A kind of pre-dispersed masterbatch carrier and the predispersed masterbatch used therein and its preparation method and application

A pre-dispersed masterbatch and carrier technology, applied in the field of rubber additives, can solve problems such as unsuitable mixing temperature, negative impact, high performance of powder or liquid additives, etc., achieve excellent dispersion and distribution effects, and facilitate transportation Effect
CN104927274BActive Publication Date: 2017-08-11RACHEM CHINA CO LTD +1
5 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN ยท China
Patent Type
Patents(China)
Current Assignee / Owner
RACHEM CHINA CO LTD
Publication Date
2017-08-11

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a pre-dispersed masterbatch particle carrier. The pre-dispersed masterbatch particle carrier comprises the following raw materials in parts by mass: 5-90 parts of rubber, 1-10 parts of stearic acid, 1-10 parts of pentaerythritol aliphatic ester, 2-10 parts of an ethylene vinyl acetate copolymer EVA and / or EVM and 0.1-10 parts of a polar plasticizer. The components are cooperatively used to form a heat softening carrier system with high compatibility and can be mixed with liquid active components, powdery active components and granular active components at the temperature of not more than 55 DEG C, and the active components can achieve excellent dispersion and distribution effects. The problems of sublimation, volatilization, reaction and failure of the active components caused by over-high pre-dispersion mixing temperature are avoided; the active components are uniformly dispersed in masterbatch particles in the absence of aggregates, so that the active components can be uniformly dispersed in a rubber system in the production process of followed rubber products to form high-performance rubber products.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a rubber additive, in particular to a pre-dispersed master rubber particle carrier, a pre-dispersed master rubber particle prepared by using the carrier, and applications of the carrier and the master rubber particle. Background technique

[0002] Various additives are needed in the production process of rubber products, such as rubber vulcanizing agent, rubber peroxide crosslinking agent, rubber peroxide crosslinking aid, rubber accelerator, rubber anti-aging agent, rubber filler and reinforcing agent, Rubber plasticizer or softener, phenolic resin, hydrocarbon resin, rubber adhesion promoter, rubber foaming agent, rubber pigment, rubber colorant, etc. In the traditional industry, the above-mentioned various additives are generally in the form of powder or liquid. When the powder is added to the rubber mixing system, it is easy to cause the powder of the additive to fly, causing dust pollution to the environment, and it is not...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine