Continuous environment-friendly preparation process of methyl phenyl silicone resin for high-temperature-resistant paint

A technology of methyl phenyl silicon and high temperature resistant coating, applied in the direction of coating, etc., can solve the problems of high production energy consumption, poor mass transfer and heat transfer effect, low production efficiency, etc.

Active Publication Date: 2015-12-02
TANGSHAN SANYOU SILICON IND
View PDF9 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The harm of silicone resin waste water is mentioned in CN101602559B, and the treatment method mentioned in it is comparatively complicated, and it is difficult to realize industrialization
CN103694477A uses alkoxysilane as a raw material to prepare methylphenyl silicone resin, which uses membrane separation and rectification to separate acid medium oil, dilute acid and alcohol, which requires large equipment investment and high en

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous environment-friendly preparation process of methyl phenyl silicone resin for high-temperature-resistant paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A continuous environment-friendly preparation process of methylphenyl silicone resin for high-temperature-resistant coatings is carried out as follows:

[0034] Feed according to the following raw material ratio:

[0035] Phenyltrichlorosilane: 42kg / h; Diphenyldichlorosilane: 8kg / h

[0036] Methyltrichlorosilane: 10kg / h; Dimethyldichlorosilane: 17kg / h

[0037] Xylene: 160kg / h; dilute acid water: 240kg / h

[0038] a. Hydrolysis

[0039] The chlorosilane monomer and xylene are fed into the static mixer according to the above ratio, and after preliminary mixing in the static mixer 11, enter the tubular hydrolysis reactor 12 to react with dilute acid water. The dilute acid water is dilute hydrochloric acid with a mass concentration of 0.9% (the washing water after the first level of water washing in the washing process of the material in the previous kettle can also be used). The hydrolysis temperature is controlled by the hydrolysis cooler 15 to be 30° C., and the react...

Embodiment 2

[0053] A continuous environment-friendly preparation process of methylphenyl silicone resin for high-temperature-resistant coatings is carried out as follows:

[0054] Feed according to the following raw material ratio:

[0055] Phenyltrichlorosilane: 50kg / h; Diphenyldichlorosilane: 6kg / h

[0056] Methyltrichlorosilane: 4kg / h; Dimethyldichlorosilane: 17kg / h

[0057] Xylene: 160kg / h; dilute acid water: 320kg / h

[0058] a. Hydrolysis

[0059] The raw materials are fed into the static mixer according to the above-mentioned ratio, and after preliminary mixing in the static mixer 11, they enter the tubular hydrolysis reactor 12 to react with dilute acid water. The dilute acid water is dilute hydrochloric acid with a mass concentration of 0.8% (the washing water after the primary water washing in the washing process of the last kettle material can also be used). The hydrolysis temperature is controlled by the hydrolysis cooler 15 to be 20° C., and the reaction gauge pressure in ...

Embodiment 3

[0073] A continuous environment-friendly preparation process of methylphenyl silicone resin for high-temperature-resistant coatings is carried out as follows:

[0074] Feed according to the following raw material ratio:

[0075] Phenyltrichlorosilane: 57kg / h; Diphenyldichlorosilane: 6kg / h

[0076] Methyltrichlorosilane: 4kg / h; Dimethyldichlorosilane: 20kg / h

[0077] Xylene: 160kg / h; dilute acid water: 240kg / h

[0078] a. Hydrolysis

[0079] The raw materials are fed into the static mixer according to the above-mentioned ratio, and after preliminary mixing in the static mixer 11, they enter the tubular hydrolysis reactor 12 to react with dilute acid water. Dilute acid water is dilute hydrochloric acid with a mass concentration of 0.5% (the washing water after the first level of water washing in the process of washing the materials in the previous kettle can also be used). The hydrolysis temperature is controlled by the hydrolysis cooler 15 to be 40° C., and the reaction gau...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a continuous environment-friendly preparation process of methyl phenyl silicone resin for high-temperature-resistant paint. The technical scheme includes: mixing according to a mass ratio of 1-20:1-10:1-10:1-20, and entering a tubular hydrolyzer to react with diluted acid water, wherein mass of benzene solvent is 1-3 times that of mixed chlorosilane monomer, and mass of the diluted acid water is 2-5 times that of the mixed chlorosilane monomer; stepwise washing hydrolysate at three or more stages to be neutral; continuously concentrating in vacuum, and allowing polycondensation when materials in a concentration polycondensation kettle reach 50-60% of volume of the kettle; after polycondensation is completed, detecting, filtering, packaging and recycling the solvent. The process has the advantages that no wastewater is discharged, the problem that conventional processes are large in discharging quantity, high in organic matter content and difficult in wastewater treatment is solved, product yield is increased, and devolatiligation time is reduced by feeding inert gas in the process of polycondensation.

Description

technical field [0001] The invention relates to a method for synthesizing methylphenyl silicone resin, in particular to a continuous and environment-friendly preparation process of methylphenyl silicone resin for high-temperature-resistant coatings. Background technique [0002] Because silicone resin has the characteristics of heat resistance, cold resistance, moisture resistance and weather resistance, it plays an important role in the special coating industry. There are many varieties of silicone coatings, which can be roughly divided into heat-resistant and weather-resistant anti-corrosion coatings, scratch-resistant transparent coatings, mold release and moisture-proof coatings, and radiation-resistant coatings. Methylphenyl silicone resin for high-temperature-resistant coatings can be used for a long time above 200 ° C, the color and gloss of the coating film change little, and the coating film is complete without cracking. Silicone coatings can be used at temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G77/06C09D183/04
Inventor 孙长江任海涛周健闫超刘秋艳王春英李献起曹鹤
Owner TANGSHAN SANYOU SILICON IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap