High-tenacity transparent PS plastic cement material and preparation method therefor

A plastic material and high toughness technology, applied in the field of plastic materials, can solve problems such as brittleness, stress cracking, and low impact strength, and achieve the effects of high toughness, excellent chemical resistance, and high impact strength

Inactive Publication Date: 2015-10-21
JIN BAOLI TECH SUZHOU
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PS has a wide range of application space, but it has obvious disadvantages, namely, brittleness, low impact strength, and due to the rigidity of the molecular chain, it is easy to cause stress cracking, which limits its application field to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: A kind of high-toughness transparent PS plastic material, it is made up of the raw material of following weight ratio:

[0024] Polystyrene (PS) 78 parts,

[0025] Polyethersulfone resin (PES) 6 parts,

[0026] 9 parts of polyvinylidene fluoride (PVF),

[0027] 7 parts of composite modifier;

[0028] The composite modifier is a compound of an impact modifier and a toughening agent, and its weight percent of the composite modifier is: 40% of the impact modifier and 60% of the toughening agent; wherein, the impact modifier The modifier is a mixture of acrylate (AIM) and methyl methacrylate-butadiene-styrene copolymer (MBS), which accounts for 70% of AIM and 30% of MBS by weight of the impact modifier; The toughening agent is a mixture of K-resin, thermoplastic elastic POE, polyol ester and ethylene-vinyl acetate copolymer (EVA), and its weight percent of the toughening agent is: K-resin 40%, thermoplastic elastic POE 40% , polyol ester 4%, ethylene-vinyl...

Embodiment 2

[0037] Embodiment 2: a kind of high-toughness transparent PS plastic material, it is made up of the raw material of following weight ratio:

[0038] Polystyrene (PS) 75 parts,

[0039] Polyethersulfone resin (PES) 6 parts,

[0040] 9 parts of polyvinylidene fluoride (PVF),

[0041] 10 parts of composite modifier;

[0042] The composite modifier is a compound of an impact modifier and a toughening agent, and its weight percent of the composite modifier is: 30% of the impact modifier and 70% of the toughening agent; wherein, the impact modifier The modifier is a mixture of acrylate (AIM) and methyl methacrylate-butadiene-styrene copolymer (MBS), which accounts for 80% of AIM and 20% of MBS by weight of the impact modifier; The toughening agent is a mixture of K-resin, thermoplastic elastic POE, polyol ester and ethylene-vinyl acetate copolymer (EVA), and its weight percent of the toughening agent is: K-resin 30%, thermoplastic elastic POE 45%, Polyol ester 5%, ethylene-vinyl...

Embodiment 3

[0045] Embodiment 3: a kind of high tenacity transparent PS plastic material, it is made up of the raw material of following weight ratio:

[0046] Polystyrene (PS) 85 parts,

[0047] Polyethersulfone resin (PES) 5 parts,

[0048] 7 parts of polyvinylidene fluoride (PVF),

[0049] Composite modifier 3 parts;

[0050] The composite modifier is a compound of an impact modifier and a toughening agent, and its weight percent of the composite modifier is: 50% of the impact modifier and 50% of the toughening agent; wherein, the impact modifier The modifier is a mixture of acrylate (AIM) and methyl methacrylate-butadiene-styrene copolymer (MBS), which accounts for 65% of AIM and 35% of MBS by weight of the impact modifier; The toughening agent is a mixture of K-resin, thermoplastic elastic POE, polyol ester and ethylene-vinyl acetate copolymer (EVA), and its weight percent of the toughening agent is: K-resin 50%, thermoplastic elastic POE 30% , polyol ester 5%, ethylene-vinyl ace...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-tenacity transparent PS plastic cement material. The high-tenacity transparent PS plastic cement material consists of the following raw materials in parts by weight: 70-85 parts of polystyrene (PS), 5-8 parts of polyether sulfone resin (PES), 7-12 parts of polyvinylidene fluoride (PVF) and 3-10 parts of a composite modifier. The invention further discloses a preparation method of the high-tenacity transparent PS plastic cement material. According to the preparation method disclosed by the invention, the PES, the PVF and the PS are blended so as to obtain the plastic cement material, a shock resistant modifier and a flexibilizer in the composite modifier are used for composite modification for the plastic cement material, so that the rigidity and the tenacity of PS products are effectively balanced, and the PS plastic cement material with high tenacity, high impact strength and favorable transparency is obtained.

Description

technical field [0001] The invention relates to the field of plastic materials, in particular to a high-toughness transparent PS plastic material and a preparation method thereof. Background technique [0002] Plastic materials are made of high molecular synthetic resin / polymer as the main component, supplemented by various auxiliary materials or additives, have plasticity and fluidity under specific temperature and pressure, can be molded into a certain shape, and maintain under certain conditions The shape-changing material has excellent electrical insulation, arc resistance, heat preservation, sound insulation, vibration absorption, and noise reduction performance. Plastic materials are widely used in various fields of life today, such as household appliances, communication electronics, wires and cables, instruments and meters, construction equipment, automobile industry, aerospace, etc. At present, most plastic materials are opaque materials. [0003] Polystyrene (PS) ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/06C08L81/06C08L27/16C08L51/04C08L23/08C08K5/103
Inventor 李明华
Owner JIN BAOLI TECH SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com