A kind of polyoxymethylene composite material that can be painted on the surface and its preparation method

A technology of composite materials and polyoxymethylene, applied in the field of polyoxymethylene, can solve the problems of increasing the cost of products produced by enterprises, changing the performance of POM matrix, increasing the production process of products, etc., so as to improve the mechanical properties, improve the paintable performance, and facilitate industrial production. Effect

Active Publication Date: 2017-12-08
重庆云天化天聚新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Japan has adopted the method of pre-coating paint, pre-coating a layer of 10-15 μm film on the surface of POM with a special pre-coating paint, and treating it at a temperature of 135°C for 30 minutes, but this excessive heat treatment temperature will cause Causes deformation of POM products
In summary, it can be seen that although the above-mentioned polymer surface treatment methods can improve the paintability of the polymer surface, these methods will change the performance of the POM matrix, cause changes in the size of the product, and increase the production process of the product and improve the quality of the product. It reduces the cost of the enterprise's production of products, and has certain shortcomings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyoxymethylene composite material that can be painted on the surface and its preparation method
  • A kind of polyoxymethylene composite material that can be painted on the surface and its preparation method
  • A kind of polyoxymethylene composite material that can be painted on the surface and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] One, a polyoxymethylene composite material that can be painted on the surface, comprising the following components by weight: 82 parts of polyoxymethylene POM, 12 parts of thermoplastic phenolic resin, 1 part of polyurethane thermoplastic elastomer TPU, 5 parts of silicon dioxide and 0.5 part of anti- Oxidizing agent 1010. The melt index of the polyoxymethylene POM is 9 g / 10 min, and the tensile strength is 58 Mpa.

[0023] Two, the preparation method of the polyoxymethylene composite material that can be painted on the above-mentioned surface, comprises the steps:

[0024] 1) Weigh the above components by weight and mix them in a high mixer for 7 minutes, then send the uniformly mixed materials into a twin-screw extruder for extrusion and granulation; wherein, the twin-screw extruder starts from The temperature of each section between the feed port and the extrusion port is: the first zone 110°C, the second zone 170°C, the third zone 200°C, the fourth zone 220°C, the ...

Embodiment 2

[0028] 1. A polyoxymethylene composite material that can be painted on the surface, comprising the following components by weight: 75 parts of polyoxymethylene POM, 15 parts of thermoplastic phenolic resin, 10 parts of polyvinyl alcohol PVA, 10 parts of calcium carbonate and 0.5 part of antioxidant 1010. The melt index of the polyoxymethylene POM is 8 g / 10 min, and the tensile strength is 60 Mpa.

[0029] Two, the preparation method of the polyoxymethylene composite material that can be painted on the above-mentioned surface, comprises the steps:

[0030] 1) Weigh the above components by weight and mix them in a high mixer for 7 minutes, then send the uniformly mixed materials into a twin-screw extruder for extrusion and granulation; wherein, the twin-screw extruder starts from The temperature of each section between the feed port and the extrusion port is: the first zone 115°C, the second zone 160°C, the third zone 190°C, the fourth zone 210°C, the fifth zone 220°C, the sixth...

Embodiment 3

[0034] One, a polyoxymethylene composite material that can be painted on the surface, comprising the composition of following parts by weight: 75 parts of polyoxymethylene POM, 15 parts of thermoplastic phenolic resin, 8 parts of polyvinyl alcohol PVA, 4 parts of polyolefin type thermoplastic elastomer TPE, 4 parts 1 part silicone rubber, 4 parts quartz sand and 0.5 part antioxidant 1010. The melt index of the polyoxymethylene POM is 10 g / 10 min, and the tensile strength is 62Mpa.

[0035] Two, the preparation method of the polyoxymethylene composite material that can be painted on the above-mentioned surface, comprises the steps:

[0036] 1) Weigh the above components by weight and mix them in a high mixer for 7 minutes, then send the uniformly mixed materials into a twin-screw extruder for extrusion and granulation; wherein, the twin-screw extruder starts from The temperature of each section between the feed port and the extrusion port is: the first zone 120°C, the second z...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
tensile strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyformaldehyde composite with the surface capable of being finished and a preparation method thereof. The polyformaldehyde composite is prepared from polyformaldehyde (POM), macromolecular surface modifiers, filler and antioxidants. The preparation method comprises the steps that all the components are weighed and put in a high mixing machine, and mixing is performed for 5-10 min; the evenly mixed materials are fed into a double-screw extruder for extrusion granulating, and then the extruded and granulated materials are dried at 50-120 DEG C for 3-4 h; injection forming is performed on the dried materials, and the polyformaldehyde composite with the surface capable of being finished is obtained. According to the prepared polyformaldehyde composite, the adhesive force between the polyformaldehyde and acrylic acid paint reaches 0 level while the excellent mechanical property of polyformaldehyde base materials is retained, and therefore the finishing property of the polyformaldehyde composite is significantly improved; compared with the other methods, the preparation method cannot cause the size changes of products and has the advantages of being easy to operate, low in cost and capable of easily achieving industrialized production.

Description

technical field [0001] The invention belongs to the technical field of polyoxymethylene, and in particular relates to a polyoxymethylene composite material whose surface can be painted and a preparation method thereof. Background technique [0002] Polyoxymethylene (POM) is one of the five major engineering plastics, with (—CH2O—) as the main chain, high crystallinity, good fatigue resistance, low friction coefficient, resistance to organic solvents, and simple molding and processing. At the same time, Polyoxymethylene also has the characteristics of low water absorption, stable size, luster, heat resistance, bending strength, high fatigue resistance, etc. It has good creep resistance, geometric stability and impact resistance, good oil resistance, overheat resistance properties such as oxides. However, due to the high crystallinity of polyoxymethylene and the fact that the molecular chain does not contain hydrophilic groups and lipophilic substrates, the paintability of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L59/00C08L61/06C08L29/04C08K3/36C08K3/26B29B9/06B29C47/92B29C45/78B29C48/92
Inventor 李又兵杨朝龙陈文张攀周桦林
Owner 重庆云天化天聚新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com