Stable-temperature magnesium-titanate-base microwave dielectric ceramic and preparation method thereof

A microwave dielectric ceramic and temperature-stable technology, which is applied in the field of temperature-stabilized magnesium titanate-based microwave dielectric ceramics and their preparation, can solve the problems of high sintering temperature, large energy consumption in the preparation process, non-compliance with low-carbon environmental protection and the like, and achieves the Reduced sintering temperature, superior microwave dielectric properties, and energy cost savings

Inactive Publication Date: 2015-09-30
TIANJIN UNIV
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, MgTiO 3 Ceramics have a high sintering temperature, and the preparation process consumes a lot of energy, which does not meet the concept of low-carbon environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stable-temperature magnesium-titanate-base microwave dielectric ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention uses MgO and TiO with a purity greater than 99% 2 , CaCO 3 、Na 2 CO 3 and Sm with a purity greater than 99.9% 2 o 3 As the starting material, microwave dielectric ceramics were prepared by a simple solid-state method. The specific implementation plan is as follows:

[0023] (1) The chemical raw materials MgO, TiO 2 According to the stoichiometric formula MgTiO 3 For batching, the ratio of raw materials is: 3.35302g MgO, 6.64698g TiO 2 . Put 10g of mixed powder into a polyester tank, add 200ml of deionized water, add 150g of zirconium balls, and ball mill on a planetary ball mill for 12 hours at a speed of 400 rpm;

[0024] (2) Put the ball-milled raw materials in step (1) into a drying oven, dry them at 100-120° C., and pass through a 40-mesh sieve;

[0025] (3) Put the powder sieved in step (2) into a medium-temperature furnace, pre-fire at 1100°C, and keep warm for 4 hours;

[0026] (4) the chemical raw material TiO 2 , CaCO 3 、Sm 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stable-temperature magnesium-titanate-base microwave dielectric ceramic and a preparation method thereof. The expression formula is 0.89MgTiO3-0.11(Ca0.4Na0.3Sm0.3)TiO3. The preparation method comprises the following steps: proportioning MgO and TiO2 according to the stoichiometric formula MgTiO3, carrying out ball milling, drying, screening, and presintering at 800-1000 DEG C; proportioning TiO2, CaCO3, Sm2O3 and Na2CO3 according to the stoichiometric formula (Ca0.4Na0.3Sm0.3)TiO3, carrying out ball milling, drying, screening and presintering at 1000-1300 DEG C; mixing the two presintered powders in a mole ratio of 89:11, carrying out ball milling, drying, screening, granulating and pressing to obtain a green compact; and sintering the green compact at 1200-1300 DEG C to prepare the magnesium-titanate-base stable-temperature microwave dielectric ceramic. The Qf value reaches 55000-72000GHz, and the temperature coefficient of resonance frequency (tau<f>) reaches -7.6 to -2.3*10<-6> / DEG C. The ceramic system has the advantages of simple preparation technique and excellent microwave dielectric properties, saves the energy cost, conforms to the concepts of low carbon and environment friendliness, and has wide application prospects.

Description

technical field [0001] The invention relates to a ceramic composition characterized by components, in particular to a temperature-stable magnesium titanate-based microwave dielectric ceramic and a preparation method thereof. Background technique [0002] With the continuous development of modern communication technology, the requirements for miniaturization, integration and modularization of components are increasingly urgent, and higher requirements are put forward for microwave dielectric materials. Microwave dielectric ceramics have become one of the most active research fields of functional ceramics in recent years. one. Among them, MgTiO 3 As a traditional microwave dielectric material, ceramics still have excellent microwave dielectric properties such as low dielectric constant and ultra-high quality factor in the millimeter wave band, but they have poor temperature stability (τ f ~-50ppm / ℃), the disadvantage of high sintering temperature (>1400℃). [0003] Micro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/465C04B35/622C04B35/64
Inventor 李玲霞李赛吕笑松孙浩叶静
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap