Exterior wall waterproof material

A technology for waterproof materials and exterior walls, which is applied in the field of building materials to achieve the effects of excellent waterproof and impermeability, enhanced reliability, and improved reliability and safety.

Active Publication Date: 2015-10-07
郑州赛诺建材有限公司
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the technical problems in the prior art that waterproof materials are likely to cause building leakage, etc., and to provide a waterproof material for exterior walls. Even if it is damaged, it will not leak or channel water, which greatly improves the reliability and safety of waterproof construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: An exterior wall waterproof material, which includes liquid material and powder material, wherein the liquid material is vinyl acetate-ethylene copolymer emulsion, and the dosage is: 400 kg. The powder materials are: Portland cement, quartz sand, plasticizer and penetrant, of which: Portland cement 400 kg, quartz sand 550 kg, fineness 200 mesh, plasticizer 25 kg, penetrant 25 kg . Wherein the plasticizer is: sodium sulfate. The penetrant is made of sodium nitrate, sodium carbonate, sodium sulfate, potassium oxide, calcium carbide and limestone in the following weight ratio: 1:1:1:2:2:2. The specific operation is: first pour 400 kg of emulsion into the bucket, use an electric mixer, and slowly add the powder material while stirring. Do not add the powder material at one time, so as to avoid the material at the bottom of the bucket from being mixed thoroughly. Thick, sticky, no agglomeration is the degree. If the paint is too thick when stirring, you can ...

Embodiment 2

[0017] Embodiment 2: An exterior wall waterproof material, which includes liquid material and powder material, wherein the liquid material is vinyl acetate-ethylene copolymer emulsion, and the dosage is: 555 kg. The powder materials are: Portland cement, quartz sand, plasticizer and penetrant, of which: 450 kg of Portland cement, 600 kg of quartz sand, fineness of 200 mesh, 30 kg of plasticizer, and 30 kg of penetrant . Among them, Portland cement is used as the cementitious material, and the plasticizer is sodium sulfate. The penetrant is made of sodium nitrate, sodium carbonate, sodium sulfate, potassium oxide, calcium carbide and limestone in the following weight ratio: 1:1:1:1:1:1.5. The specific operation is: first pour 555 kg of emulsion into the bucket, use an electric mixer, and slowly add the powder material while stirring. Do not add the powder material at one time, so as to avoid the material at the bottom of the bucket from being mixed thoroughly. Thick, sticky, ...

Embodiment 3

[0018] Embodiment 3: An exterior wall waterproof material, which includes liquid material and powder material, wherein the liquid material is vinyl acetate-ethylene copolymer emulsion, and the dosage is: 560 kg. The powder materials are: Portland cement, quartz sand, plasticizer and penetrant, of which: 680 kg of Portland cement, 920 kg of quartz sand, fineness of 250 mesh, 40 kg of plasticizer, and 40 kg of penetrant . The penetrant is made of sodium nitrate, sodium carbonate, sodium sulfate, potassium oxide, calcium carbide and limestone in the following weight ratio: 1:1:1:2:3:2.5. The specific operation is: first pour 560 kg of emulsion into the bucket, use an electric mixer, and slowly add the powder material while stirring. Do not add the powder material at one time, so as to avoid the material at the bottom of the bucket from being mixed thoroughly. Thick, sticky, no agglomeration is the degree. If the paint is too thick when stirring, you can add an appropriate amoun...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impermeabilityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an exterior wall waterproof material, comprising liquid material and powder material. The weight ratio of the liquid material to the powder material is 1:(2-4); the liquid material is vinyl acetate-ethylene copolymer emulsion; the powder material is made with Portland cement, quartz sand, plasticizer and penetrant according to the weight ratio: (15-18):(20-24):1:1. The exterior wall waterproof material is both rigid and flexible and has the advantages of both the rigid material and the flexible material; added with various unique material compositions and active factors, the exterior wall waterproof material is excellent in waterproofing and impervious performances, is resistant to high and low temperatures, ageing resistant, high in weatherability, nontoxic and odorless and green, allows double waterproofing by single construction, is resistant to long-term soaking, and has certain anticorrosion effect; during construction, the exterior wall waterproof material is rarely destructed, water leakage rarely occurs even if a waterproof layer is destructed, water channeling or water leakage never occurs even if a base layer is severely damaged, a leak point is easy to locate, and local repairing is required only.

Description

technical field [0001] The invention relates to a building material, in particular to an exterior wall waterproof material. Background technique [0002] In the past 10 years, China has entered a period of rapid growth in construction. Construction sites are everywhere in the country. However, due to various reasons, construction leakage occurs frequently. According to CCTV information, the national leakage rate is as high as 80%. At the beginning of the project, various manufacturers, including large and small waterproof manufacturers, talked about how good their materials were, but in the later stages of the project site, serious leakage occurred, resulting in frequent occurrences of buck-passing and lawsuits in the later stages. At present, the most widely used waterproof materials in China's domestic projects are various coiled materials and polypropylene fiber. The leakage is very serious. There are many reasons for the leakage, such as the settlement of the sit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B41/50C04B14/06C04B24/26C04B22/14C04B22/06C04B103/65
Inventor 王福州蔡家润
Owner 郑州赛诺建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap