insulation is performed, the plates are discharged from the furnace for air cooling; the lead plates are welded; and the copper plate is sealed in the lead plates. The brazing method applies a brazing technology to weld heterogeneous metals, and solves the surface-surface metallurgic bonding problem of copper / lead heterogeneous metals.

Description

technical field [0001] The invention belongs to the field of welding technology, and relates to a brazing method for compounding copper and lead heterogeneous metals, in particular to a resistance furnace for brazing a conductive beam of a zinc electrolytic anode; the invention also relates to a brazing method using the resistance furnace Method for welding conductive beams of zinc electrolytic anodes. Background technique [0002] At present, the manufacturing method of the zinc electrolytic anode conductive crossbeam is copper and lead bimetallic casting. This technology has the following defects: 1) Due to the inability to form a metallurgical bond between copper and lead. Therefore, first tin-plate the copper surface and then inject metal lead liquid into the mold embedded with copper bars to realize the joint of copper and lead. Due to the poor bonding force and easy cracking of the copper / aluminum metal interface formed by tin, the contact resistance increases. 2) W...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K3/053B23K3/08B23K1/008B23K1/20
CPCB23K1/008B23K1/206B23K3/053B23K3/08B23K2103/12
Inventor 宋宝兴马进宋衎蒲敬文
Owner NORTHWEST RES INST OF MINING & METALLURGY INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com